Low Cycle Fatigue Behavior and Deformation Mecha-nism of TWIP Steel

Low cycle fatigue behavior of TWIP （twinning induced plasticity） steel was investigated in axial symmetric tension-compression cyclic loading pattern. Fracture surfaces and microstructures were examined by optical, scanning electron and transmission electron microscopes. It was found that the fatigue life at the strain amplitude of 0.4 % is up to 15 000 cycles, which is much longer than TRIP780 and HSLAS00 steels. The strain hardening and softening features are significant until the strain amplitude comes to 1.25 ~. Persistent slip bands and tiny mechanical twinning layers were observed after fatigue deformation. Deformation mechanism of TWIP steel at low cycle fatigue process is not only twinning, but a complex of both twinning and persistent slip bands.     

微合金元素对700MPa级低碳贝氏体钢组织与性能的影响

通过对700 MPa级低碳贝氏体钢静态CCT曲线及不同冷却速度下组织的分析,研究了两组不同Ti、Nb含量的低碳贝氏体钢的组织、性能。结果表明,Ti、Nb含量的增加促使抗拉强度、屈服强度提高,但是Ti含量过量时对低温冲击功是不利的;wTi=0.015%-0.025%、wNb=0.04%-0.05%可满足700 MPa级别低碳贝氏体钢的强度与韧性要求,该成分钢在TMCP处理后采用回火工艺,可以获得理想的力学性能。     

Na3AlF6-AlF3-Al2O3-CaF2-MgF2-NaCl低温铝电解质密度的研究

用阿基米德实验方法,采用二次正交回归实验设计,研究了低温铝电解质Na3AlF6-AlF3-Al2O3-CaF2-MgF2-NaCl体系的密度.得到密度(ρ)与温度(t/℃)、分子比(CR)和NaCl质量分数(B/%)关系的简化方程:ρ=2.7305-1.225×10-3t 2.204×10-1 (CR)-2.014×10-3 (B-8.292)2.绘制了低温铝电解质密度的等值面图,并讨论了各因素对低温铝电解质密度的影响.经计算得出了实验条件下的密度为1.80～2.05 g/cm3,并与该电解工艺条件下的铝液密度对比,讨论了铝液与低温铝电解质的分离效果.     

全尾砂最佳絮凝沉降浓度及调控方式研究

针对新疆某铜矿充填溢流跑浑现象严重、充填尾砂利用率低等问题,对影响尾砂沉降速度的主要因素进行了研究,包括尾砂粒级组成、表面形状和进砂浓度等。通过试验探究了进砂质量浓度分别为10%、15%和20%条件下尾砂沉降高度(H)与时间(T)之间的拟合关系式,其相关系数(R ²)均大于0.975,推导出最有利于该铜矿尾砂沉降的进砂浓度值为16%~17%。通过对比进砂浓度为16.5%条件下沉降试验实测值与预测值,证明该方法能够较好地预测尾砂的最佳沉降进砂浓度值。试验研究及分析为现场生产提供了实际指导,通过增加进砂浓度调节设施,并将各设施的相关参数在充填站控制系统中进行数据联锁,使进砂浓度始终保持在16%~17%之间,絮凝剂的添加量与进砂量匹配并维持在最佳添加量范围内,实现了砂仓顶溢流水澄清,提高了充填尾砂的利用率。     

低碳耐材在连铸极低碳钢和纯净钢生产中的应用

主要介绍武钢第二炼钢厂在连铸极低碳钢和纯净钢时，为确保减少连铸过程中钢水增碳．开发和应用了低碳钢包砖、大包保护管以及中间包浸入式水口，并取得了良好的使用效果。     

浅谈锅炉中的低温腐蚀和烟气脱硫

为提高火力发电厂锅炉的热效率,延长锅炉的使用寿命,保护环境,提出了低氧燃烧和烟气脱硫两种方案。     

4G1型气缸盖的铸造缺陷及解决措施

在用AC4B合金低压铸造生产4G1发动机缸盖过程中,从模具砂芯结构、铸造冷却条件及铸造压力数值的设定等方面,采取必要的技术手段来减少AC4B合金铸件缺陷的产生。     

低温电沉积硅工艺研究进展

半导体硅的传统制备工艺主要有直拉法、区熔法及气相沉积法等,这些制备工艺都需要在高温下进行,且涉及到大型设备,制备成本较高,操作较为复杂。采用低温电沉积法制备硅具有简单可控、低成本的特点,因而受到了研究者青睐。主要从电极、溶剂的选取及电沉积方法等方面阐述了低温电沉积硅工艺研究现状,同时对低温电沉积硅存在的问题和发展趋势进行了讨论。     

Effects of Technical Conditions on Structure, Morphology and Crystalline Size of Nanocrystalline Nd-Doped Ceria Powders

Nanocrystalline solid solution CeO2-Nd2O3 powders were prepared by low temperature combustion process.Special attention was paid to the influence of the glycine/metal ratio and calcination temperature on the powders phase structure, morphology and particle size.TG-DSC curves and XRD peaks of different glycine/metal ratio show that smaller particle size can be obtained with a slightly fuel-deficient ratio.XRD results indicate that the as-prepared powders are crystallized in a single fluorite structure.The crystalline size ranges from 9 to 24 nm, which increases with the increase of calcination temperature.The lower SEM images were characterized by the spongy and form-like microstructure of the powders.Organic agent may be gradually eliminated by high temperature calcination process.     

K3AlF6-Na3AlF6-AlF3铝电解体系密度的研究

采用流体静力称重法研究了K<,3>AlF<,6>-Na<,3>AlF<,6>-AlF<,3>铝电解质体系的密度.探讨了K<,3>AlF<,6>,AlF<,3>含量和温度与K<,3>AlF<,6>-Na<,3>AlF<,6>-AlF<,3>体系密度的关系.实验结果表明:K<,3>AlF<,6>-Na<,3>AlF<,6>-AlF<,3>体系密度与温度成较好的线性关系,温度升高,密度降低;随着AlF<,3>含量的降低,体系的密度对温度的变化更加敏感.相同过热度下,固定KR(钾冰晶石含量),随着AlF3含量的增加,体系的密度呈现出不同的变化规律,相同过热度条件下,对于较低的KR=0.1值,随着AlF<,3>含量的增加,体系的密度逐渐下降,对于较高的KR=0.5值,随着AlF<,3>含量的增加,体系密度先降低后增加,存在最低点.相同过热度下,固定AlF<,3>含量,随着KR增加,体系密度也呈现出不同的变化规律,当AlF<,3>为22%,随着KR增大,体系密度变化不大;当AlF<,3>为26%,30%,随着KR增大,体系密度先降低后增加.