为使聚氯乙烯具有抗静电性能,采用加入具有导电性填料的方法,但加入大量的填料,会使硬聚氯乙烯的冲击性能降低,加工性能变差。本文是在以炭黑为填料的基础上,研究不同的改性剂和加工助剂改进硬聚氯乙烯的效果,结果表明,加入冲击改性剂和加工助剂后,大大增加了硬聚氯乙烯的冲击强度,且加工性能也得到改善,同时由于炭黑具有补强效果,其拉伸强度和弯曲强度在加入改性剂后也能满足使用要求。     

Reaction products of ammonium nitrate phosphate fertilizers of varying water-soluble phosphorus content in different Indian soils

Studies were undertaken on the isolation and identification of reaction products of ammonium nitrate phosphate (ANP) fertilizers containing 30, 50 and 70 per cent water-soluble phosphorus (WSP) of total phosphorus in representative soils of the vertisol, oxisol, alfisol, entisol, mollisol and aridisol groups of India. ANP fertilizers were applied in solid form to soil, and reaction products formed at and around the site of ANP fertilizer placement were identified after six weeks incubation in moist soils by X-ray diffraction technique. DCPD (dicalcium phosphate dihydrate- CaHPO₄ · 2H₂O) was the major reaction product of ANP fertilizers containing 30 and 50 per cent WSP in vertisol, entisol, aridisol, mollisol, oxisol and alfisol, and of ANP containing 70 per cent WSP in vertisol, entisol, alfisol, aridisol and mollisol. DCP (dicalcium phosphate-CaHPO₄) was detected with ANP of 30 and 50 per cent WSP in the vertisol, alfisol, entisol, mollisol and aridisol groups of soils. In addition to DCPD, FePO₄ · 2H₂O (metastrengite) and AlPO₄ · 2H₂ O-monoclinic (metavariscite) were formed in alfisol and oxisol soils with ANP of 30 and 50 per cent WSP. FePO₄ · 2H₂O and AlPO₄ · 2H₂O (metavariscite) were identified in alfisol and oxisol soils while AlPO₄ · 2H₂O-orthorhombic (variscite) was formed in alfisol soils with ANP of 70 per cent WSP.     

离子色谱法测定配煤、焦炭和焦油中的氯含量

研究了用带电导检测器的离子色谱对配煤、焦炭和焦油中的Cl- 进行测定的方法。在YSA型8126A-4# 阴离子分离柱上用3.5mmol/LNa2CO3、5.3mmol/LNaHCO3做淋洗液对Cl-进行测定,方法简便快速。Cl-的检出限为2×10-6。该法也适用于F-、NO2-、NO3-、SO42-等的测定。     

二合一石墨合成炉的应用

对石墨合成炉运行中出现的故障进行分析和探讨，并提出一些建议和改进措施，以实现石墨合成炉的稳定运行。     

Zinc hydroxystannate and zinc stannate as flame‐retardant agents for flexible poly(vinyl chloride)

The flame‐retardant and smoke‐suppressant properties of inorganic tin compounds such as zinc hydroxystannate (ZHS) and zinc stannate (ZS) were investigated in a comparison with alumina trihydrate, magnesium hydroxide, and Sb₂O₃ through the limiting oxygen index test and smoke density test. The flame‐retardant mechanisms were studied through the char yield test, SEM, quantitative analysis, thermogravimetry and differential thermal analysis. The thermal degradation in air of flexible PVC treated with the above compounds was studied by thermal analysis from ambient temperature to 800°C. The results showed that tin compounds such as ZHS and ZS could be used as a highly effective flame retardant for flexible PVC, and it appears that the tin compound may exert its action in both the condensed and vapor phases, but mainly in condensed phases as a Lewis acid. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 98: 1469–1475, 2005     

Effects of the reinforcement and toughening of acrylate resin/CaCO3 nanoparticles on rigid poly(vinyl chloride)

Novel composite particles based on nanoscale calcium carbonate (nano‐CaCO₃) as the core and polyacrylates as the shell were first synthesized by in situ encapsulating emulsion polymerization in the presence of the fresh slush pulp of calcium carbonate (CaCO₃) nanoparticles. Subsequently, these modified nanoparticles were compounded with rigid poly(vinyl chloride) (RPVC) to prepare RPVC/CaCO₃ nanocomposites. At the same time, the effects of the reinforcement and toughening of these modified nanoparticles on RPVC were investigated, and the synergistic effect of modified nanoparticles with chlorinated polyethylene (CPE) was also studied. The results showed that in the presence of nano‐CaCO₃ particles, the in situ emulsion polymerization of acrylates was carried out smoothly, and polyacrylates successfully encapsulated on the surface of nano‐CaCO₃ to prepare the modified nanoparticles, breaking down nano‐CaCO₃ particle agglomerates, improving their dispersion in the matrix, and also increasing the particle–matrix interfacial adhesion. Thus, the effects of the reinforcement and toughening of these modified nanoparticles on RPVC were very significant, and the cooperative effect of the nanoparticles with CPE occurred in the united modification system. Scanning electron microscopy analyses indicated that large‐fiber drawing and network morphologies coexisted in the system of joint modification of nanoparticles with CPE. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3940–3949, 2007     

PVC╱NBR╱BR三元共混弹性体的制备

采用结合丙烯腈含量为26％的NBR、分子量适中的悬浮法Ⅲ型PVC和BR共混,制得了综合性能较PVC/NBR并用胶优异的弹性体。优选的工艺条件为:PVC/NBR/BR=30/60/10(质量比);补强剂选用炭黑40份,超细碳酸钙50份,轻质碳酸钙20份;硫化体系选用过氧化物加少量硫磺;混炼温度为140—170℃,混炼时间为10—15min。通过电子显微镜和动态力学分析,弹性体存在两个T,PVC为分散相,橡胶为连续相。     

Use of Re(C5H7O2) in preparation of catalysts for olefin metathesis

New catalysts for olefin metathesis are obtained upon interaction between rhenium trisacetylacetonate and -Al₂O₃ surface. After high temperature treatment in flows of O₂ and N₂ and addition of organometallic compound as a cocatalyst the activity of the resulting catalyst exceeds that of known Re/Al₂O₃ catalysts prepared by impregnation. The catalysts exhibit maximal activity at a cocatalyst surface concentration of 3 × 10^–7 mol/m². Further increase of the cocatalyst concentration leads to deactivation.     

氨基硫脲的研制

以硫氰酸铵和水合肼为原料，用丙酮作异构催化剂合成氨基硫脲。一次收率为８９．０３％，用５０％母液循环使用，收率达到９２．５％，产品质量符合要求。