Improvement of adhesion and paint ability of EVA copolymers with different vinyl acetate contents by treatment with UV-ozone

The surface modifications produced by UV-ozone treatment of two ethylene-vinyl acetate (EVA) copolymers containing 12 and 20 wt% vinyl acetate (EVA12 and EVA20 respectively) were studied. The treatment with UV-ozone improved the wettability of both EVAs due to the creation of new carbon–oxygen moieties. The extent of these modifications increased with increasing length of the treatment and the modifications produced in EVA20 were produced for shorter lengths of treatment. The UV-ozone treatment also created roughness and heterogeneities on the EVA surfaces. Whereas roughness formation prevailed on the UV-ozone treated EVA12, important ablation was dominant on the treated EVA20. T-peel strength values in joints made with polychloroprene adhesive increased when the EVAs were treated with UV-ozone. Short length of UV-ozone treatment (1 min) produced higher T-peel strength in joints made with EVA20 whereas higher T-peel strength values in joints made with EVA12 were obtained after treatment for 5–7.5 min in which a cohesive failure into a weak boundary layer on the treated EVA surface was found. Furthermore, the adhesion of UV-ozone treated EVA20 to acrylic paint increased. Finally, the ageing resistance of the treated EVA/polychloroprene adhesive joints was good and the surface modifications on the UV-ozone treated EVAs lasted for 24 h after treatment at least.     

Nonlinear response in glass fibre non-crimp fabric reinforced vinylester composites

This paper addresses the nonlinear stress-strain response in glass fibre non-crimp fabric reinforced vinylester composite laminates subjected to in-plane tensile loading. The nonlinearity is shown to be a combination of brittle and plastic failure. It is argued that the shift from plastic to brittle behaviour in the vinylester is caused by the state of stress triaxiality caused by the interaction between fibre and vinylester. A model combining damage and plasticity is calibrated and evaluated using data from extensive experimental testing. The onset of damage is predicted using the Puck failure criterion, and the evolution of damage is calibrated from the observed softening in plies loaded in transverse tension. Shear loading beyond linear elastic response is observed to result in irreversible strains. A yield criterion is implemented for shear deformation. A strain hardening law is fitted to the stress-strain response observed in shear loaded plies. Experimental results from a selection of laminates with different layups are used to verify the numerical models. A complete set of model parameters for predicting elastic behaviour, strength and post failure softening is presented for glass fibre non-crimped fabric reinforced vinylester. The predicted behaviour from using these model parameters are shown to be in good agreement with experimental results.     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Electromagnetic shielding properties of iron oxide impregnated kenaf bast fiberboard

The electromagnetic shielding effectiveness of kenaf fiber based composites with different iron oxide impregnation levels was investigated. The kenaf fibers were retted for removing the lignin and extractives from the fibers and magnetized. Using the unsaturated polyester and the magnetized fibers, kenaf fiber based composites were manufactured by the compression molding process. The transmission energies of the composites were characterized when the composite samples were exposed under the irradiation of electromagnetic (EM) wave with a variable frequency from 9 GHz to 11 GHz. Using the Scanning Electron Microscope (SEM), the iron oxide nanoparticles were observed on the surfaces and inside the micropore structures of single fibers. As the Fe content increased from 0% to 6.8%, 15.9% and 18.0%, the total surface free energy of kenaf fibers with the magnetizing treatments increased from 44.8 mJ/m² to 46.1 mJ/m², 48.8 mJ/m² and 53.0 mJ/m², respectively, while the modulus of elasticity reduced from 2875 MPa to 2729 MPa, 2487 MPa and 2007 MPa, respectively. Meanwhile, the shielding effectiveness was increased from 30–50% to 60–70%, 65–75% and 70–80%, respectively.     

Fabrication of 3D structures via direct ink writing of kaolin/graphene oxide composite suspensions at ambient temperature

Kaolin/graphene oxide composite has been widely utilized in aero-space and architectural engineering applications due to its excellent mechanical property. Direct ink writing (DIW) is a freeform rapid prototyping technology that could be used to accurately fabricate the resulting size with complex shapes. In this study, we reported the DIW of kaolin/graphene oxide (GO) composite suspensions (KGCS) to assemble 3D structures at ambient temperature for the first time. The effects of GO on the chemical constitution and microstructure of kaolin suspensions were investigated. Rheology was characterized to ensure printability of KGCS. The addition of GO in kaolin suspensions quickened a flocculation structure, which dramatically changed their rheology properties. The DIW of 3D structures from the optimal KGCS sample maintained their initial shape without spreading. The flexural and compressive strengths of the dried optimal KGCS samples were obviously enhanced due to the improvement and reduction of the micro-defects compared from cured kaolin matrix.     

