棕刚玉粉中Al2O3含量分析方法的探讨

对耐火材料——棕刚玉粉的质量分析控制，提出了用实用性的检测方法测定其Al2O3含量。通过与国家标准分析方法的对比试验，证实快速实用分析方法测定棕刚玉粉中Al2O3含量是可行的。     

CO2压缩机节油措施与效果

本分析了山西分公司二期CO2压缩机润滑油消耗高的原因，介绍了采取的针对措施以及2002年取得的节能效果，并进一步指出了CO2压缩机的节能空间。     

合成2,4-二叔丁基苯酚工业试验

以离子交换树脂为催化剂，苯酚和甲基叔丁基醚为原料合成2，4-二叔丁基苯酚(简称2，4酚)，合成产物经过滤再经间歇真空精馏精制提纯，得到高纯度的2，4酚成品。成品精馏后釜中残液在酸性白土催化剂的作用下通过歧化反应生成对叔丁基苯酚，再经精馏提纯得到成品对叔丁基苯酚。通过工艺优化，使2，4酚、对叔丁基苯酚形成联产生产工艺，降低了生产原料消耗和成本。     

Study on Adsorption Behavior of Rare Earth Complexes on Nanometer-Size Titanium Dioxide with ICP-AES

Inrecentyears ,rareearthelements (REEs)havebeenwidelyusedinfunctionalmaterials ,cata lystsandotherproductsinindustry ,diagnosisreagentsofmagneticresonanceimaging (MRI)inmedicineandsomefertilizersinagricultureespeciallyinChina .However,asaresultoftheirusage ,moreandmoreREEsaregettingintotheenvironment,andalsointohumanbodyviafoodchain[1,2 ] .Itisnotclearwhetherrareearthelementsareessentialforman ,soitisveryurgenttostudythebiologicaleffectofrareearthelementsinhumanhealthandenvironment .Inthes…     

溶液中微量甲基异丁基酮的分析方法

研究了微量甲异丁基酮在氟氧铌酸（H2NbOF5)及氟钽酸（H2TaF7)溶液中存在的形式，找到利用碘仿-硫代硫酸钠联合滴定的方法，来标定微量甲基异丁基酮在H2NbOF5及H2TaF7溶液中的含量，本方法在钽铌冶炼过程中操作简便易行且结果重现性好。     

TiSiW12O40/TiO2催化合成丙酸正丙酯

研究了固载杂多酸盐TiSiW12O40/TiO2催化丙酸与正丙醇的酯化反应，探讨了催化剂用量，反应时间及醇酸摩尔比对酯收率的影响。当醇酸摩尔比为1.3:1，催化剂的量为醇酸总质量的1.5%。反应时间为1.0h，酯产率可达71.4%以上，采用该催化剂合成丙酸正丙酯不仅酯化反应温度低，反应时间较短，催化剂用量少，而且可较好地回收利用，可降低成本；因此，TiSiW12O40/TiO2是合成丙酸正丙酯的优良催化剂，具有良好的应用前景。     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

运用PLC技术改造385m~2凯利式叶滤机控制系统

根据生产实践 ,结合PLC的技术特点和 385m2 凯利式叶滤机的电气联锁特性 ,阐述了应用PLC技术 ,可进一步提高 385m2 凯利式叶滤机的运转率和自动化水平。     

Synthesis of chemically and structurally modified dicalcium silicate

This paper describes the synthesis of cements, chemically and structurally related to Ca₂SiO₄. Silica was obtained from rice hull after heating at 600 °C. Calcium oxide and small amounts of barium chloride were mixed in order to obtain a final (Ca/Si) or (Ca+Ba)/Si ratio equal to 1.95, 1.90, and 1.80, which is lower than in the conventional cement. The solids were mixed and ultrasonically treated for 1 h with a water/solid ratio of about 20. After drying and grinding, the mixtures were heated up to 1100 °C. It was possible, in some cases, to obtain a cementitious material. These cements are structurally related to β-Ca₂SiO₄ and the lower (Ca+Ba)/Si ratio obtained was 1.95. The initial chemical compositions of these cements are: (Ca_1.83+Ba_0.12)SiO₄ and (Ca_1.79+Ba_0.16)SiO₄. A further lowering in the (Ca+Ba)/Si ratio changes the nature of the silicates.     

Microstructure and properties of MoSi2–MoB and MoSi2–Mo5Si3 molybdenum silicides

MoSi₂-based intermetallics containing different volume fractions of MoB or Mo₅Si₃ were fabricated by hot-pressing MoSi₂, MoB, and Mo₅Si₃ powders in vacuum. Both classes of alloys contained approximately 5 vol.% of dispersed silica phase. Additions of MoB or Mo₅Si₃ caused the average grain size to decrease. The decrease in the grain size was typically accompanied by an increase in flexure strength, a decrease in the room temperature fracture toughness, and a decrease in the hot strength (compressive creep strength) measured around 1200 °C, except when the Mo₅Si₃ effectively became the major phase. Oxidation measurements on the two classes of alloys were carried out in air. Both classes of alloys were protected from oxidation by an in-situ adherent scale that formed on exposure to high temperature. The scale, although not analyzed in detail, is commonly recognized in MoSi₂ containing materials as consisting mostly of SiO₂. The MoB containing materials showed an increase in the scale thickness and the cyclic oxidation rate at 1400 °C when compared with pure MoSi₂. However, in contrast with the pure MoSi₂ material, oxidation at 1400 °C began with a weight loss followed by a weight gain and the formation of the protective silica layer. The Mo₅Si₃ containing materials experienced substantial initial weight losses followed by regions of small weight changes. Overall, the MoB and Mo₅Si₃ additions to MoSi₂ tended to be detrimental for the mechanical and oxidative properties.