复相Al2O3/SiCw陶瓷与不锈钢钎焊接头的界面反应和反应产物

采用氩气保护下活性金属钎焊法对碳化硅晶须增韧氧化铝陶瓷（Al2O3/SiCw）与不锈钢（1Cr18Ni9Ti)进行了钎焊，所用钎料为Ag-Cu-Ti3活性钎料，通过X－射线衍射仪（XRD）对界面的反应产物进行了物相分析，并用能谱仪（EDAX）分析了界面元素组成，结果表明，钎焊接头界面的反应十分复杂，反应产物多种多样，主要有TiO,Ti2O,TiC,Fe2Ti4O,Ni3Ti,AlTi等物质，界面反应层按Al2O3 SiC/TiO AlTi TiC/TiO2 Fe2Ti4O/Ag-Cu的规律过渡。     

Joining alumina to inconel 600 and UMCo-50 superalloys using an Sn10Ag4Ti active filler metal

Alumina ceramics were brazed to Inconel 600 and UMCo-50 superalloys at 900 °C for 10 min using an Sn10Ag4Ti active filler metal. The brazing filler showed good wettability on alumina and superalloys. The flexural strengths were 69 and 57 MPa for alumina/Inconel 600 and alumina/UMCo-50 joints, respectively. In both cases, the brazed specimens fractured along the Sn10Ag4Ti/superalloy interfaces after four-point bending tests. Electron probe microanalysis (EPMA) elemental mapping revealed that the Ni of Inconel 600 and the Co of UMCo-50 dissolved into Sn10Ag4Ti filler metal, which serves to reinforce the weak Sn10Ag4Ti matrix.     

钨粉分级在粗晶碳化钨粉生产中的应用

晶粒粗大且均匀的碳化钨粉一直是粗晶硬质合金制造者的迫切需要,本文通过对钨粉分级再碳化工艺的研究,有效解决粉末夹粗夹细现象,制造粗晶碳化钨粉。试验表明,此方法制造的粗晶合金结构均匀,性能优越。     

复合钎料的特点及研究现状

为缓解钎焊接头的列余应力，人们提出了在普通钎料中加入一定体积比的作为增强相的各种形态的高温合金、碳纤维及陶瓷颗粒等形成复合钎料方法。该钎料不仅具有较好的填缝能力，同时获得的钎缝接头具有良好的高温强度和抗冲击性能，复合钎料钎焊方法是一种很有潜力的钎焊陶瓷与金属的方法。     

Low-melting-point titanium-base brazing alloys—part 1: Characteristics of two-, three-, and four-component filler metals

The melting point, microstructure, phase, and electrochemical behavior of Ti-21Ni-15Cu alloy, together with two-, three-, and four-component low-melting-point titanium-base brazing alloys, are presented in this paper. Five filler metals were selected for the study, in which melting points were measured by differential thermal analysis, phases identified by x-ray diffractometry, and corrosion behaviors tested by potentiodynamic polarization. The experimental results show that the three-component Ti-15Cu-15Ni and the newly developed Ti-21Ni-14Cu alloys exhibit the combination of lower melting point and superior corrosion resistance compared to the two-and four-component titanium alloys, 316L stainless steel, and a Co-Cr-Mo alloy in Hank’s solution at 37 °C. On a short time basis, the presence of Ti₂Ni and Ti₂Cu intermetallics in the Ti-15Cu-15Ni and Ti-21Ni-14Cu alloys should not be preferentially dissolved in galvanic corrosion with respect to the dissimilar Ti-6Al-4V alloy.     

