溶胶-凝胶法制备(Sr,Pb)TiO3纳米晶粉及表征

采用溶胶－凝胶法成功地合成了（Sr,Pb)TiO3纳米晶粉，并利用FTIR技术对凝胶的形成过程及350℃，1．5h煅烧获得的粉体材料进行了表征。实验以TG－DSC分析作为拟定煅烧温度的依据，以XRD作为煅烧产物的分析手段，最佳煅烧温度为600℃，所合成的（Sr,Pb)TiO3纳米晶粉的平均晶粒尺寸约为21nm，属钙钛矿型立方顺电相结构。     

凝胶燃烧法合成LiCoO2超细粉体的研究

以LiNO3和Co(NO3)2@6H2O为原料,柠檬酸为燃料.采用凝胶低温燃烧技术合成了LiCoO2超细粉体.并利用各种分析技术对柠檬酸和硝酸盐形成的凝胶及凝胶燃烧合成的粉体进行了研究柠檬酸硝酸盐凝胶在350-400℃之间发生燃烧反应,得到黑色疏松粉体X射线衍射分析表明.适当提高柠檬酸在凝胶中的含量.燃烧后得到的粉体晶粒尺寸显著减小未经燃烧的粉体中除含有LiCoO2外.还有CoO,Li2CO3等杂质相.但在450℃下经短时间煅烧后.杂质相消失,其晶相为层状岩盐结构的高温LiCoO2相扫描电镜和透射电镜观察发现.随着煅烧温度的提高.LiCoO2粉体的粒径有所增大.但远小于在相同煅烧条件下用固相反应法制备的LiCoO2粉体.这表明采用燃烧法更适于合成具有单一相结构的,可在低温条件下烧结的超细LiCoO2粉体.     

Toward Largely Enhanced Toughness and Balanced Strength in PA1012/EPDM Blends via Synergistic Effect of Sacrificial Bonds and Network Structure

Here, zinc-neutralized ethylene propylene diene monomer (EPDM) ionomers with different neutralization levels are prepared through melt blending, and are then incorporated with polyamide 1012 (PA1012) to fabricate PA1012/EPDM ionomer blends. Interestingly, complex crosslinking networks are formed in the blends due to the construction of sacrificial bonds (Zn²⁺-carboxyl, Zn²⁺-amide). The as-formed network structure and sacrificial bond endow the PA/EPDM blends with largely enhanced toughness (16 times higher than that of neat PA), as well as balanced strength and stiffness. Meanwhile, the rheological behaviors of PA1012/EPDM ionomer blends indicate their relative low melting viscosity, which can avoid the processing shortcomings of plastics toughened with rubber. Moreover, PA1012/EPDM ionomer blends show obvious gelation behavior, and a maximum notched Izod impact strength exhibited at the gel point, in which unique double network structure can be observed obviously, indicating that there is a corresponding correlation between the rheological and mechanical parameters. Furthermore, the supper-toughening mechanism of PA1012/EPDM ionomer blends at gel point is explored, which origins from the large deformation and cavitation of rubber particles and the destruction of special double network morphologies. This study provides a novel and effective strategy to fabricate PA materials with outstanding toughness and excellent strength simultaneously.     

Effect of Bio-Based Cobalt Alginate on the Fire Safety and Mechanical Properties for Epoxy Resin

There is a growing demand to develop epoxy resins (EP) with smoke suppression as well as satisfactory flame retardancy. Herein, bio-based cobalt alginate is successfully fabricated and incorporated into EP to prepare EP/Cobalt Alginate composites with better fire safety performance. The addition of cobalt alginate reduces the thermal-decomposition rate, temperature at maximum weight-loss rate of EP, whereas obviously improves the thermal stabilities at a higher temperature range. Furthermore, the addition of cobalt alginate substantially reduces the fire hazard of EP, resulting in 56.2% reduction in peak heat release rate, as well as 17.8% and 56.3% reduction in total smoke production and peak smoke production rate, respectively, compared with EP matrix. Moreover, the presence of cobalt alginate increases smoke-suppressant properties, according to the smoke density test. Additionally, the incorporation of cobalt alginate has no obviously destructive effect on the mechanical properties of EP, while EP/Cobalt Alginate-3 exhibits a 27.0% improvement in impact strength. In prospective, this study may provide a significant method for producing eco-friendly flame retardant EP.     

