碱锰扣式电池的现状与发展

从品种、产量、生产设备、应用市场等方面详细说明了碱锰扣式电池近10年的发展与现状;简要介绍了碱锰扣式电池技术方面的改进措施,指出这类电池放电容量和耐漏液性能已达到世界先进水平;最后简要探讨了碱锰扣式电池的未来发展趋势和发展中存在的问题。同时指出,生产企业将面临电池无汞化、材料上涨、利润下降、产能过剩、无序竞争的严峻局面。     

Kinetics of Zn cathodic deposition in alkaline zincate solution

Kinetic parameters of the electrode reactions were measured by investigating steady-state current-potential behaviors. The Tafel slopes of cathodic and anodic processes are -0.113 8 V and -0.041 18 V, the anodic and cathodic apparent transfer coefficients are 0.519 3 and 1.435 2, respectively, and the stoichiometric number of rate-deterrnining step is 1. The theoretical kinetics equation of electrode reaction was deduced, from which the dynamic parameters can be calculated as follows： the cathodic and anodic Tafel slopes are -0.118 V and -0.039 4 V, respectively, consisting with the experimental values, Finally, the correctness of the mechanism was further demonstrated using apparent transfer coefficient according to the electrochemical dynamic equation of multi-electron reaction.     

加快大型号碱锰电池发展的探讨

分析了R20S等普通锌锰电池污染环境、浪费资源,难以实现产业可持续发展的现状;探讨了我国大型号电池向碱性化发展的必要性,既是市场发展的必然结果,也是世界发展的趋势;从市场前景和无汞锌粉、电解二氧化锰、零配件以及设备的开发等方面,探讨了LR20等大型号碱锰电池逐步替代普通锌锰电池的可能性。     

AFC电催化剂的研究进展

碱性燃料电池(AFC)具有启动温度低、性能可靠、可用非贵金属作催化剂等优点。综述了国内外AFC电催化剂的研究进展。为达到商业化,必须在非贵金属催化剂的稳定性和电极性能方面取得突破;对于贵金属催化剂,应大力开发与贵金属复合的多元催化剂,提高贵金属利用率,降低贵金属负载量。     

燃煤锅炉碱性废物及其脱硫能力的研究

通过对燃煤锅炉排放碱性废物及其可利用形式的分析，指出其含量受煤种、水质、燃烧方式、灰渣处理方式等多因素影响。实测了一台4t／h链条炉的排污水、离子树脂反洗水，设计了飞灰碱性溶出率的条件试验，并从理论上计算了碱性废物烟气脱硫的可能性。为便于比较，采用了将脱硫能力折合为单位蒸吨脱除率的表示方法。研究结果表明，在试验条件下单位蒸吨锅炉碱性废物可脱除0．415kg的SO2，占总排放量1．275kg的32．56％。其中排污水、反洗水和飞灰分别占8．63％、23．06％和0．87％。反洗水虽有脱硫能力，但成分复杂，可对水循环系统产生腐蚀，实际中尚未利用。飞灰脱硫能力低，因试验煤种钙镁氧化物含量仅为6．5％，在PH值为2．61时达到13．23％平衡溶出率：试验结果表明：飞灰碱性物质溶出率与PH值，搅拌时间有关。PH值低，溶出率大，搅拌时间长，溶出率高。飞灰的脱硫能力主要取决于煤灰的碱性氧化物含量。对碱性含量不高的飞灰，碱性溶出率少，利用其进行烟气脱硫的能力非常有限。这一点不同于钙镁含量高的褐煤和某些低硫煤。     

耐盐高温碱性蛋白酶产生菌株SD-142的脱毛条件研究

对耐盐高温碱性蛋白酶菌株SD -1 42在脱毛应用中的最适条件做了系统的研究 ,结果表明 :该菌株发酵液有较好的脱毛能力 ,脱毛的最适 pH为 8.5～ 1 0 .5 ,最适温度 2 8～ 3 0℃ ,最佳脱毛酶浓度为 1 5 0～ 2 5 0U/g ,其胶原酶活力较低     

Hydration Products and Reactivity of Blast-Furnace Slag Activated by Various Alkalis

Pastes of blast-furnace slag were cured for up to 90 d using sodium silicate (waterglass), NaOH, and three different mixtures of Na₂CO₃–Na₂SO₄–Ca(OH)₂ to activate reactions. The highest slag reactivity was observed for NaOH activation and the least for waterglass, although nonevaporable water indicated similar amounts of hydration products formed. The main hydration products found using X-ray diffractometry in all systems were calcium silicate hydrate (C-S-H) and a hydrotalcite-type phase. Microanalysis was performed on pastes activated using 50% Na₂CO₃·25% Na₂SO₄·25% Ca(OH)₂, NaOH, and waterglass; the chemical composition of the C-S-H in the waterglass case was different relative to the other two alkalis. For all alkaline agents used, the C-S-H seemed finely intermixed with a hydrotalcite-type phase of Mg/Al = 1.82, on average.     

含碱和表面活性剂的HPAM/Cr+3弱凝胶调驱剂的研制

从3种有机酸铬中选择一种烯基多元羧酸铬为交联剂,用于交联大庆油田三元复合驱油体系,制备弱凝胶调驱剂。以阻力系数(RF)特别是残余阻力系数(RRF)作为性能参数筛选调驱剂各组分的用量,得到了基本配方(以g/L计)如下:HPAM(M=1.2×107,HD=25%)0.9 交联剂(有效成分50%)0.18 表面活性剂(ORS41)3 碱(NaOH)8 稳定剂0.2,用大庆某三元复合驱试验区污水(矿化度3824mg/L)配液,其RRF值为清水(矿化度890mg/L)弱凝胶的～45%。基本配方弱凝胶45℃下7天时粘度18.3mPa·s,RF值81.2,RRF值8.2,随时间而减小,120天时分别为12.8mPa·s,66.1和7.3;油水界面张力仍在10-3mN/m数量级,只比常规三元复合体系略高;体系中表面活性剂在油砂上的静态吸附量为0.495mg/g油砂,比常规三元复合体系的相应值(0.462mg/g油砂)略高;岩心流动实验中测得的表面活性剂滞留量(0.067和0.070mg/g岩心)也高于常规三元复合体系的相应值(0.054和0.059mg/g岩心)。若用Na2CO3代替NaOH,则碱剂浓度可由6～8g/L提高到8～10g/L。表8参4。     

代汞缓蚀剂用In2O3纳米粉体的研究

描述了高纯氧化铟（In2O3）纳米粉末的制备方法及自制的In2O3纳米粉末的物理、化学性能。从BET测试结果和TEM照片看出,该粉末为比表面积大、分散性好的纳米粉末。与进口In2O3粉末进行应用对比表明：新电的电性能以及高温（60℃）贮存后的析气量均差别不大。测试结果显示：该纳米粉末具有良好的缓蚀效果。     

新型碱性催化剂制备丙二醇单甲醚

研制开发了新型碱性催化剂制备的二醇单甲醚。对催化剂的选择、反应温度、反应时间、反应物的配比、催化剂用量及其回收等影响因素进行了讨论,确定了新型碱性催化剂制备丙二醇单甲醚的配方及制备工艺。