Skin layer of A380 aluminium alloy die castings and its blistering during solution treatment

Skin layer is a characteristic microstructure of aluminium die castings, which would effect the surface blistering during solution treatment. In this study, the microstructures of skin layer were investigated by the methods of optical microscope (OM), scanning electron microscope (SEM) and electron probe micro-analyzer (EPMA). High resolution X-ray CT was used to compare the skin layer with normal surface before and after solution treatment. With the aid of computational fluid dynamics (CFD), the formation mechanism of the skin layer was discussed based on microstructure distribution, solute segregation, porosity distribution and surface blistering. The results suggested that the skin layer is related to a succession of complex processes before the filling process finished. Pore clusters or laminar defects would be formed in skin layers during solution treatment and cause severe surface blistering.     

深冷处理对低碳高合金马氏体轴承钢力学性能及组织的影响

利用洛氏硬度计、X射线衍射仪、扫描电子显微镜及透射电子显微镜等研究了低碳高合金马氏体轴承钢深冷处理后的硬度变化及组织演化。结果表明:深冷处理促使部分残留奥氏体转变为马氏体,导致深冷处理后实验钢的硬度较淬火态硬度有所升高。经深冷处理后实验钢在0~100 h回火过程中的硬度均比未深冷处理实验钢的硬度高。深冷处理促使钢中碳原子偏聚并在回火过程中以碳化物的形式析出,与未经深冷处理的实验钢相比,经深冷处理的实验钢回火后马氏体基体中的含碳量更低,表明实验钢经深冷处理后在回火过程中析出更多的碳化物。透射电镜分析表明,实验钢在回火过程中析出的大量弥散分布的纳米级M2C和M6C型碳化物是实验钢长时间回火后保持高硬度的主要原因。     

TC11钛合金中α'相和α'相的组织演变和显微硬度

研究了TC11钛合金中α"相和α'相的显微组织转变和显微硬度。金相显微组织观察和X射线衍射分析的结果表明： 随着固溶温度的提高α"相逐渐向α'相的晶体结构转变,α相、α"相和α'相的显微组织演变规律为：α+α",α+α"+α',α+α',α'。显微硬度测试的结果表明：在935~995℃固溶后显微硬度随着温度的提高先增大后减少,在985℃固溶后显微硬度达到峰值。综合分析显微组织影响合金显微硬度的机理：在935~985℃固溶后α'片层的厚度和间距变化的幅度小,β转变组织长大缓慢,在β转变组织中先后析出α"和α'相,随着固溶温度的提高α'片层的含量随之提高产生了相变强度效果,使其显微硬度提高;在985~995℃固溶后α'片层的厚度和间距明显增大,β转变组织变粗大,α"相消失,α'相的含量降低,相变强化的效果减弱,使β转变组织的显微硬度降低。     

基于回声状态网络的BOD在线软测量模型

针对污水处理过程的BOD建模问题,提出了一种基于回声状态网络的BOD在线软测量方法;基于梯度下降规则对回声状态网络的在线学习算法进行了研究;为保证学习算法的收敛性,基于Lyapunov理论对学习率范围进行了确定;实验表明,基于回声状态网络的在线BOD预测方法较常规神经网络预测精度提高约两个数量级,模型的适应性也大幅提高。     

25Cr_2Mo_1V钢螺栓在长期高温高压下脆化机理的研究

通过对已脆化的２５Ｃｒ２Ｍｏ１Ｖ钢螺栓及经恢复热处理后的螺栓的金相及电子显微分析,阐述了２５Ｃｒ２Ｍｏ１Ｖ钢在长期高温高压下工作发生脆化的原因,讨论了恢复热处理对脆化螺栓恢复性能的作用     

新一代动三轴仪计算机数据采集与处理系统

在８０年代研制的动三轴仪基础上,采用现代计算机技术,实现了对动三轴试验全过程动应力、动应变和动孔压发展变化的实时采集、显示和数据文件在线存盘。不仅使数据处理过程全部自动化,且成功地解决了滞回圈等非规则曲线面积及莫尔圆公切线求解等一系列难题。     

硬质合金激光热处理表面强化

研究低钴（ＹＧ８）硬质合金激光相变硬化的结果表明：合理选择激光淬火工艺参数及表面涂黑状况等,可使合金力学性能有较明显的提高,并对激光处理的合金组织结构与性能的改变的机理作了讨论与分析。     

球墨铸铁铁路配件的生产

本文对比了两种铸铁的机械性能,叙述了铸态球墨铸铁铁路配件的生产,分析了球化处理、孕育处理对配件质量的影响。     

阳离子染料可染改性涤纶及涤纶织物的碱减量研究

以阳离子染料可染改性涤纶丝与普通涤纶丝混纺（或交织）织物为研究对象,探讨碱剂。促进剂、减量温度及时间等因素对减量率的影响以及不同减量工艺经阳离子染料染色对织物闪色效果的影响。研究表明在保证一定减量率的基础上,染色后织物具有一定的闪色效果。     