This article reviews the evidence and theory pertaining to a form of perspective-taking failure--a difficulty in setting aside the privileged information that one knows to be unavailable to another party. The authors argue that this bias (epistemic egocentrism, or EE) is a general feature of human cognition and has been tapped by 2 independent and largely uncommunicating research traditions: the theory-of-mind tradition in developmental psychology and, with more sensitive probes, the "heuristics and biases" tradition in the psychology of human judgment. This article sets the stage for facilitating communication between these traditions as well as for the recognition of EE's breadth and potential interdisciplinary significance. The authors propose a life-span account and a tentative taxonomy of EE; and they highlight the interdisciplinary significance of EE by discussing its implications for normative ethics. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

底支承对小口径反射镜镜面变形的影响

论述了运用有限元技术研究镜面变形的方法及分析底支承在不同口径，焦比、厚径比和相对支承半径时镜面变形的技术；在取得的相互关联的最大镜面变形数据基础上，研究了影响小口径反射镜底支承镜面变形的因素。     

φ140mm套管拔套侧钻工艺技术在濮城油田的应用

濮城油田开发后期,因事故导致损坏的井数不断增多,不仅损失了相当一部分储量,而且严重威胁着油田的发展。针对这一问题,应用拔套侧钻工艺技术对有潜能的事故井进行侧钻更新,投产后取得了良好的效果,成为油田增储上产和挖潜剩余油的重要手段,同时也为解决困扰油田发展的难题找到了好的方法。     

Q195冷轧板材轧制困难原因分析

针对部分Q195冷轧板材存在轧制困难的现象，进行了现场检验与分析。带状组织、混晶现象严重导致变形强化系数偏高是造成轧制困难的主要原因。     

橡胶Mooney—Rivlin模型材料系数对轴向刚度影响分析

在橡胶小变形范围内，采用理论推断的方法，得到在相同硬度下橡胶Mooney—Rivlin模型材料系数由C2／C1决定的关系式。并采用ABAQUS有限元软件分析的方法，结合橡胶轴向刚度常规解，分析了C2／C1不同值对橡胶轴向刚度的影响进行，结果显示其影响呈现一定规律性。     

锅炉未焊透椭圆接管结构应力数值分析

应用有限元法对未焊透的椭圆接管结构进行了应力数值分析,并应用压力容器分析设计法,对该结构进行了疲劳分析,得出结构因未焊透缺陷导致疲劳破坏。     

Plane Problem for Layered Composites with Periodic Array of Interfacial Cracks Under Compressive Static Loading

The current paper addresses the problem of 2-D modelling of the onset of failure process in a layered composite with periodic array of interfacial cracks under static compression along layers. The statement of the problem is based on the most accurate approach, the model of piecewise-homogenous medium. The condition of plane strain state is considered. The shear and the extensional buckling modes are examined. The laminae are modelled by transversally isotropic material (a matrix reinforced by continuous parallel fibres). The complex non-classical failure mechanics problem is solved utilizing finite element analysis. It is found that the 0°-plies volume fraction, the crack length and the mutual position of cracks influence the critical strain in the composite.     

P–I diagram method for combined failure modes of rigid-plastic beams

Closed-form solutions of pressure-impulse (P–I) diagrams for simply supported and fully clamped rigid-plastic beams subjected to impact load are developed. Two failure categories, i.e., bending failure and shear failure, are considered and the responses of the beams are analyzed based on five transverse velocity profiles. With proper failure criteria, the critical P–I equations for bending and shear failure are derived. After the simplification of the critical P–I equations, the influences of the shear-to-bending strength ratio and the boundary conditions on the P–I diagrams are discussed. The results are compared with those based on a single-degree-of-freedom (SDOF) model. It is shown that the proposed P–I diagram method can be conveniently applied to assess beam damage extents and damage patterns. Especially, the P–I diagrams have good agreement with those based on an elastic, perfectly plastic model when severe damage occurs.     

Bruchanalyse an Hohlgläsern

Failure analysis of hollow glasses The failure analysis is very important to clarify damages of hollow glasses. Damages of glass bottle through over pressure are very often linked with damages to persons. This is the reason why the causal research is from particular importance. Different surface characteristics of glass fragments as well as the fracture pattern give hints to the direction of the crack, the stress just before breakage and the reason of stress. A reconstruction of the bottle is a further helpful instrument for cause studies. The difference of the various characteristics of the surface will be explained. Further on there will be discussed different reasons and mechanism of fracture.     

旋转控制头胶芯失效形式分析

在欠平衡钻井过程中，胶芯是旋转控制头核心密封元件，通过对Williams 7100型旋转控制头胶芯失效形式进行分析，并提出了相应的对策，旨在推动胶芯的国产化进程。