Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Electromagnetic shielding properties of iron oxide impregnated kenaf bast fiberboard

The electromagnetic shielding effectiveness of kenaf fiber based composites with different iron oxide impregnation levels was investigated. The kenaf fibers were retted for removing the lignin and extractives from the fibers and magnetized. Using the unsaturated polyester and the magnetized fibers, kenaf fiber based composites were manufactured by the compression molding process. The transmission energies of the composites were characterized when the composite samples were exposed under the irradiation of electromagnetic (EM) wave with a variable frequency from 9 GHz to 11 GHz. Using the Scanning Electron Microscope (SEM), the iron oxide nanoparticles were observed on the surfaces and inside the micropore structures of single fibers. As the Fe content increased from 0% to 6.8%, 15.9% and 18.0%, the total surface free energy of kenaf fibers with the magnetizing treatments increased from 44.8 mJ/m² to 46.1 mJ/m², 48.8 mJ/m² and 53.0 mJ/m², respectively, while the modulus of elasticity reduced from 2875 MPa to 2729 MPa, 2487 MPa and 2007 MPa, respectively. Meanwhile, the shielding effectiveness was increased from 30–50% to 60–70%, 65–75% and 70–80%, respectively.     

Finite element analysis of fracture behavior in ceramics: Competition between artificial notch and internal defects under three-point bending

Evaluation of the nonlinear relationship between the surface defect size and fracture strength of ceramics is important for engineering applications. In this study, we aim to predict the apparent nonlinear relationship between the defect size and fracture strength of single-edge notched beams (SENBs) using the finite element method. Specifically, we applied the methodology for predicting fracture strength from microstructure distribution data (relative density, pore size, aspect ratio, and grain size) to a finite element analysis (FEA) model in which the shape and size of the initial defects are defined at notch locations. By reproducing the apparent nonlinearity caused by the competition between the surface and internal defects within the framework of linear elastic fracture mechanics, the effectiveness of the FEA methodology for the evaluation of strength scatter and allowable crack size in ceramics was demonstrated.     

基于小波变换的分数阶微分算法在肝脏肿瘤CT图像纹理增强中的应用

图像纹理增强过程中容易丢失平滑区域纹理细节，而分数阶微分增强虽然能够非线性保留平滑区域纹理细节，但对频率分辨率敏感。针对这个问题，提出一种基于小波变换的分数阶微分纹理增强算法，应用于平扫计算机断层扫描（CT）图像的肝脏肿瘤区域的纹理增强。首先，通过小波变换将图像感兴趣区分解成多个子带分量；其次，基于分数阶微分定义构造一个带补偿参数的分数阶微分掩膜；最后，使用该掩膜与每个高频子带分量进行卷积并利用小波逆变换重组图像感兴趣区。实验结果表明，该方法在使用较大分数阶次显著增强肿瘤区域的高频轮廓信息的同时，有效地保留了低频平滑的纹理细节：增强后的肝细胞癌区域与原区域相比，信息熵平均增加36.56%，平均梯度平均增加321.56%，平均绝对差值平均为9.287；增强后的肝血管瘤区域与原区域相比，信息熵平均增加48.77%，平均梯度平均增加511.26%，平均绝对差值平均为14.097。     

一种抗运动干扰的实时心率提取方法

针对基于容积脉搏波（PPG）提取运动心率时，传统心率提取算法由于运动噪声干扰使测量结果误差大、实时性不好的问题，提出一种抗运动干扰的实时心率提取方法。该方法通过实时小波去噪，同时结合三轴加速度信号（ACC）对运动进行分类训练，计算各运动状态心率增益，对实时心率值进行补偿。实验结果表明，通过与同时采集的ECG信号计算出的实时心率进行对比，绝对误差率仅为1.2%左右。相比传统心率提取算法，该算法具有抗干扰性强，实时准确的特点。     

B Cells with a Senescent-Associated Secretory Phenotype Accumulate in the Adipose Tissue of Individuals with Obesity

Senescent cells accumulate in the adipose tissue (AT) of individuals with obesity and secrete multiple factors that constitute the senescence-associated secretory phenotype (SASP). This paper aimed at the identification of B cells with a SASP phenotype in the AT, as compared to the peripheral blood, of individuals with obesity. Our results show increased expression of SASP markers in AT versus blood B cells, a phenotype associated with a hyper-metabolic profile necessary to support the increased immune activation of AT-derived B cells as compared to blood-derived B cells. This hyper-metabolic profile is needed for the secretion of the pro-inflammatory mediators (cytokines, chemokines, micro-RNAs) that fuel local and systemic inflammation.     

Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Experimental study to assess the effect of carbon nanotube addition on the through-thickness electrical conductivity of CFRP laminates for aircraft applications

The present paper tests experimentally the through-thickness electrical conductivity of carbon fiber-reinforced polymer (CFRP) composites laminates for aircraft applications. Two types of samples were prepared: Type A samples with carbon nanotubes (CNTs) and Type B samples without CNTs. During the electrical experiments, electrical currents of several mA were injected through the specimens. Electrical resistance was monitored simultaneously in order to deduce the changes in the through-the-thickness electrical conductivity caused by the addition of CNTs. Improvement of electrical conduction by two orders of magnitude was achieved through the addition of 1 wt% carbon nanotubes as compared to classic CFRP without CNTs. For moisture saturated samples, the influence of moisture absorption on such measures was found to be negligible.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Restructuring bank networks after mergers and acquisitions: A capacitated delocation model for closing and resizing branches

During restructuring processes, due to mergers and acquisitions, banks frequently face the problem of having redundant branches competing in the same market. In this work, we introduce a new Capacitated Branch Restructuring Model which extends the available literature in delocation models. It considers both closing down and long term operations׳ costs, and addresses the problem of resizing open branches in order to maintain a constant service level. We consider, as well, the presence of competitors and allow for ceding market share whenever the restructuring costs are prohibitively expensive.We test our model in a real life scenario, obtaining a reduction of about 40% of the network size, and annual savings over 45% in operation costs from the second year on. We finally perform a sensitivity analysis on critical parameters. This analysis shows that the final design of the network depends on certain strategic decisions concerning the redundancy of the branches, as well as their proximity to the demand nodes and to the competitor׳s branches. At the same time, this design is quite robust to changes in the parameters associated with the adjustments on service capacity and with the market reaction.