Study on the machinability of resulfurized composite free-cutting steels

The machinability of S, S-Ca, S-RE, and S-RE-Ca system resulfurized composite free-cutting steels were investigated, where RE is rare earths, mostly cerium. The experimental results showed that in the low cutting speed range (≤35 m/min), the S-RE system free-cutting steel had better machinability than the others and that the S-RE-Ca system free-cutting steel exhibited the best machinability at high cutting speeds. A protective layer capable of preventing diffusion wear was formed on the rake face of a P30 tool when S-RE-Ca system free-cutting steel was machined in the cutting speed range of 120 to 160 m/min.     

高温W/Re流口复合界面上的扩散层

W/Re流口在高温下使用时,复合界面处会发生反应扩散而形成一个由固溶体(W),双相σ,双相x,固溶体(Re)4个相组成的过渡层。并作出了不同反应扩散时间的浓度分布曲线,及浓度突变形成的双相区,从而确定了各相成份组成。对经反应扩散后的复合界面进行微观观察发现x相、σ相内有许多间隔式微裂纹,据此认为高温下W/Re流口失效原因是使用过程中上述两x,σ相内裂纹扩散,熔体渗入所致。     

A New Process to Make a Porous PTFE Structure from Aqueous PTFE Dispersion with the Help of Hydrogel

A novel method to make a porous material having relatively large cell diameter (200–300 m), which consisted of mainly poly(tetrafluoroethylene) (PTFE), was developed from aqueous PTFE dispersion by using the characteristics of hydrogel with the addition of carbon nanofiber (CNF). The porous material was produced as follows: firstly, an aqueous agar gel containing PTFE and CNF was prepared; secondly, the gel was freeze-dried; thirdly, the dried gel was heat-treated at 400°C where the agar was almost decomposed and PTFE became molten. The porous material showed electric conductivity (about 50 ), high porosity (about 96 vol%), and relatively uniform cell structures without shrinkage during freeze drying and heat treatment. While the method without CNF resulted in large shrinkage during heat treatment, meaning that CNF prevented the shrinkage. It was explained by the idea that the existence of rigid CNF, which was dispersed in the cell wall, prohibited the shrinkage of PTFE during heat treatment. It was unexpectedly found by SEM analysis that the porous materials had another macro-porous structure inside the cell wall, suggesting that the developed materials had a double porous structure.     

The Structure of the Irreversibly Bound Adhesion Promoter-Substrate Interfacial Layer of γ-Aminopropylsilanetriol on Crystalline Si, as Measured by XPS and FTIR

The irreversibly bound interfacial layer deposited by the γ-aminopropysilanetriol adhesion promoter onto a crystalline silicon substrate, which remains even after profuse washing, was found by XPS to have resulted from the fragmentation and rearrangement of the original γ-aminopropylsilanetriol molecule. A mechanism is proposed, involving the homolytic scission of the terminal N-C bond. One of the subsequent reactions is believed to involve hydrogen loss by abstraction and the formation of a terminal vinyl group, which bonds to the substrate. Support for this mechanism is found in IR spectroscopy of this layer.     

Humidity Sensor Characteristics of Woodceramics

The humidity sensor characteristics of Woodceramics were investigated. The Woodceramics used in this experiment were prepared at 650–900°C. The size of specimens selected was 1 × 1 × 10 mm . One was used as-cut and the other was polished. Above 700°C, the resistance of the specimen was below 50 and the decrease of resistance with increasing relative humidity was small. The specimen prepared at 650°C had a resistance of about 1 k. The resistance of as-cut specimens decreased with increase in relative humidity, but that of the polished specimen did not change significantly. The difference between as-cut and polished samples was explained by the differences in surface micro-structure.     

锂电极表面膜的组成和阻抗行为

介绍了锂电池中锂电极的表面膜的组成和阻抗行为，并根据其表面膜的阻抗行为提出了电化学模型。     

Characterization of nanoporous materials prepared from montmorillonite clay and its application to the decolorization of mare's milk oil

Nanoporous materials have been prepared by leaching the purified montmorillonite clay with sulfuric acid (H₂SO₄) solution with varying concentrations (0.5–2 M) at 80°C for 0.5–4 h. Acid leaching causes partial amorphisation of the clay with depletion of MgO, Al₂O₃, CaO and Fe₂O₃ components mostly from interlayer and octahedral sites. This increases the specific surface area by more than 3 times, i.e. from 49.1 to 157 m²/g. The pore-size distribution curves calculated from the adsorption isotherms of the leached montmorillonite show that most of the pores are in the mesoporous region with their diameter ranging 3–4 nm. This material turns out to be appropriate for bleaching of the mare's milk oil. The chemical and structural changes of the acid-leached montmorillonite are discussed in terms of the decolorization capacity.     

Electrical double layer characteristics of nanoporous carbon derived from titanium carbide

Electrochemical parameters of the nanoporous carbide-derived carbon|organic electrolyte have been studied by cyclic voltammetry and electrochemical impedance spectroscopy. The gas adsorption measurements have been used for evaluating the specific surface area, pore size distribution and porosity as the essential parameters influencing the double layer performance of carbon. The region of ideal polarizability, values of series and parallel resistance, capacitance and other important electrical double layer parameters were established. It was shown that specific capacitance of typical nanoporous carbon derived from titanium carbide is in the range of 70-90 F cm⁻³ or 100-130 F g⁻¹ and it depends on the synthesis conditions. The influence of the electrolyte solvent to the capacitance was insignificant, although acetonitrile was advantageous with respect of smaller viscosity.     

Fabrication of Porous SiC Ceramics with Special Morphologies by Sacrificing Template Method

Sacrificial template technique is widely used in producing porous materials with controlled morphologies and tailored properties. In this paper, unique templates such as filters, carbon nanotube, carbon fiber and silica were used to make porous SiC ceramic with special morphologies. Template derived porous ceramic plates, SiC nano-net, fiber-inverse and bead-inverse porous SiC ceramic were successfully prepared from the preceramic precursor, polymethylsilane (PMS). The synthesis procedures were involved with the infiltration of the templates with appropriate concentration of the preceramic polymer, their curing, pyrolysis and subsequent template removal. The synthesized porous SiC was characterized by SEM, TEM, XRD and BET methods.     

一种应用层组播可靠性技术

组播是一种高效的多点通信方式,IP组播效率高,但需专门的组播路由器,代价大,至今未能大规模部署.应用层组播数据的复制转发功能由终端主机完成,不涉及现有网络基础设施的更新,在Internet上容易实现,但终端主机的稳定性和安全性不如组播路由器,容易导致单点失效,且数据恢复困难.为解决应用层组播存在的可靠性问题,提出了一种树环结构的应用层组播方案,通过环结构来增加数据传输的可靠性,并采用主动随机转发技术来解决树环结构的多点失效问题.该方案既有效解决了应用层组播可靠传输问题,又降低了恢复时延和系统开销.