Thermal Evaluation of Scorched Graphite-Epoxy Panels by Infrared Scanning

A simple measurement system is described for evaluating damage to graphite-epoxy panels, such as those used in high-performance aircraft. The system uses a heating laser and infrared imaging system to measure thermal performance. Thermal conductivity or diffusivity is a sensitive indicator of damage in materials, allowing this thermal measurement to show various degrees of damage in graphite-epoxy composites. Our measurements track well with heat-flux damage to graphite epoxy panels. This measurement system, including analysis software, could easily be used in the field, such as on the deck of an aircraft carrier or at remote air strips.     

控制转炉炉壳蠕变变形

转炉采用镁碳砖炉衬后，炉壳温度急剧增加，炉壳的局部区域会发生永久变形。分析认为：炉壳的永久变形是由于蠕变变形引起，而不是塑性变形引起，给出了影响蠕变变形的因素，指出了控制炉壳蠕变变形的策略。     

香豆胶衍生物的化学结构及稳定性研究

将市售商品溶于水,用异丙醇沉析提纯,溶于0.1 mol/L NaNO3纯水溶液中,经0.5μm滤膜过滤后用水相凝胶渗透色谱法(GPC)测定,测得香豆胶(FG)、羟丙基香豆胶(HPFG)、阳离子香豆胶(CFG)的数均、重均相对分子质量Mn、Mw分别为:1.19×105、3.36×105,8.52×104、2.85×105,9.33×104、2.87×105。用甘露聚糖链在碱性条件下醚化时发生降解,解释两种改性FG的相对分子质量较FG低而多分散性(Mw/Mn)较FG高的测试结果。认为商品FG的1%水溶液黏度(1300 mPa.s)高于商品HPFG和CFG(分别为705和610 mPa.s)的原因是前者相对分子质量较高且残渣含量也较高(~10%,后二者为1%~2%)。HPFG的取代度为0.12,根据文献发表的13C-NMR数据确认HPFG分子链上羟丙基取代位置为C6。讨论了香豆胶(半乳甘露聚糖)的化学结构。热重分析法测定的热稳定性,HPFG高于CFG,CFG又高于FG。图6表3参13。     

辽河催化裂化澄清油中间馏分热反应研究

采用先加入絮凝剂脱灰，再经减压蒸馏切割420～500℃馏分的方法，将辽河催化裂化澄清油预处理，考察了澄清油、加入絮凝剂脱灰后的澄清油以及脱灰后再减压蒸馏所得的中间馏分这3种原料在热转化过程中中间相的转化历程，并采用偏光显微镜观察热转化产物。结果表明，澄清油预处理效果明显，所得中间馏分具有较低的H／C原子比（nH／nC）和适宜的组成分布，是生产针状焦的理想原料。热转化产物的光学组织结构属于各向异性发达的广域-流线型结构。     

The flame retardant mechanism of polyolefins modified with chalk and silicone elastomer

This paper presents the current understanding of the flame retardant mechanism of Casico?. The study includes the flame retardant effect of each individual component: ethylene–acrylate copolymer, chalk and silicone elastomer, as well as the formation of an intumescent structure during heating. The flame retardant properties were investigated by cone calorimetry and oxygen index tests. To obtain insight into the flame retardant mechanism, heat treatment under different conditions has also been performed. The results indicate that the flame retardant mechanism of Casico is complex and is related to a number of reactions, e.g. ester pyrolysis of acrylate groups, formation of carbon dioxide by reaction between carboxylic acid and chalk, ionomer formation and formation of an intumescent structure stabilized by a protecting char. Special emphasis is given to the formation of the intumescent structure and its molecular structure as evaluated from ¹³C MAS‐NMR and ²⁹Si MAS‐NMR, ESCA and XRD analysis. After treatment at 500°C the intumescent structure consists mainly of silicon oxides and calcium carbonate and after treatment at 1000°C the intumescent structure consists of calcium silicate, calcium oxide and calcium hydroxide. Copyright © 2003 John Wiley & Sons, Ltd.     

提高加热炉热效率措施的探讨

对本厂常减压装置提高加热炉热效率采取的措施进行了分析和总结     

Copolymerization of bromophenylmaleimide with ethyl or butyl methacrylate

N‐p‐Bromophenylmaleimide (BrPMI) does not polymerize in solution by conventional free radical mechanism. However, it readily polymerized in bulk when mixed with a free radical initiator and heated in a microwave oven for 7–8 min. Copolymerization of ethyl methacrylate or butyl methacrylate with BrPMI was conducted in dioxane. The copolymers were characterized by IR and ¹H NMR spectroscopy and gel permeation chromatography. The monomer reactivity ratios were calculated by a non‐linear least‐square analysis. Thermal analysis indicated a great improvement in thermal stability of the copolymers compared with the methacrylate homopolymers. BrPMI was also polymerized in bulk in the DSC pan, which allowed the calculation of the activation energy of its polymerization. Copyright © 2003 Society of Chemical Industry     

转动玻璃圆筒激光器

本文介绍了转动玻璃圆筒激光器的设计及实验结果,得到了脉冲能量为13J,重复频率为15Hz的激光输出。电光转换效率为2.2％,斜效率为3.4％。     

Hydrothermal Synthesis and Low-Temperature Sintering of Zinc Gallate Spinel Fine Particles

Nanosized powders of single-phase zinc gallate (ZnGa₂O₄) spinel were hydrothermally synthesized from solutions in the presence of NaOH over the pH range of 1.9 to 7.0 and from solutions above pH 7.0, i.e., the very basic medium (pH of 13.85), by removing the residual ZnO phase by washing with aqueous H₂SO₄ from the precipitate mixtures of zinc gallate spinel particles and ZnO. A very wide compositional range (Zn/2Ga = 0.705–1.157) of zinc gallate spinel solid solutions could be hydrothermally synthesized in the form of nanosized particles from acid and very basic mediums (pH of 2.4–13.85) in the presence of NaOH. These hydrothermally synthesized spinel powders showed good sinterability and almost full densification at 1100°C for 1 h. Dense sintered bodies consisting of single-phase zinc gallate spinel were fabricated at 1100°C using zinc gallate spinel powders having almost stoichiometric composition formed from the solution at pH 9.95 in the presence of aqueous ammonia.     

焦化加热炉空气预热器腐蚀结垢与预防

空气预热器运行的好坏直接影响到加热炉的热效率 ,文章结合焦化装置加热炉空气预热器的使用、维修、改进等 ,论述了预热器存在的露点腐蚀问题。同时提出从设计、操作、设备等方面采取有效措施 ,保障预热器的长周期高效运行。