高强度钢焊接裂纹检测及其成因分析

为了充分认识高屈强比、高强度低温材料焊接裂纹的敏感性，通过对NK—HIT—EN610U2L低合金高强度钢球罐支柱角焊缝裂纹的检测、解剖对比和成因分析，发现焊缝外表面缺陷与内部焊接缺陷存在一定关系，高应力设计部位比较突出，因此检测与焊接要引起高度注意。     

大型弹簧钢片开裂原因分析

为保证大型弹簧钢片在热处理过程中，不发生开裂和翘起度超差，重新制订了热处理工艺。通过增加高温回火、降低淬火温度、加快冷却速度等手段，获得了最好的效果。     

Fatigue crack growth resistance of SiC<Subscript>p</Subscript> reinforced Al alloys: Effects of particle size,particle volume fraction,and matrix strength

The main aim of this work was to study the effects of particle size, particle volume fraction, and matrix strength on the long fatigue crack growth resistance of two different grades of Al alloys (Al2124-T1 and Al6061-T1) reinforced with SiC particles. Basically, it was found that an increase in particle volume fraction and particle size increases the fatigue crack growth resistance at near threshold and Paris regimen, with matrix strength having a smaller effect. Near final failure, the stronger and more brittle composites are affected more by static modes of failure as the applied maximum stress intensity factor (K _max) approaches mode I plane strain fracture toughness (K _IC).     

Q345·C厚壁压力容器锥体变径段焊接裂纹分析及返修

针对Q345·C厚壁压力容器锥体变径段焊接后校圆过程中所出现的裂纹进行了分析,制定了合理的返修工艺,保证了焊缝返修的成功。     

脱硫塔501-EA的焊接修复

脱硫分厂脱硫塔焊缝缺陷威胁生产，修复后有效消除了隐患，延长设备使用寿命，现系统运行良好。     

环氧灌注料开裂问题及采取的措施

从断裂力学的角度分析了环氧树脂灌注料在灌封电子变压器时产生裂纹的原因，针对灌注料中存在的内应力及其他缺陷提出了预防和解决的具体措施。     

适用于扩展有限元裂缝计算的钢筋与混凝土粘结滑移关系

以定量分析钢筋与混凝土粘结滑移关系为目标,利用RCXFEHohai-P扩展有限元程序,计算采用不同粘结滑移公式时钢筋混凝土简支梁的最大裂缝宽度。结果表明,计算所得最大裂缝宽度各不相同,且都与《混凝土结构设计规范》(GB 50010—2010)所列最大裂缝宽度公式计算值存在差别。为此,基于GA-BP神经遗传网络,以规范最大裂缝宽度公式计算值为预测目标,反演得到适用于扩展有限元裂缝计算的粘结滑移公式,算例表明该公式能满足扩展有限元裂缝宽度计算要求。研究成果对提高扩展有限元裂缝分析的准确性具有一定的参考价值。     

裂解炉下集气锥形接管失效分析

通过化学成份分析、金相的宏微观考察、Manson-Haferd参数对锥形接管持久寿命的估算,以及热应力的计算,对锥形接管的失效原因进行了分析,认为是由温差应力导致失效。所以应该充分注意高温构件保温措施的有效性,避免非正常温差应力的产生。     

电除尘器绝缘子的设计与选择

根据电除尘器绝缘子的功能、工况条件等特点，分别从材质、外形尺寸等方面介绍了设计和选择的注意事项。为用户合理地选择电除尘器绝缘子提供了帮助。