Effect of structural and electrochemical properties of different Cr-doped contents of Li[Ni1/3Mn1/3Co1/3]O2

Layered Li[Ni_(1−x)/3Mn_(1−x)/3Co_(1−x)/3Cr_x]O₂ materials with x = 0, 0.01, 0.02, 0.03, 0.05 are prepared by a solid-state pyrolysis method. The oxide compounds were calcined with various Cr-doped contents, which result in greater difference in morphological (shape, particle size and specific surface area) and the electrochemical (first charge profile, reversible capacity and rate capability) differences. The Li[Ni_(1−x)/3Mn_(1−x)/3Co_(1−x)/3Cr_x]O₂ powders were characterized by means of X-ray diffraction (XRD), charge/discharge cycling, cyclic voltammetry, and SEM. XRD experiment revealed that the Li[Ni_(1−x)/3Mn_(1−x)/3Co_(1−x)/3Cr_x]O₂ (x = 0, 0.01, 0.02, 0.03, 0.05) were crystallized to well layered -NaFeO₂ structure. The first specific discharge capacity and coulombic efficiency of the electrode of Cr-doped materials were higher than that of pristine material. When x = 0.02, the sample showed the highest first discharge capacity of 241.9 mAh g⁻¹ at a current density of 30 mA g⁻¹ in the voltage range 2.3–4.6 V, and the Cr-doped samples exhibited higher discharge capacity and better cycleability under medium and high current densities at room temperature.     

水热法合成Co（C14H8O4）（C12H12N2）微晶粉体及初步表征

根据文献合成了联苯二甲酸,并通过水热法制备了Co（C14H8O4）（C12H12N2）暗紫色的微晶粉体。通过元素分析、IR等方法对配合物进行了表征,并通过TG分析对该配合物的热稳定性及热分解机理做了初步探讨。     

锂离子电池Si_(1.81)Co_(0.6)Cr_(0.6)Zn_(0.2)/MGS复合负极材料的制备与性能

采用两步高能球磨法制备了一种新的锂离子电池硅基复合负极材料Si1.81Co0.6Cr0.6Zn0.2/MGS.用X射线衍射(XRD)和扫描电镜(SEM)表征了材料的组成和形貌结构.电化学测试表明,Si1.81Co0.6Cr0.6Zn0.2/MGS作锂离子电池负极材料有较好的电化学性能:首次可逆容量为561 mAh.g-1,50个循环后,可逆容量的保持率为91%.Si1.81Co0.6Cr0.6Zn0.2/MGS循环性能的改善归因于电极结构在循环过程中的稳定性.     

Engineering oxygen vacancy-rich Co3O4 nanowire as high-efficiency and durable bifunctional electrocatalyst for overall alkaline water splitting

A novel kind of vacancy-rich nanowire arrays were prepared by reducing rough Co₃O₄ nanowires with NaBH₄ solution on 3D nickel foam at room temperature for overall water splitting. Co₃O₄/NF treated by NaBH₄ for 10 min was highly active for oxygen evolution reaction (OER) and simultaneously efficient for hydrogen evolution reaction (HER) with the need of the overpotentials of 240 and 132 mV to drive 10 mA·cm^-2 in alkaline media, respectively. Furthermore, the electrocatalysts as both cathode and anode in a two-electrode system presented excellent durability for over 60 h at 10 mA·cm^-2, maintaining the cell voltage of merely 1.63 V. This work provides new methods and ideas for the preparation of transition metal oxide bifunctional electrocatalysts rich in oxygen vacancies.     

放电等离子烧结工艺对Ca3Co4O9陶瓷织构及电性能的影响

采用溶胶-凝胶与放电等离子烧结(SPS)相结合的方法制备了Ca3Co4O9陶瓷.通过X射线衍射、扫描电镜等表征手段,研究了放电等离子烧结工艺对Ca3Co4O9物相、显微结构和性能的影响.实验结果表明片状颗粒和放电等离子烧结工艺,特别是烧结温度的提高有利于Ca3Co4O9织构的形成.初步认为是片状颗粒在脉冲电流所产生的脉冲磁场作用下发生重排,使颗粒定向排列.本实验范围内,当烧结温度从700℃提高到900℃时,Ca3Co4O9晶粒取向度从0.75增大到0.87,700℃下的电阻率从6.24×10-5 Ωm降低到5.59×10-5 Ωm.此外,Ca3Co4O9块体表现出典型的半导体电学特征,电导率随着SPS烧结温度和测量温度的升高而增大,当SPS烧结温度为850℃时,P型Ca3Co4O9化合物在700℃有最大电导率.     

