Extraction of penicillin G from simulated media by an emulsion liquid membrane process

The extraction of penicillin G from simulated media was performed by water/oil/water (w/o/w) emulsion liquid membranes (ELMs) and studied under various operational conditions in a batch system. The degree of extraction achieved was between 80% and 95% under specific conditions. A concentration of greater than nine times the initial concentration of penicillin G in the external phase was obtained in the internal phase. The pH of the internal aqueous solution, containing a basic salt, was theoretically calculated on the basis of the amount of penicillin G transported into the internal phase. The calculated results agreed with the experimental data well and were used to select a suitable type and concentration of a basic salt in the internal phase to give a pH within the range 5 to 8 where penicillin G was stable after the termination of extraction. The extraction of penicillin G was successfully performed by the ELM process with sodium carbonate in the internal phase.     

Preparation and properties of silicone‐containing poly(methyl methacrylate) gels

Poly(methyl methacrylate) (PMMA) gels with varying amounts of silicone and solvent and constant amounts of crosslinker were prepared by solution free radical crosslinking copolymerization of methyl methacrylate (MMA), ethylene glycol dimethacrylate (EGDM), tetraethoxysilane (TEOS) and vinyltriethoxysilane (VTES) comonomer systems. They were then studied in benzene at a total monomer concentration of 3.5 mol L^?1 and 70 °C. The conversion of monomer, volume swelling ratio, weight fraction and gel point were measured as a function of the reaction time, silicone concentration and benzene content up to the onset of macrogelation. Structural characteristics of the gels were examined by using equilibrium swelling in benzene, gel fraction and Fourier‐transform infrared (FTIR) analysis. The morphology of the copolymers was also investigated by SEM. Based on the obtained results, it was concluded that the FTIR data did not have the capacity to show the presence of the VTES or TEOS moiety in these kinds of copolymers. On the other hand, the variation of weight fraction of gel, W_g, and its equilibrium volume swelling ratio in benzene, q_v, exhibited the same behaviour as that of MMA/EGDM copolymers. Also, the dilution of the monomer mixture resulted in an increase in the gel point and swelling degree and a decrease in the percent of conversion and gel fraction. Finally, TEOS is not an ideal silicone compound for reaction in the MMA/EGDM copolymerization system, whereas VTES is a suitable silicone comonomer for this system and it has been proved useful. Copyright © 2005 Society of Chemical Industry     

The emulsifying properties of a polysaccharide isolated from the fruit of Cordia abyssinica

Polysaccharide was isolated from Cordia abyssinica and its effect, at differing concentrations, on its emulsifying ability was determined. Emulsions of vegetable oil containing up to 1% of the polysaccharide in phosphate pH 7.4 buffer, were prepared by using a hand piston homogenizer. Emulsification was assessed by diluting samples of the emulsions in sodium dodecyl sulphate and measuring absorbance at 500 nm. Addition of increasing concentrations of the polysaccharide up to 1% enhanced emulsification and emulsion stability. Above 1% concentration the polysaccharide solutions were too viscous for making emulsions conveniently. At a constant concentration of the polysaccharide, addition of up to a 1% concentration of salt enhanced emulsion formation. Further addition of salt above 1% resulted in no further changes in emulsifying ability, but the stability of the emulsions formed decreased on increasing the concentration of salt above 1%. The effect of pH on emulsifying ability was investigated by preparing emulsions using buffers of different pH, from pH 3 to pH 13. The polysaccharide had poor emulsifying ability below pH 7. Emulsifying ability increased with pH between pH 7 and 11. At pH above 11 there was a decrease in emulsifying ability.     

Effects of three crosslinkers on colored pH‐responsive core–shell latexes

Environmentally responsive hydrogels have become attractive research subjects for many applications. In this work, a series of pH‐sensitive and color‐changing nanoparticles (nanogels) with core–shell structures were synthesized. The cores were blue latex particles synthesized by a miniemulsion technique with styrene and methacrylic acid as monomers and Neozapon Blue 807 as a dye. The shell was a pH‐sensitive polymer that was precipitation‐polymerized onto the core from 2‐(diethylamino) ethyl methacrylate with N,N′‐methylenebisacrylamide, poly(propylene glycol) diacrylate, and divinylbenzene as crosslinking agents. In the resultant latexes, the color was observed to change from deep blue to pale blue as the pH of the system was changed from a high of 10 to a low of 3. The synthesized latexes and particles (gels) were then characterized with an ultraviolet–visible spectrometer, dynamic light scattering, Fourier transform infrared, and nuclear magnetic resonance. Atomic force microscopy was also used to investigate the different morphologies of the particles after the synthesized latexes were dried at different pH values. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis of poly(methyl methacrylate)/silica nanocomposite through emulsion polymerization using dimethylaminoethyl methacrylate

