低碳钢热变形过程中铁素体的织构形成规律

利用背散射电子衍射取向成像技术定量分析了热模拟单向压缩条件下Q235碳素钢热变形时铁素体的织构形成规律。结果表明,在710℃纯铁素体热压缩过程中,形成〈100〉和〈111〉方向的线织构。〈111〉方向织构增强的速度较快,到应变为1.0时达最大值,然后随应变的加大而减弱;〈100〉方向织构在形变量较小时增强的速度较慢,在大应变时增强的速度很快。大应变时虽导致一定程度的动态再结晶,使铁素体晶粒细化,但组织不均匀,织构过强,造成强烈的各向异性。在奥氏体与铁素体两相区变形时,先共析铁素体因形变同样产生强烈的织构。随着形变温度的提高和先共析铁素体的减少,织构减弱。     

碳纤维增强混凝土构件正截面计算的双界限系数法

以材料的力学性能分析为基础，利用双界限系数将碳纤维增强混凝土受弯构件划分成三种正截面的破坏形态，对每一种破坏形态，建立了单、双筋矩形截面极限承载力的计算式，使碳纤维增强混凝土构件正截面计算与现行的规范相一致。     

Works of adhesion at the carbon fiber-liquid interface determined using a modified wetting technique

Works of adhesion W_SL between aqueous solutions with pH values in the range from 1 to 14 and carbon fibers from different sources, which were additionally treated in an inert atmosphere or in oxygen, were measured by use of a microbalance. These works of adhesion W_SL were found to show distinct stepwise dependencies on the pH value. The works of adhesion W_SL are attributed to dispersion interactions W_SL¹ and various acid-base interactions w_sl^ab—in the latter case between the acidic and basic surface groups of carbon and the various basic and acidic aqueous solutions.     

活性炭单柱提取肌苷新技术研究

活性炭单柱提取肌苷新技术研究李永泉，张进，姚恕，郑莲英，俞峰（杭州大学生物系杭州３１００２８）（浙江大学化工系杭州３１００２７）关键词：肌苷，提取技术，活性炭单柱１前言目前，国内肌苷发酵后处理工艺落后，在分离提取工序中肌苷损失严重，收率一般只有５０％...     

Asbestos replacement aspects: Modification of the fibre-matrix interphase in lonomer based composites

Asbestos fibres, of the chrysotile variety, and chopped carbon fibres were pretreated by an in-situ polycondensation technique eventually resulting in a polyamide coating on the fibre surface. Ionomer based composites containing either carbon or asbestos fibres in random in plane fibre orientation were prepared, and the influence of this coating process on the tensile properties was investigated. It was found that for the asbestos-filled composites the presence of the nylon 6,6 interlayer improves the tensile performance, especially at moderate polyamide depositions. This is not the case with the pretreated carbon-filled composites for which carbon fibres with higher polyamide contents are preferred. Combinations of the treated asbestos fibres with carbon and/or aramid fibres may be used to reduce the asbestos content in asbestos-only based engineering plastics.     

X-ray structure analysis and elastic properties of a fabric reinforced carbon/carbon composite

The effect of heat treatment on microstructure of a plain-weave carbon fabric reinforced carbon-carbon composite with phenolformaldehyde-derived carbon matrix was investigated by X-ray diffraction. The diffraction patterns were analysed by the least-square fitting program Carbonxs. After heat treatment from 1000 to 2800 °C the interplanar distance of (002) planes decreased from 3.488 to 3.420 Å and the lattice parameter in basal plane increased from 2.440 to 2.464 Å, respectively. Simultaneously, the coherent block size in the basal plane directions increased from 18 to 54 Å, which was accompanied by an increase of the fraction of organised carbon atoms from 0.50 to 0.85. The 002 diffraction profile of the composite was much narrower than the sum of peaks of the matrix and fabric alone. This can probably be caused by a better crystallographic ordering (or by a partial graphitisation) of the matrix in the composite. On the other hand, the composite Young’s modulus slightly decreased with the treatment temperature increasing from 2200 to 2800 °C in spite of the established strong improvement of fibre crystallinity and, therefore, fibre modulus. The mechanisms diminishing the modulus of composite (e.g. partial matrix graphitisation at the fibre/matrix interface and decreasing fibre/matrix contact area) probably prevailed over the increasing contribution of the fibre modulus.     

制氢尾气二氧化碳回收装置设计

对制氢尾气二氧化碳的回收装置进行了简捷设计，流程分析，并对换热装置的换热量和传热面积给出了算法和有关数据。     

碳纳米管/ABS树脂基复合材料的力学性能和雷达波吸收性能的研究

采用竖式炉流动法制备的碳纳米管经液相阳极氧化表面处理后增强ABS热塑性工程塑料。复合材料的力学性能研究显示:碳纳米管的加入有效提高了复合材料的拉伸性能,但材料的耐冲击性能下降。当碳纳米管含量为12 wt%时,复合材料的拉伸强度由45.00 MPa提高到69.96 MPa,杨氏模量由0.75 GPa提高到1.93 GPa。对碳纳米管/ABS复合材料的反射系数测定表明:复合材料在一定频率范围内有雷达波吸收性能。