天然气吸附储存脱附过程的动态模拟

通过热动力学计算,认识了脱附过程当中储罐内温度剖面分布的典型特征:储罐轴心处的温度下降幅度最大。分析了脱附过程当中储罐壁的热交换、吸附剂的导热系数以及储罐内的初始压力对储罐内的温度剖面的影响。结论是加强储罐外壁的热交换、增大吸附剂的导热系数皆能改善吸附储罐内的温度剖面。     

Inhibition effect of carbon dioxide on the oxidation of hydrogen over a platinum foil catalyst

This paper investigates the catalytic ignition of the H₂/O₂/CO₂ mixture on platinum in a stagnation flow at atmospheric pressure experimentally and numerically. We measure the ignition temperatures of the gas mixtures flowing towards resistively heated platinum with various composition ratios and various diluent gases of N₂, Ar and CO₂. Compared with N₂ or Ar, the CO₂ dilution shows higher ignition temperature by about 50 K, even at the same composition ratio. The ignition temperature increase is proportional to the dilution ratio. Through the numerical simulation, it is illustrated that higher ignition temperature is caused by the adsorption of CO₂ and following dissociation on platinum surface, which was to date considered negligible in catalytic combustion.     

Investigation into polishing process of CVD diamond films

A new technique used for polishing chemical vapor deposition (CVD) diamond films has been investigated, by which rough polishing of the CVD diamond films can be achieved efficiently. A CVD diamond film is coated with a thin layer of electrically conductive material in advance, and then electro-discharge machining (EDM) is used to machine the coated surface. As a result, peaks on the surface of the diamond film are removed rapidly. During machining, graphitization of diamond enables the EDM process to continue. The single pulse discharge shows that the material of the coated layer evidently affects removal behavior of the CVD diamond films. Compared with the machining of ordinary metal materials, the process of EDM CVD diamond films possesses a quite different characteristic. The removal mechanism of the CVD diamond films is discussed.     

烧结NdFeB合金中的夹杂物

使用金相显微镜、扫描电镜及Ｘ射线能谱和波谱观察并分析了ＮｄＦｅＢ烧结材料中夹杂物的形态、数量和组成。磁粉制备后立即烧结的ＮｄＦｅＢ磁体中的夹杂物是氧化钕；而在不同环境条件下放置后的ＮｄＦｅＢ粉再烧结的材料中发现，除了氧化钕的夹杂物外，还有钕的氮化物及钕的氮氧复合夹杂物。同时还论讨了这些夹杂物对于ＮｄＦｅＢ材料磁性能的影响。     

Interaction of triton X-100 on silica: A relationship between surface characteristics and adsorption isotherms

Adsorption of Triton X-100 on various silica substrates has been investigated. A number of solids, including a natural quartz, this quartz washed with HCl acid and subsequently heated at 1273 K; two aerosils and one Kieselgel silicas were studied. These solids exhibit surface areas in the range of 5 to 430 m² g^?1. All the Triton adsorption isotherms display an S-shape at the adsorption temperatures studied (298 and 308 K). It has been found that the pretreatments of natural quartz (by water washing, impurities removed by acid and/or high temperature calcination) affect considerably the amounts of TX-100 adsorbed. Measurements of surface composition have been made by X-ray photoelectron spectroscopy (XPS) with particular emphasis on the presence of impurities and on the number of OH groups at the surface of the samples. The nature of the surface hydroxyl has also been studied by infrared spectroscopy. Furthermore, the specific number of hydroxyl groups on the surface of the silica samples has been determined by thermogravimetric analysis. Finally an attempt to correlate solid surface characteristics with adsorption isotherms has been developed.     

烧结工艺对液相合成（SrPb）TiO3基陶瓷热敏特性影响的研究

本文在液相合成（ＳｒＰｂ）ＴｉＯ３粉的基础上，研究了升温速率、保温时间、烧结温度及降温方式对（ＳｒＰｂ）ＴｉＯ３基陶瓷的Ｖ型ＰＴＣ热敏特性的影响。实验表明：升温速率对其热敏特性影响不大，保温时间和烧结温度的作用是一致的，具有一最佳范围。而降浊方式对材料的热敏特性影响较大。综合各因素的影响，本配方中，样品的烧结制度定为：以２００℃／ｈ的速率升温，在１２５０℃保温１ｈ，炉冷至９５０℃，保温０．５ｈ，再     

PP／SiO2／SBS共混复合材料性能的研究

通过加入增强剂、增韧剂、抗氧剂等添国剂可改善聚丙烯力学性能。以ＳｉＯ２为填料，丁苯橡胶（ＳＢＳ）为增韧剂，探讨ＳｉＯ２、丁苯橡胶含量对共混体系强度、韧性的影响，结果表明，在ＳＢＳ含量大于５％、ＳｉＯ２一小于１０％的范围内，可使ＰＰ／ＳｉＯ２／ＳＢＳ复合的拉伸弹性模量和冲击强度明显提高，其力学性能均为均衡。     

氢电弧等离子体法制备的纳米镍铈粒子的催化特性

利用氢电弧等离子法制备具有储氢特性纳米镍铈粒子，并在气相苯加氢反应中研究了其催化特性，发现其催化活性与储氢特性及表面层中ＮｉＣｅ合金存在有关，且具有高的选择性和热稳定性，这与纳米粒子独特的结构及铈的加入有关。     

Processing of Yttria-Alumina Coated Silicon Nitride Slips by Slip Casting

Si₃N₄powders coated with 6 wt% Y₂O₃and 4 wt% Al₂O₃were prepared by coprecipitation. The resulting powders were dispersed in water at different pH values and with addition of various amounts of ammonium polyacrylate (NH₄PA) to produce 32 vol% slips. The influence of the amount of NH₄PA solution added and pH on the rheological properties of 32 vol% coated Si₃N₄slips were studied. In addition, the sintered density of cast samples was determined and related to the degree of slip dispersion. The adsorption of the NH₄PA on the coated particle surface was rather high and the surface became saturated near 0.86 mg/m²at pH 9.2. High NH₄PA concentrations (1.7–3 wt%) were necessary to obtain well dispersed 32 vol% coated Si₃N₄slips at pH 9.2. The best stabilization was obtained with the addition of 2.3 wt% NH₄PA; in this condition, the viscosity reached a minimum value of 35 mPa.s at 100 s^–1. The slip viscosity increased with increasing pH from 9.2 to 10.2. Slips with low viscosities gave a more dense packing of cast samples and consequently higher sintered density values.     

低频电脉冲采油工程设备的开发与应用

低频电脉冲采油技术是通过升压、整流、充电等电路将电能蓄积在电容器中,通过触发电路,使能量瞬时释放,在井内液体中产生震动波,作用于地层,改善地层的渗流状况,达到提高采收率的目的。Ⅰ型设备在双河油田应用11井次,成功率72%;Ⅱ型设备在古城油田应用10井次,成功率90%。主要是由于Ⅰ型设备关键部件在处理油井时要放在井下,受高温、高压的影响及井下空间的限制,设备稳定性差、寿命短、能量小、效果差;Ⅱ型设备解决了上述问题,从而提高了试验成功率。