Q-52-51型摩托车车轮轮毂开裂原因分析

检测和分析了Q-52-51型摩托车车轮轮毂从材料成分，力学性能和金相组织。结果表明，轮毂在径向冲击检测时开裂的主要原因是镁含量偏高，以及热处理加热温度高造成组织过热所致。     

Penetration treatment of plasma-sprayed ZrO2 coating by liquid Mn alloys

The penetration phenomena of liquid manganese (Mn) alloy into porous ZrO₂ (8 vvt % Y₂O₃) coating plasma sprayed on SS400 steel substrate was studied by heating in a vacuum atmosphere. The improvement in mechanical properties of the coating by heat treatment with liquid Mn alloys was examined. Liquid Mn alloys, such as Mn-Cu, Mn-Sn, and Mn-In, rapidly penetrated the coating and formed a chemical bond between the coating and the substrate. The densification of the ZrO₂ coating occurred when ZrO₂ particles were sintered with liquid Mn alloys that penetrated the porous coating. The dense coating was free of porosity, and its hardness increased after heat treatment with Mn alloys, compared with assprayed ZrO₂ coating. Moreover, the fracture toughness of the coating reached the same levels as those of sintered yttria-stabilized PSZ.     

洗发水瓶盖注射模设计和工艺分析

注射成型是重要的塑料成型方式,成型中工艺参数对塑件质量有重要影响。通过对洗发水瓶盖的工艺分析,确定零件的生产方案并设计了二次分型注射模具。在模具中设计了螺纹脱模机构、通过控制运动方向的特殊弧形侧抽芯机构、浇注系统、螺纹转动保险机构和温度控制系统的结构设计,对该注射模具的设计过程进行了全面的阐述。     

大塑性变形珠光体钢丝低温球化退火工艺研究

研究了70Nb和50Cr两种金属针布合金钢丝经大塑性变形后在低温下球化退火的工艺及组织。结果表明，在冷却速度一定的条件下，变形量为96．6％的70Nb合金钢丝在730℃保温240min球化效果较好，球化等级达到3．5～4级；变形量为84．6％的50Cr合金钢丝在730℃保温随保温时间延长球状碳化物逐渐长大．但尺寸始终保持在1～1．2μm。     

二次喷丸42CrMo钢表面完整性的数值模拟研究

目的探究二次喷丸工艺参数对42CrMo钢零件表面完整性的影响规律。方法建立三维随机喷丸有限元模型,并通过实验验证有限元模型预测残余应力的准确性。将一次喷丸后零件的表面形貌和应力应变结果作为初始状态导入到二次喷丸模型中,构建出二次喷丸预测模型。分析二次喷丸参数对42CrMo钢零件表面残余应力场、表面粗糙度以及等效塑性形变场的影响情况。结果二次喷丸后,42CrMo钢零件近表层(0～100μm)的残余压应力值均比初始状态有所增加。增加二次喷丸覆盖率对表面残余应力的提升作用最为明显,最大可比初始状态提高63.3%,而增加二次喷丸直径对残余应力的改善效果最不明显。过度增加二次喷丸速度会导致表面粗糙度明显增加,提高二次喷丸覆盖率可显著降低表面粗糙度,覆盖率为300%时,粗糙度比初始状态减小了14.4%。表层PEEQ值随着二次喷丸速度、弹丸直径和覆盖率的增加而增加,但当二次喷丸速度、弹丸直径和覆盖率增加到一定程度后,表层PEEQ值会趋于饱和。结论二次喷丸预测模型揭示了二次喷丸参数与42CrMo钢零件表面完整性之间的影响规律,为二次喷丸的工业应用提供了一定的参考意义。     

用微型杯突试验法评价和估算钢的强度和塑性

采用一种新型在线无损检测的试验方法--微型杯突试验法研究电站锅炉管道用9Cr-1Mo-V-Nb-N钢的强度和塑性.结果表明:该试验方法与常规的单轴拉伸试验之间有很好的可比性,并且通过微型杯突试验的结果估算9Cr-1Mo-V-Nb-N钢的屈服强度与抗拉强度及伸长率,给出相应的经验公式.同时在采用微型杯突试验法估算9Cr-1Mo-V-Nb-N钢的塑性时,首次提出断裂挠度率的概念.     