喷涂与激光重熔技术制备镍基纳米钴包碳化物复合涂层的研究

采用横流2．0kW CO2激光器，在45钢表面制备了表面较平整、较细密、基本消除了裂纹与孔隙并与基体呈冶金结合的镍基纳米WC／Co复合涂层。通过SEM，EDAX，XRD，AFM及Nano Indenter XP分析了熔覆层的显微组织、成分、物相及结合强度。结果表明，涂层的显微组织为涂层中镶嵌着大量与Ni基合金结合良好的WC／C。颗粒，其中在原子力显微镜下可见相当数量的粒度≤100μm的纳米颗粒。涂层的结合强度比传统热喷涂涂层提高了2．1倍。涂层中纳米WC／Co的纳米效应在激光熔覆中起着重要作用。     

Surface modification of spherical LiNi1/3Co 1/3 Mn1/3O2 with Al2O3 using heterogeneous nucleation process

To improve the cycle stability at high voltage and high charge/discharge rate, spherical LiNi1/3Co1/3Mn1/3O2 was coated with Al2O3 by using heterogeneous nucleation process, and the physical and electrochemical properties were studied. The SEM images show that there is a uniform coating on the modified spherical LiNi1/3Co1/3Mn1/3O2. The electrochemical tests indicate that the properties of LiNi1/3Co1/3Mn1/3O2 coated with 0.5% aluminum oxide are the best. The initial capacities are 150 and 173 mA.h/g at the rate of I C in the voltage range of 2.7-4.3 V and 2.7-4.6 V, respectively, and the discharge capacities maintain about 99% and 85% after 30 cycles, respectively. While those of the bare LiNi1/3Co1/3Mn1/3O2 are only 90% and 75%, respectively. The CV tests of LiNi1/3Co1/3Mn1/3O2 show that Al203-coating can restrain the oxide-reduction peak currents fading during the charge/discharge course.     

Synthesis and characterization of LiNi0.45Co0.10Mn0.45O2 cathode for lithium ion batteries

1INTRODUCTIONAdvanced rechargeable lithium ion batteriesare attractive for use in consumer electronic andelectric vehicle(EV)application because of a fa-vorable combination of voltage,energy density,cycling performance,and have been developed rap-idly worldwide during the past decade[1,2].LiCoO2has been widely used as a cathode material in com-mercial lithiumion battery because it is reasonableeasy to synthesize and shows a stable discharge ca-pacity[3].But due to its high cost and toxic…     

高Co稀土热作模具钢析出相沉淀析出的研究

采用X射线衍射和透射电镜对新研制的高Co稀土热作模具钢的析出相及析出动力学进行了分析和探讨。结果表明 ,经过固溶和时效处理后合金中同时析出大量金属间化合物和碳化物。金属间化合物主要为 μ相和Laves相 ,碳化物主要为MC、M2 3 C6和M6C。在 70 0℃时效不同时间后 ,析出相的总量随时效时间的延长而不断增大 ,但 μ相增加的速度比较缓慢 ;M2 3 C6、M6C、Laves相增加较快 ;而MC逐渐减少。M2 3 C6、M6C是通过基体中的M和C原子的直接反应的形式析出长大的。     

火花等离子烧结技术制备的WC/Co纳米硬质合金

研究了火花等离子烧结工艺与YG10、YG12两种纳米硬质合金性能的关系.然后采用火花等离子烧结技术制备了硬质合金功能梯度材料,该材料由纳米WC/10%Co、纳米WC/12%Co、微米WC/15%Co混合粉以及不锈钢圆片烧结而成.显微硬度压痕显示该材料各层间的应力较小.