13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

Reticulated Porous Multiphase Ceramics with Improved Compressive Strength and Fracture Toughness

A multiphase reticulated porous ceramic (RPC) as Si₃N₄–Al₂O₃–SiO₂ was fabricated by replication techniques. Proper volumes of additives and twice sinter- twice immerse process endow the RPC an excellent crack healing and submerging property. The compressive strength and fracture toughness improved owing to the crack bridging behavior. The existence of pores in struts in RPC blunt the crack tip and increased the external force needed to propagate the crack. The mechanisms play a beneficial role in enhancing the compressive strength and fracture strength. Si₃N₄ RPC with additives of 5%Al and 5% Al₂O₃ yielded the compressive strength of 9.8 MPa and fracture toughness of 0.3 MPa m^1/2.     

锌基合金模具的应用及探讨

本文分析了锌基合金模具制造及使用过程中容易出现热裂、翘曲、收缩的问题，并提出了解决这些问题的措施。     

65 Mn热轧带钢表面裂纹分析

分析了热轧带钢表面裂纹产生的原因，介绍了采取的工艺措施及其效果。     

基于高抗热震性能的陶瓷刀具材料的微观结构设计

本文以现有的抗热震断裂和抗热震损伤的评价理论为基础，通过对材料中微裂纹的长度进行预测，从而实现了对陶瓷刀具材料的抗热震性能的微观结构设计。根据此理论对现有材料的抗热震性能的进行预测，预测结果与实际的测量结果相符，验证了该理论的正确性。     

Characterization of Ceramic Composite-Membranes Prepared by ORMOSIL Coating Sol

Sol-gel methods offer many advantages over conventional slip-casting, including the ability to produce ceramic membranes. They are purer, more homogeneous, more reactive and contain a wider variety of compositions. We produced ormosil sol using sol-gel process under different molecular weight of polymer species [polyethylene glycol (PEG) ] in total system [Tetraethyl ortho silicate(TEOS)-polyethylene glycol (PEG)]. The properties of as-prepared ormosil sol such as,viscosity, gelation time were characterized. Also, the ceramic membrane was prepared by dip-coating with synthetic sol and its micro-structure was observed by scanning electron microscopy. The permeability and rejection efficiency of membrane for oil/water emulsion were evaluated as cross-flow apparatus. The ormosil sol coated Membrane is easily formed by steric effect of polymer and it improves flux efficiency because infiltration into porous support decreased. Its flux efficiency is elevated about 200(1/m2·h) compared with colloidal sol coated membrane at point of five minutes from starting test.     

Evaluation of Slow Crack Growth Resistance in Ceramics for High-Temperature Applications

The slow (subcritical) crack growth (SCG) resistance of Si₃N₄ and SiC ceramics has been evaluated by a stepwise loading test on bending bars precracked by Vickers indentation. Three highly refractory materials were selected for the evaluation: i.e., (1) high-purity Si₃N₄ sintered by hot isostatic pressing (HIP) without additives and (2,3) α - and β - SiC pressureless sintered with B and C addition. Under the hypothesis of linear elastic behavior at high temperature, which was found satisfied in the present materials, the SCG resistance was expressed in terms of initial stress intensity factor critical for SCG failure within a predetermined lifetime. The present method was found useful in shortening the testing time and consistent with other traditional fatigue tests (e.g., static-fatigue test): It is recommended as a screening test for materials under research and development. Among the materials tested in the present study, the highest SCG resistance up to 1440°C was found in the high-purity Si₃N₄ without additives.     

Numerical modelling for scattering of waves in three-dimensional cracked material

In this paper, a mathematical model is proposed for the problem of the scattering of plane waves in a three-dimensional cracked materials. Instead of obtaining closed-form solutions as in conventional theoretical analysis methods, this approach, called the Equivalent Nodal Force (ENF) method formulates the mechanical effects of cracks as an equivalent nodal force in a numerical procedure, and physically translates cracked material into an equivalent continuous one. Several mechanical relations between waves and cracks are evident from this method. Also the results of several numerical calculations are presented and these are compared with those obtained by the conventional methods.