Effects of secondary carbide precipitation and transformation on abrasion resistance of the 16Cr-1Mo-1Cu white iron

The relationship between secondary carbide precipitation and transformation of the 16Cr-1Mo-1Cu white iron and abrasion resistance were investigated. The results show that secondary carbide precipitation and transformation at holding stage play an important role in the hardness and abrasion resistance. After being held for a certain time at 853 K for subcritical treatment, the grainy secondary carbide, (Fe,Cr)₂₃C₆, precipitated first and then Fe₂MoC or MoC carbides precipitated in the alloy, both of which improve the bulk hardness and abrasion resistance of the alloy. The reasons for these improvements are the secondary carbide precipitates from the austenite and the retained austenite transforms into the martensite, both make the matrix strengthen. So the matrix has more effective support to the harder eutectic carbide against exterior abrasion. With expanding the holding time, the in situ transformation from the granular (Fe,Cr)₂₃C₆ carbide into laminar M₃C carbide causes the formation of the pearlitic matrix and an associated decrease of the alloy abrasion resistance.     

SiCp/AlCuMgAgCe复合材料的显微组织与力学性能

采用压铸浸渗法制备了53%SiCp增强的AlCuMgAgCe基复合材料。通过X射线衍射、金相观察、扫描电镜与透射电镜分析以及力学性能测试,研究了SiCp/AlCuMgAgCe复合材料的显微组织与力学性能。结果显示,在AlCuMgAgCe合金中加入53%体积分数的SiC颗粒后,复合材料的组织致密,分布均匀,其断裂方式包括界面脱开、基体韧断和增强体开裂,SiC颗粒与基体之间并没有发生明显的界面反应。在185℃的等温时效析出过程中,复合材料的析出相主要由Ω相和少量θ′相组成。     

氮对高纯奥氏体不锈钢耐晶间腐蚀性能的影响

采用电化学、化学浸渍、俄歇电子能谱分析、物理化学相分析等方法研究了氮对高纯奥氏体不锈钢000Cr19Ni14耐敏化态晶间腐蚀和非敏化态晶间腐蚀性能的影响,并探讨了其作用机理.结果显示,高纯奥氏体不锈钢加氮合金化(≤0.20%)基本上消除敏化态晶间腐蚀,敏化处理不会引起晶界贫铬;当氮含量不超过0.087%时,对非敏化态晶间腐蚀影响很小,而超过0.087%时,由于在晶界氮元素的偏聚以及氮化铬的析出加速非敏化态晶间腐蚀.     

下贝氏体碳化物源的高温电镜观察

在JEM-1000超高压透射电镜高温台中对40CrMnSiMoV钢310℃等温所得下贝氏体进行定点动态观察的结果表明,原先无碳化物的贝氏体铁素体内,在高于等温转变温度经一定时间回火后,析出了典型下贝氏体碳化物。这说明下贝氏体铁素体是过饱和碳的。奥氏体中也可析出碳化物,但不具备下贝氏体碳化物的典型特征。     

Simultaneous Internal Oxidation and Nitridation of Ni–Cr–Al Alloys

A series of Ni–Cr–Al alloys was subjected to thermal cycling to 1100°C in air for up to 260 1-hr cycles. All alloys exhibited poor corrosion resistance. Repeated scale spallation led to subsurface alloy depletion in aluminum and, to a lesser extent, chromium. This caused transformation of the prior alloy three-phase structures (-Cr+-NiAl+-Ni) to single-phase -nickel solution. Destruction of the external scale allowed gas access to this metal, which was able to dissolve both oxygen and nitrogen. Inward diffusion of the two oxidants led to development of a complex internal-precipitation zone: Al₂O₃ and Cr₂O₃ beneath the surface, followed by Al₂O₃, then AlN, then AlN+Cr₂N, and, finally, AlN alone in the deepest region. This distribution is shown to reflect the relative stabilities of the precipitates and the higher permeability of nitrogen. Diffusion-controlled kinetics were in effect initially, but mechanical damage to the internal-precipitation zone led to more rapid gas access and approximately linear kinetics in the long term.     

连续碳分CO2吸收率分析及探讨

本文简述了CO2 气体吸收率的测定原理 ,着重分析了影响连续碳分CO2 气体吸收率的因素 ,提出了提高连续碳分CO2 气体吸收率的途径     

纳米氧化铝粉体的特殊液相沉淀法制备

本文通过液相反应胶粒析出机理分析，首次采用快速高强度机械混合液相沉淀法技术制备了小粒径(平均2nm)无定型氢氧化铝纳米粉体。经1250℃焙烧，获得α相纳米氧化铝。在制备过程中，采用适当的混合强度和反应液浓度可加强浆料过滤性，从而大大节省时间，得到小粒径高温相纳米氧化铝粉体。     

Al、V微合金高强度船板的研究

采用Gleeble-1500热模拟试验机测试了2种微合金钢(Al、Al V)经1150℃加热、20％压缩变形条件下的显微组织状态，结果表明，Al、V复合强化的试验钢以2℃／s速度冷却时，钢中出现针状铁素体。冷却速度为5℃／s时出现贝氏体，而Al强化钢中出现针状铁素体的冷速要达到5℃／s，因此建议生产含V钢时冷速控制在1～5℃／s。     

MICROSCOPIC PHASE-FIELD SIMULATION COUPLED WITH ELASTIC STRAIN ENERGY FOR γ′(Ni3Al) PRICIPITATION IN Ni-Al ALLOY

基于微观相场动力学模型和微观弹性能理论,对Ni-Al合金中沉淀相Ni3Al(γ′)形貌演化、早期沉淀机制和后期粗化过程进行了原子层面的计算机模拟.结果表明:沉淀过程中γ′相形貌由早期随机分布的圆形或不规则状逐渐向方形转变,其排列的取向性也越来越明显,最后形成周边圆滑的长方块状颗粒,沿[10]和[01]弹性"软"方向规则排列.弹性应变能作用下的粗化过程遵循优先选择的原则,位于弹性"软"方向上的颗粒不断长大和粗化,位于弹性"软"方向外的颗粒逐渐消失,沉淀后期在基体中形成高度择优取向的微观组织.低浓度Ni-Al合金中γ′相的早期沉淀机制为非经典形核长大机制,其演化序列为:过饱和固溶体→非化学计量比有序相→化学计量比平衡γ′相→长大.