Synthesis of LiFePO4 with fine particle by co-precipitation method

LiFePO₄ is a potential candidate for the cathode material of the lithium secondary batteries. A co-precipitation method was adopted to prepare LiFePO₄ because it is simple and cheap. Nitrogen gas was needed to prevent oxidation of Fe²⁺ in the aqueous solution. The co-precipitated precursor shows the high reactivity with the reductive gas, and the single phase of LiFePO₄ is successfully synthesized with the aid of carbon under less reductive conditions. LiFePO₄ fine powder prepared by co-precipitation method shows high rate capability, impressive specific capacity and cycle property.     

Effects of gallia additions on sintering behavior of gadolinia-doped ceria

The effects of gallia additions on the sintering behavior of gadolinia-doped ceria were systematically investigated from the following aspects: the variation in sintered density, the variation in grain size, and the existing forms of Ga₂O₃ in CeO₂.Sintered density increased with increasing Ga₂O₃ content up to 5 mol.% and then it decreased with further addition of Ga₂O₃. Grain size also increased with increasing Ga₂O₃ content up to 5 mol.% and then decreased with further addition of Ga₂O₃. Decrease in grain size was caused by a pinning effect of Ga₂O₃ precipitation at grain boundaries. Lattice constant decreased with increasing Ga₂O₃ content up to 5 mol.%. This decrease will be due to the substitution of smaller Ga³⁺ ions for Ce⁴⁺ ions in the CeO₂ structure. According to the results obtained from scanning electron microscope (SEM) and X-ray diffraction (XRD) analyses, the solubility limit of Ga₂O₃ in Ce_0.8Gd_0.2O_1.9 ceramics can be estimated to be nearly 5 mol.%. The addition of Ga₂O₃ up to the solubility limit was found to promote the sintering properties of Gd₂O₃-doped CeO₂.     

Electrical conductivity and gas sensitivity of Zn-Sb-O thick films

The thick film of Zn-Sb-O was prepared by coating the paste of nanoparticles mixture (Sb₂O₃:ZnO=1:3) on the alumina substrate, followed by sintering at 500-900 °C for 2 h in air. The electrical resistance and gas-sensing properties to benzene, alcohol and acetone of Zn-Sb-O films were found to be dependent on the change of phase structure caused by sintering temperature.     

真空制盐蒸发结晶器的设计与实践

真空蒸发制盐外热式强制逆循环轴向出料蒸发结晶器，经多个厂家生产应用实践证明是成功的，具有生命力的。这种新型结构，作为一项新技术新设备应加强研究，总结提高，推广应用。不断完善。文章从流体力学、结晶机理角度要求，到具体工程设计参数和材质选用。论述了该罐的特点。     

Expressive Facial Gestures From Motion Capture Data

Human facial gestures often exhibit such natural stochastic variations as how often the eyes blink, how often the eyebrows and the nose twitch, and how the head moves while speaking. The stochastic movements of facial features are key ingredients for generating convincing facial expressions. Although such small variations have been simulated using noise functions in many graphics applications, modulating noise functions to match natural variations induced from the affective states and the personality of characters is difficult and not intuitive. We present a technique for generating subtle expressive facial gestures (facial expressions and head motion) semi‐automatically from motion capture data. Our approach is based on Markov random fields that are simulated in two levels. In the lower level, the coordinated movements of facial features are captured, parameterized, and transferred to synthetic faces using basis shapes. The upper level represents independent stochastic behavior of facial features. The experimental results show that our system generates expressive facial gestures synchronized with input speech.     

Grain growth kinetics in Dy-doped Bi0.5Na0.5TiO3 ceramics

Dysprosium-doped bismuth sodium titanate ceramics were prepared using the conventional mixed-oxide method. The amount of dysprosium used was varied from 0 to 2 at.%. The mixed powders were calcined at 800 °C and checked for phase purity using X-ray diffraction technique. The calcined powders were then cold-pressed into pellets and sintered at 1050 °C for the time ranging from 2 to 48 h. The ceramics were checked for phases and microstructures using an X-ray diffractometer and a scanning electron microscope, respectively. The analysis showed that undoped BNT ceramics sintered at longer time exhibited a significant grain growth with non-uniform grain size distribution and shape. The Dy-doped BNT however showed a much more limited grain growth behavior, resulting in smaller grain size and more equiaxed grain shape. It was also found that all Dy-doped BNT ceramics sintered at 48 h possessed lower porosity than those sintered for shorter time.     

Potential of vibro-milling technique for preparation of electroceramic nanopowders

The potential of the vibro-milling technique as a simple method to obtain usable quantities of single-phase electroceramic powders with nanosized particles was examined. A detailed study considering the role of both milling time and firing condition on phase formation and particle size of the final product was performed. The calcination temperature for the formation of the desired phase was lower when longer milling times have been applied. More importantly, by employing an appropriate choice of the milling time and calcination condition, high purity electroceramic nanopowders have been successfully prepared with a simple solid-state reaction method.     

Effects of compressive and tensile stress on the growth mode of epitaxial oxide films

Oxide films were deposited on different substrates by laser molecular beam epitaxy. Reflection high-energy electron diffraction was performed to in situ investigate the change of growth mode and the lattice relaxation during the growth. An asymmetrical phenomenon was found in the two kinds of strain states, compressive stress and tensile stress of heterostructures with different lattice mismatch. In the case of BaTiO₃/SrTiO₃ (2.2%), 2D layer-by-layer growth mode without lattice relaxation can be maintained for a longer period for BTO films on STO with compressive stress, comparing to STO films on BTO with tensile stress. When MgO films were deposited on SrTiO₃ with a large mismatch of 7.8%, compressive stress leads to rapid lattice relaxation with a very thin wet layer, and 3D strained island were observed. As a comparison, SrTiO₃ films on MgO with tensile stress were configured. No RHEED patterns can be observed duo to a large tensile stress.     

Effect of hot pressing on processing and properties of BBN ceramics

BBN (BaBi₂Nb₂O₉) is very interesting and promising lead free material with relaxor properties in capacitors, sensors and actuators.     

Novel electro-optic properties of epitaxially grown (Pb, La)(Zr, Ti)O3 (PLZT) thin films derived by advanced sol–gel methods

Advanced sol–gel methods using a secondary solvent addition into (Pb, La)(Zr, Ti)O₃ (PLZT) sol–gel solution and a methanol pre-treatment of sapphire substrates are demonstrated. For the secondary solvent addition, the additive affected the crystallinity and electro-optic (EO) property of PLZT films and only methanol addition can improve them. In addition, the methanol pre-treatment is also appeared to be effective to improve film characteristics.

Through these optimizations, epitaxially grown PLZT thin films on r-cut sapphire are obtained and a high Pockels coefficient which is comparable to those of bulk PLZTs is achieved. It is believed that these PLZT thin films are applicable for integrated EO devices and open the door for the future data communication systems.