2—甲基—1，4—萘醌对DNA光敏损伤的诱导作用

选择波长337nm的激光作为激励光源，借助凝胶电泳研究了2－甲基－1，4－萘醌诱导的DNA光敏损伤。结果表明：在氧气饱和、脱氧条件下光敏损伤显著，DNA损伤主要与光子剂量、核酸与萘醌浓度比及DNA存在形式有关。     

Ionic liquid mediated nano-composite polymer gel electrolyte for rechargeable battery application

ABSTRACT

Nano-composite polymer gel electrolytes (NPGEs) based on polymer poly(vinylidene fluoride-co-hexafluoropropylene) PVdF-HFP, ionic liquid, 1-butyl-3- methylimidazolium bis(trifluoromethanesulfonyl)imide BMIMTFSI, Li-salt along with the addition of SiO₂ nanoparticles have been synthesized and characterized by various techniques. Prepared NPGEs show high room temperature ionic conductivity (~10^?3 S/cm) and have a wide electrochemical window (ECW) (~3.3–3.5 V). The galvanostatic charge/discharge profile was studied by sandwiching best performing NPGEs between a LiFePO₄ cathode and lithium metal anode. The specific discharge capacity of the cell (Li/NPGE/LiFePO₄) room temperature at 0.1C rate is found to be 138 mAh/g.     

NO reduction by CH4 over Pd/Co-sulfated zirconia catalysts

A series of sulfated zirconia supported Pd/Co catalysts was synthesized by the sol–gel method and examined for NO_x reduction by methane. The NO conversion increased up to a Co/S ratio of 0.43, and then decreased at a higher Co loading (Co/S = 0.95). Sulfate content was also essential for obtaining high selectivity to molecular nitrogen. A catalyst loaded with 0.06 wt.% Pd, 2.1 wt.% Co and 2.1 wt.% S (Pd/Co-SZ-2) exhibited remarkable performance under lean conditions and displayed stability in a long-term durability test using a synthetic reaction mixture containing 10% water vapor. This catalyst exhibited the highest sulfur retention most probably as cobalt sulfide. Besides, the catalytic oxidation of NO to NO_y groups was confirmed by FT-IR, in agreement with the general mechanism for the SCR of NO by hydrocarbons. In the absence of oxygen in the feed stream, the catalyst was highly active for NO reduction with methane. IR stretching bands assigned to N₂O and adsorbed nitro groups were identified upon adsorbing NO on Pd/Co-SZ-2. This indicates that under rich conditions disproportionation of NO to N₂O and NO₂ occurs and confirms that the formation of NO₂ species is an essential step for NO reduction by CH₄.     

Miniemulsion and conventional emulsion copolymerization of styrene and butadiene: Effect of process on gel content

The properties of styrene/butadiene copolymers obtained by conventional emulsion and miniemulsion polymerizations were studied. Thin layer chromatography with flame ionization detection was used to determine the gel fraction of the copolymer in the latex particles as a function of conversion. It was found that the gel formation began at a higher conversion in the miniemulsion polymerization when compared with that in the conventional process. Also, a lower glass transition temperature was noted at the lowest conversion sampled (～25%), implying a higher initial butadiene monomer concentration within the nucleated miniemulsion monomer droplets when compared with particles formed conventionally. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 4616–4622, 2006     

钛掺杂硅胶块体吸附剂

以陶瓷纤维纸片为基材,顺次经水玻璃、酸性钛盐溶液浸渍共沉淀制得新型陶瓷基钛掺杂硅胶块体吸附剂.多孔介质表面分析显示:掺杂硅胶孔径在0.5～6 nm范围,以中孔为主.Fourier变换红外谱在波数954 cm 1处的特征吸收峰表明吸附剂中形成了Si-O-Ti键.根据掺杂前后固体魔角核磁共振硅谱中硅原子化学位移的变化(向高场方向移动)及X射线光电子能谱中各原子结合能的变化(Ti2p3/2的结合能随钛含量的增加而增加,而Si2p,O1s的结合能则呈相反趋势)进一步表明:钛原子替代硅原子进入硅胶网络.热重分析及烧结实验结果显示:钛掺杂吸附剂具有更好的热稳定性.新型吸附剂优异的吸附性能除了与其高的比表面积相关外,还与Ti-O键对水分子的亲合力紧密相关,其耐热性能增强与形成高热稳定性Ti-O Si键及材料表面导热性能提高有关.     

超细纤维素胶体和丙烯酰胺的接枝共聚

本文用纤维素材料经酸分解制备具有平衡聚合度（LODP）的微晶纤维素，再分散成超细纤维素胶体（准均相纤维素体系）。用扫描电镜（SEM）观察处理前后的纤维素颗粒尺寸，并比较它们和丙烯酰胺接枝共聚的反应速率、聚合转化率、接枝率、接技效率、聚丙烯酰胺支链的分子量及其分布的情况。