Burkholderia thailandensis E264/pBMTL3-tdpR发酵生产抗癌药物ThailandepsinA的研究

在伯克氏菌Bth264野生株产新型抗癌药物Thailandepsin A以及调节基因tdp R正向调控Thailandepsin A生物合成的基础上,利用基因工程菌Bth264/p BMTL3-tdp R发酵生产Thailandepsin A,以提高产量。以0.5%乳糖为诱导剂,确定最佳诱导条件:发酵15 h添加乳糖,诱导时间6 h;通过单因素实验,确定葡萄糖和胰蛋白胨作为碳氮源、装液量65/250 m L以及接种量1%;同时结合优化发酵培养基进行发酵,Thailandepsin A产量达到252.14 mg·L-1,比优化前的产量提高56%;另外在发酵过程中,添加大孔树脂HP-20原位吸附产物,Thailandepsin A产量可达283.75 mg·L-1,比不加树脂提高13.8%;最后,基于RT-PCR和比较Ct值法,基因工程菌和野生菌相比,Thailandepsin A生物合成基因tdp B、tdp C1的转录水平分别提高11.4倍和6.0倍,对应的产量增加4.6倍,从而在很大程度上说明调节基因tdp R的过表达促进生物合成基因转录水平的提高以及产量的增加。     

The status of and opportunities for utility-scale battery storage in Australia: A regulatory and market perspective

Australia's electricity market is rapidly adding renewable energy generation. Utility-scale batteries could have a major role in facilitating these transitions; however, their deployment is still largely state-subsidized. We summarize the current and future roles for batteries from a legal-economic perspective in the context of Australia's electricity market framework. We find that the future of batteries in Australia is not only a function of the large-scale deployment of renewables, their cost development and the comparative future cost of competing gas turbines but also of national electricity market and state policy reforms focusing on reliability.     

Effect of Li2O on the crystallization behavior of CaO-Al2O3-SiO2-Li2O-Ce2O3 mold slags

The effect of Li₂O on the crystallization properties of CaO-Al₂O₃-SiO₂-Li₂O-Ce₂O₃ slags was investigated. With increasing the Li₂O content, LiAlO₂ and CaCeAlO₄ were the main crystalline phases. LiAlO₂ formed for the charge compensating of Li⁺ ions to [AlO₄^5?]-tetrahedrons, and CaCeAlO₄ formed as a result of the charge balance of Ce³⁺ ions, Ca²⁺ ions, and [AlO₆^9?]-octahedrons. Increasing the content of Li₂O to 10%, the crystallization temperature was the highest, and the incubation time was the shortest. The crystallization ability was strong due to the three factors of strengthening the interaction between ions and ion groups, decreasing the polymerization degree, and increasing the melting temperature. Further increasing the content of Li₂O, the crystallization performance was obviously suppressed, because the melting temperature and the force between the cations and the anion groups decreased.     

Effect of steel slag on 3D concrete printing of geopolymer with quaternary binders

A new type of 3D-printable ‘one-part’ geopolymer was synthesized with fly ash (FA), granulated blast furnace slag (GBFS), steel slag (SS) and flue gas desulfurization gypsum (FGD). The effects of SS content (0–40%) on the rheological properties, 3D-printability, mechanical anisotropy and reaction kinetics of geopolymer were investigated. The yield stress and plastic viscosity monotonically decreased with the increasing SS content. Contrarily, the geopolymer with 10% of SS presented better extrudability, buildability and mechanical strength than those with 0, 20%, 30% and 40% of SS. This was mainly attributed to the conflicting influence of SS on geopolymerization, of which the OH^? produced by hydration of SS raised the alkalinity of the reaction system and accelerated the dissolution of SiO₄^4? and AlO₄^5?, while the low reactivity prohibited the following polymerization process. Furthermore, the 3D-printed geopolymer presented more compact microstructure and less mechanical anisotropy thanks to the crosslinking of morphologically complementary products, including N(C)-A-S-H, C–S–H, AFt and CH, formed via synergistic reaction of FA-GBFS-SS-FGD system.