Molten salts/ceramic-foam matrix composites by melt infiltration method as energy storage material

A new type of high temperature energy storage material was obtained through the melt infiltration method, using compounding SiC ceramic foam as matrix and Na₂SO₄ as phase change material. The resulting composite material was measured by XRD, SEM, TG-DSC methods. The experimental results indicate that the composite is composed of silicon carbide, sodium sulfate and square quartz, and no chemical reactions occurs between Na₂SO₄ and SiC matrix. Na₂SO₄ has a good bonding with the SiC ceramic foam matrix. As the composite material is characterized by high thermal energy storage density and high thermal conductivity, it is suit for energy storage under high temperature. Funded by the “863” Hi-Tech Research and Development Program of China (2008AA05Z418)     

基于Morlet小波变换和改进遗传算法的动态识别

如何合理地识别大型复杂结构的动力参数一直是工程领域关心的问题.为此,以Morlet小波变换和采用单亲遗传算子的改进遗传算法为基础,构造一结构动态参数识别模型.并且以C++为平台,通过计算机内部命令调用ANSYS等软件,实现识别模型的程序化.通过模拟算例计算,计算结果与理论值一致.同时,结合一水电站厂房现场振动试验,对该大型结构进行动态参数识别,识别结果与工程经验值基本吻合.     

电网企业物资集约化管理探讨

分析电网企业的物资集约化管理现状,明确物资集约化管理的重要性和必要性,从而探索研究电网企业物资集约化管理的途径.     

关于体育教学改革的问题探讨

分析体育课教学中的主要任务、教材内容、教学方法、成绩考核等几个问题,并对此进行初步的研究和探讨,提出改革意见和措施,以改善体育课的教学效果。     

基于自学习规则和改进贝叶斯结合的问题分类*

根据对中文问题的分析可知,问题中的疑问词和中心词等关键词对问题所属类型起着决定性的作用。提出利用自学习方法建立疑问词—类别和疑问词+中心词—类别两种规则,并结合改进贝叶斯模型的问题分类方法。该方法充分利用了关键词对分类的贡献。实验结果表明,该分类方法有很大的改进,准确率达到了84%。     

干燥、粉碎一体化装置

本文对干燥、粉碎一体化装置的典型设备惰性粒子流化床干燥器进行剖析,介绍应用情况,并作了经济性评价。     

Synthesis of thermosetting poly(phenylene ether) containing allyl groups

New thermosetting poly(2-allyl-6-methylphenol-co-2,6-dimethylphenol)s (3) have been developed by oxidative coupling copolymerization of 2-allyl-6-methylphenol (1) with 2,6-dimethylphenol (2), followed by thermal curing. Copolymerization was conducted in nitrobenzene in the presence of copper(I) chloride and pyridine as the catalyst under a stream of oxygen, producing high molecular weight copolymers (M_n∼50,000) with broad molecular weight distributions (M_w/M_n∼35). The structure of resulting copolymers 3 was characterized by IR, ¹H, and ¹³C NMR spectroscopy. Cross-linking reactions of copolymers were carried out by thermal treatment in the absence or presence of a peroxide (3 wt%, 2,5-dimethyl-2,5-di(tert-butylperoxy)-3-butane). The 10% weight loss and glass transition temperatures of the cured copolymers were 436 °C in nitrogen and 235 °C, respectively after curing at 70 °C for 1 h and 300 °C for 1 h. The average refractive index of the cured copolymer (3b) film was 1.5407, from which the dielectric constant (ε) at 1 MHz was estimated as 2.6. The ε and dissipation factor of copolymer-films at 1 MHz were directly measured from their capacitances as 2.5-2.6 and 0.0015-0.0019, respectively.     

Large magnetic-field-induced strains in rare earth polycrystalline Ni-Mn-Ga

The magnetic-field-induced strains (MFIS) of polycrystalline Ni50Mn29Ga21 alloys containing Tb were studied. A large MFIS of-1.10% was obtained under compressive prestress conditions. The addition of Tb can fine the crystal grains, enhance the bending strength obviously, and make MFIS increase further, indicating that a moderate amount of Tb does not hinder twin boundary motion and it conversely makes the material more practical.     

Electrochemical properties of some cobalt antimonides as anode materi-als for lithium- ion batteries

Some cobalt antimonides have been prepared and studied as the candidate anode materials for lithium ion batter-ies. Reversible capacities of 424,423 and 546 mA·h·g-1 were measured at the first cycle for as-solidified CoSb2, CoSb3 and annealed CoSb3 respectively. A low lithium ions diffusion coefficient in the order of 10-16 m2·s-1 was estimated from the coulometric titration measurements in the annealed CoSb3 electrode. It was found that the electrochemical properties of fine powders are significantly better than coarse powders. However the SEM picture shows that the nano-sized CoSb3 powders gathered to larger granules, which worsens somewhat the capacity retention of the nano-sized materials, although the volume capacities of the annealed and ball milled CoSb3 remain near twice of that of graphite after 50 cycles.