床沙粒径及级配对非均匀沙起动的影响分析

对Wu W.等的荫暴系数计算方法进行了修正,根据滚动起动模型建立了以荫暴系数为主要参数的起动底流速公式,在此基础上理论探讨了暴露程度、床沙各分组泥沙粒径及其质量比对泥沙起动的影响,并论述了非均匀沙起动中完全暴露、完全荫蔽和极限跃移3种极限起动情况。结果表明:1非均匀沙起动底流速随着荫暴系数的增大而减小,荫暴系数越大,泥沙越容易起动;2在由两种粒径泥沙组成的非均匀沙中,粗颗粒的荫暴系数在定义域上均随着细颗粒床沙比例和粗细颗粒比例的增大而增大,即细颗粒比例越大,粗细颗粒间粒径差异越大,粗颗粒越容易起动;细颗粒的荫暴系数在定义域上随着细颗粒床沙比例的增大而增大、粗细颗粒比例的增大而减小,即细颗粒的比例愈大,细颗粒愈容易起动,且起动规律渐趋于和均匀沙的相仿,粗细颗粒粒径相差愈大,细颗粒受到的荫蔽作用愈显著,其起动流速也愈大。     

人工大理岩骨料应用几个关键问题与对策分析

国内某大型水电工程的混凝土骨料母岩为洞挖大理岩渣料,应用中面临岩性较脆、料源均一性欠佳、毛料含水率大、粗骨料裹粉严重且级配较差、干法生产的人工砂石粉含量超标严重等诸多问题。大理岩人工骨料大规模用于大型水电工程,并采用干式制砂系统,在国内尚属首次。根据工程建设中长期的跟踪检测数据,针对上述问题进行了深入剖析,提出了增加缓降装置和二次筛分及水洗装置、采用胶带运输、调整主筛分车间筛网、筛除毛料中大于20 mm的颗粒、调整风选车间参数等相应对策。在取得较好的技术效果的同时,为类似工程的进一步大范围应用积累了经验。     

Al-20Cu-9.6Si-xEr钎料对SiC_p/A356复合材料真空钎焊接头组织与性能的影响EI北大核心CSCD

采用不同铒含量的7组Al-20Cu-9.6Si-xEr钎料分别对SiCp/A356复合材料进行了真空钎焊。利用扫描电镜和能谱分析等方法对接头微观组织进行了观察和分析。通过剪切实验对钎焊接头的抗剪强度进行了测定,并对剪切断口的微观形貌进行了观察。结果表明：添加稀土后,钎焊接头的抗剪强度明显提高。当w（Er）=0%时,钎缝处SiC颗粒聚集严重,接头强度为43.5MPa;当w（Er）=0.05%时,钎缝边界无SiC颗粒的聚集,接头强度最高,达到68.6MPa;当w（Er）=0.1%-0.4%时,钎缝处SiC颗粒聚集趋势减弱,接头强度值在45.3-50.5MPa之间;当w（Er）=0.5%时,SiC颗粒分布在钎缝内部,接头强度明显提高,达到62.2MPa。     

连接SiCp/6063Al复合材料的Al-Si-Cu-Ce-Ti箔状钎料制备及其性能研究

采用快凝甩带技术制备了6组不同Ti含量的(Al-10Si-20Cu-0.05Ce)-xTi急冷箔状钎料,并对SiCp/6063Al复合材料进行真空钎焊,然后对钎料及接头的显微组织和性能进行分析。结果表明,急冷箔较常规铸态钎料的组织细小、均匀;固、液相线降低,熔化区间变窄;随着Ti含量的增加,急冷箔中片状Al-Si-Ti金属间化合物相增多,导致钎料脆性增加;6组钎料在复合材料上润湿性较差,但在6063Al合金上润湿性良好。在580℃钎焊温度、保温30min条件下,采用1%Ti含量急冷箔状钎料成功连接了SiCp/6063Al复合材料,钎焊接头组织致密、完整,急冷箔状钎料与6063Al合金基体连接界面可进行充分的冶金结合,且接头剪切强度达到104.9 MPa;钎焊前采用夹具增加接头压力可显著提高接头的连接质量。     

耐候防腐涂料的研究进展

综述了耐候防腐涂料的研究进展和提高常温固化防腐涂料耐候性能的几种途径,主要包括耐候型成膜物质的制备与改性,如含氟类、有机硅类、丙烯酸类等树脂,以及耐候型功能颜填料的添加,如钛白粉、纳米导电聚合物等填料和各类光稳定剂等,并对提高常温固化防腐涂料耐候性能可能的方法进行了展望。