Polymer/Silica nanocomposite latex particles were prepared by emulsion polymerization of methyl methacrylate (MMA) with dimethylaminoethyl methacrylate (DM). The reaction was performed using a nonionic surfactant and in the presence of silica nanoparticles as the seed. The polymer‐coated silica nanoparticles with polymer content and number average particle sizes ranged from 32 to 93 wt % and 114–310 nm, respectively, were obtained depending on reaction conditions. Influences of some synthetic conditions such as MMA, DM, surfactant concentration, and the nature of initiator on the coating of the silica nanoparticles were studied. Electrostatic attraction between anionic surface of silica beads and cationic amino groups of DM is the main driving force for the formation of the nanocomposites. It was demonstrated that the ratio of DM/MMA is important factor in stability of the system. The particle size, polymer content, efficiency of the coating reaction, and morphology of resulted nanocomposite particles showed a dependence on the amount of the surfactant. Zeta potential measurements confirmed that the DM was located at the surface of the nanocomposites particles. Thermogravimeteric analysis indicated a relationship between the composition of polymer shell and polymer content of the nanocomposites. The nanocomposites were also characterized by FTIR and differential scanning calorimetry techniques. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Effects and properties of poly(arylene ether benzonitrile)s of various molecular weights blended with sulfonated poly(ether ether ketone)

Poly(arylene ether benzonitrile) (PAEBN) was synthesized with 2,6‐dichlorobenzonitrile and biphenol. PAEBNs with various molecular weights (MWs), 1,640,000 and 185,000 g/mol, were synthesized by control of the stoichiometry of the monomers and were blended with sulfonated poly(ether ether ketone) (SPEEK). The effects of MW on the water uptake, swelling, methanol permeability, and proton conductivity of the SPEEK/PAEBN blend membranes were investigated. The molecular mobility of the SPEEK/PAEBN blends was also examined in this study. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis and properties of PDMS modified waterborne polyurethane–acrylic hybrid emulsion by solvent-free method

A new type of polysiloxane modified polyurethane–acrylic hybrid emulsion was synthesized by solvent-free method and the polysiloxane was introduced into the soft segment of polyurethane chains using dihydroxybutyl-terminated polydimethylsiloxane (PDMS). The formed film from the hybrid emulsion could provide obviously higher water-resistance property. The preparation technologies such as the content of carboxy group and acrylic monomer, the rate and the time of emulsification were discussed systematically. The chain structure and the particle size were confirmed by the analysis of Fourier transform infrared spectroscopy and transmission electron microscopy, respectively. The effect of PDMS content on the water resistance and the mechanical property were investigated by absorbed water ratio, water contact angle and dynamic mechanical measurement.     

Influence of Two Salicylate Components on the Particle Size of an Oil-in-Water Emulsion with Nonionic Surfactants

This paper reports a study undertaken using techniques of static and dynamic light scattering to investigate the influence of sodium salicylate and methyl salicylate on droplet size of oil-in-water emulsions. The rates of changes were measured by determining the size and distribution of the oil droplet in the material. All emulsions showed a bimodal size distribution; the mean diameters and polydispersity were calculated from intensity. These data were analyzed with nonlinear regressions and bootstrap methodology. An amount of methyl salicylate component induced a decrease of mean diameter and standard deviation. On the contrary, sodium salicylate entailed the growth of all droplet populations and coalescence for the highest concentration.     

Ultrasonic study of molecular association of poly(vinyl chloride) solution in tetrahydrofuran

Ultrasonic absorption, velocity, adiabatic compressibility, relaxation time and relaxation amplitude measurements are reported on poly(vinyl chloride) (PVC) solution in tetrahydrofuran (THF) using pulsed ultrasonic apparatus operating at 2 MHz and 313 K. Results show a linear increase of velocity. density, viscosity, absorption coefficient, relaxation time and relaxation amplitude values with the increase of PVC concentration in THF. In contrast the compressibility decreases with increasing PVC concentration. This suggests interaction between PVC and THF molecules.     

γ 射线引发 VAc 乳液聚合以制备白乳胶的动力学及工艺条件研究

研究了ＶＡｃ的辐射乳液聚合动力学，并对其聚合工艺条件作了初步探索。得出ＶＡｃ乳液在进行辐射聚合时，成核期结束较早（转化率在１０％以下），有相当长的恒速期存在。乳胶粒子直径在０．５～３μｍ之间，比一般的乳液聚合乳胶粒子要大。同时从动力学数据还可以看出几种成核机理（胶束成核，水相成核和液滴成核）同时存在，由此对试验条件提出了相应的要求。