流动液体中夹杂物超声去除的影响因素

以高密度聚乙烯（HDPE）颗粒和水形成的悬浮液为研究体系。考察了有无超声波作用下。介质流量、夹杂物数量以及夹杂物的粒径对总去除率、上浮去除率、壁面粘附去除率的影响。实验结果表明，在短时间内（30s)超声波对流动液体中的夹杂物具有明显的去除效果。总去除率达93％。夹杂物的总去除率随着超声波输入电功率的增大而提高；超声波对较多数量或较大粒径的夹杂物去除效果更显著。超声波作用下流动液体中的夹杂物比静止液体中的更容易去除。超声波对流动液体中夹杂物去除效果的去除机理主要是通过气泡捕获夹杂物，超声空化效应产生直接包裹夹杂物的气泡以及通过夹杂物碰撞凝聚使夹杂物容易上浮实现去除。     

Corrosion behavior of wire-arc-sprayed stainless steel coating on mild steel

The corrosion characteristics of a wire-are-sprayed stainless steel coating on mild steel have been investigated in regards to atomizing gases and sealing treatment. Salt spray test was performed. The corrosion behavior of the coating was observed under a microscope succesively through a cycling test of wetting and drying in a salt solution. The sealing-treated coating was found to rust faster compared with the non-sealing-treated coating; it protected the mild steel substrate against corrosion, but even it deteriorated the coating itself due to the interruption of the substrate as an anode. The air-atomized coating ruste more heavily than the nitrogen-atomized one. Four different phases were observed in the coating in regards to corrosion behavior; namely, chromium-based oxide, iron-based oxide, chromium-depleted metallic phase, and stainless steel matrix phase. It was found that the chromium-depleted metallic phase and the iron-based oxide are non-corrosion-resistant, whereas the chromium-based oxide and the stainless steel matrix phase are corrosion-resistant.     

氧化铝溶出过程压力容器用钢高温碱脆研究

本文采用慢应变速率的试验方法(SSRT)研究了3种夹杂物分布状态不同的低合金钢(16MnR,A48CPR,16MnRE),在模拟Bayer法生产氧化铝条件下的高温碱脆行为。结果表明,3种低合金钢在260℃苛性偏铝酸钠溶液中均有碱脆敏感性。沿轧向分布的条状MnS夹杂使16MnR钢横向抗碱脆性能明显低于其纵向抗碱脆性能。钢中加入稀土元素可使夹杂物呈球状、弥散分布,降低材料各向异性程度,从而提高材料抗高温碱脆能力。分析表明,夹夹物对低合金钢碱脆性能的影响,受裂纹尖端塑性区单位体积中夹杂物在垂直于受力方向平面上的     

超声冲击细化22SiMn2TiB超高强钢焊接接头晶粒研究

晶粒细化有助于提高焊接接头性能。应用超声冲击装置对母材为22SiMn2TiB、焊接材料为Cr20Ni10Mn6的异种钢焊接接头进行冲击强化试验,研究了冲击区域金属的塑性变形情况。用扫描电镜观测冲击层断面区,可看到冲击塑性变形层达到150μm,其中晶粒细化区超过50μm;用X-Ray衍射仪测试冲击层细晶衍射线宽化现象,并计算冲击层细化晶粒尺寸,计算结果表明母材冲击层平均晶粒尺寸为63nm,焊缝金属冲击层平均晶粒尺寸为82nm。研究表明,超声冲击时冲击针的高频大能量输入,引起冲击层金属晶格畸变,位错增殖、运动、重排,是晶粒细化的主要原因。