分析检验拉拔过程中发生断裂的65MnTi盘条的金相组织和断口形貌，得出结论；65MnTi金条发生断裂的原因是热轧后冷却速度过快，金相组织中出现了低温转变组织──马氏体组织；而理想的组织应为京氏体；并且最佳冷却速度为5℃／s左右。     

Experimental and numerical investigation of fracture in double-edge notched steel plates

Double-edge notched (DENT) steel plates were pulled until complete fracture and several experimental observations were made (using profilometry and scanning electron microscopy). The essential work of fracture (EWF) model was found to be well verified. Numerical simulations—up to the maximum load only—of some experiments were performed using the finite element method (FEM), and incorporating geometric and material non-linearities (large deformation elasto-plasticity). Some experimental measurements were compared with the corresponding numerical computations and excellent agreement was found.     

铈和磷对中碳锰钢低温回火脆性的影响

本文采用冲击试验和断口扫描电镜，俄歇谱分析等方法，研究了铈对不同磷含量的中碳锰钢低温回火脆性的影响。结果表明，磷在奥氏体晶界偏聚是导致含磷锰钢产生低温回火脆性的原因，而铈的加入，可减少磷的偏聚程度，增加回火马氏体的冲击值，从而降低中碳锰钢的回火脆性。     

THE FRACTURE MECHANISM OF 475°C EMBRITTLEMENT IN A DUPLEX STAINLESS STEEL

The mechanism of “475°C embrittlement” of a duplex stainless steel was investigated using finite element modelling of the stress distribution at brittle fracture initiation. Brittle fracture initiated at a critical shear stress, which increased with ferrite hardness. The fracture stress was affected by the duplex microstructure. Fracture was nucleated by deformation twins, which were identified using electron back-scatter diffraction. The ductile-to-brittle fracture transition was sensitive to age-hardening and could be described simply by the effect of age-hardening and test temperature on the yield stress.     

双重孔隙介质油藏中的吸渗排油作用

利用美国SSI公司研制的COMPN模拟软件对双重孔隙介质油藏一种重要的开采机理 吸渗排油进行了模拟研究,考察了一个基质岩块为四周裂缝所包围时.在驱动压力和毛管压力的不同平衡(驱动压力和毛管压力的相对大小)关系下的水驱油采收率和水驱油效率的变化规律.     

On basic definitions of unified fracture mechanics terminology

The adoption of unified fracture mechanics terminology (UFMT) will promote efficient communication between specialists in different fields of fracture research, harmonization of national and international standards relating to fracture mechanics, and last but not least improvement of the existing methodology for teaching and education in fatigue and fracture. In this paper the definitions of some basic and related terms included in different standards on fracture mechanics terminology are confronted with one another. Alternative definitions of the same terms are offered. By this strategy the author tries to show that the definitions of basic and related terms appropriate for the UFMT should emerge as a consequence of harmonizing a crack model with an actual crack and then both taken together with a fracture model, laboratory test methods, and failure assessment codes.Published in Problemy Prochonsti, No. 1, pp. 17–29, January, 1996.This paper is published as a matter of discussion.     

用小尺寸R－CT试样研究核压力容器钢断裂韧性及与Charpy试样的比较

提出了一种用双边带深侧槽的小尺寸圆形紧凑拉伸试样评定核压力容器（ＲＰＶ）钢断裂韧性的单试作试验方法，给出了用该方法测定的两个厂家生产的核压力容器用Ａ５０８ＣＬ３钢的断裂韧性参数，还与Ｃｈａｒｐｙ试样的试验结果及大尺寸标准试样的试验结果进行了比较。研究结果表明：用双边带深侧槽的小尺寸Ｒ－ＣＴ试样测得的断裂韧性值比相同恻槽深度预制疲劳裂纹Ｃｈａｒｐｙ试样的测试值更接近有效断裂韧性值，所以，用于核压力容器断裂韧性的监测是可行的。     

考虑初始椭圆度的套管抗载能力分析

针对套管的不同初始椭圆度建立了套管、水泥环、地层平面应变力学模型。分析认为，在非均匀地应力作用下，套管内壁的径向变形较大，抗载能力明显降低，破坏主要是由地下非均匀地应力引起的；随着初始椭圆度的增加，在地应力作用下套管各部位产生的应力分布不均程度增大，使得套管抗外载能力减弱。建议在生产和使用过程中应严格将套管椭圆度控制在规定的范围内，从而提高套管的抗载能力。     

-50℃用20MnMoD钢锻件及其焊接接头性能

研究了-50℃的20MnMoD钢锻件及其焊接接头在不同热处理状态时的综合力学性能。结果表明,-50℃的20MnMoD钢锻件具有良好的低温韧性,可与-50℃级正火型低温压力容器钢15MnNiNbDR配套使用。