Strength of pure alumina ceramics above 1 GPa

Up to now, commercially available alumina ceramics were claimed to have strength between 400 and 550 MPa. However, our study shows strength ~ 2 times higher for commercially available alumina than commonly believed. The average and characteristic strength, measured on 31 pure alumina ceramic discs by ball on three balls (B3B) test, were 1205 ± 93 MPa and 1257 MPa, respectively, with a Weibull modulus of m = 11.8. Tested specimens were in form of discs with a diameter of 5 mm and thickness 0.5 mm. The grain size distribution of the alumina is bimodal with an average grain size of ~ 850 nm measured at the surface. The fracture reveals a mixed transgranular / intergranular failure mode. To avoid incorporation of additional flaws, the discs were tested as sintered. The characteristic flexural strength measured in B3B was recalculated according to Weibull theory for standard 4-point bending bars of size 3 × 4 × 45 mm as bend 856 MPa. The measured strength of nearly 900 MPa shows the potential of strength for high purity alumina ceramics.     

Experimental and numerical study on compressive performance of perforated brick masonry after fire exposure

This paper discusses the compressive performance of perforated brick masonry after fire exposure. Compressive strength tests of the mortar, clay perforated brick, and perforated brick masonry specimens were performed in accordance with ISO834 fire tests of different durations. The temperature distribution of the masonry materials and specimens was simulated using the finite element software ABAQUS, with the thermal parameters of masonry materials recommended by European standard Eurocode 6 and related literature. The compressive strength reduction factors of mortar and clay perforated brick exposed to different fire durations were calculated via the layered method suggested by European standard Eurocode 1. In addition, the compressive strength reduction factors after cooldown were obtained from the experimental data of the masonry materials, and by considering further reductions in the compressive strength after cooling from high temperatures. Experimental data of the masonry specimens were compared with the numerical results obtained using the reduction factors proposed in this work. The comparison revealed an overall acceptable approximation. Thus, the method presented in this paper can be used to evaluate the residual capacity of masonry structures after fire.     

Strength and dilatancy behaviors of deep sands in Shanghai with a focus on grain size and shape effect

With rapid development of infrastructures like tunnels and open excavations in Shanghai, investigations on deeper soils have become critically important. Most of the existing laboratory works were focused on the clayey strata up to Layer 6 in Shanghai, i.e. at depth of up to 40 m. In this paper, Layers 7, 9, and 11, which were mostly formed of sandy soils at depth of up to 150 m, were experimentally investigated with respect to physico-mechanical behaviors. The stress–strain behaviors were analyzed by the consolidated drained/undrained (CD/CU) triaxial tests under monotonic loading. One-dimensional (1D) oedometer tests were performed to investigate the consolidation properties of the sandy soils. Specimens were prepared at three different relative densities for each layer. Also, the micro-images and particle size analyzers were used to analyze the shape and size of the sand grains. The influences of grain size, density, and angularity on the stress–strain behaviors and compressibility were also studied. Compared to the other layers, Layer 11 had the smallest mean grain size (D₅₀), highest compressibility, and lowest shear strength. In contrast, Layer 9 had the largest mean grain size, lowest compressibility, and highest shear strength. Layer 7 was of intermediate mean grain size, exhibiting more compressibility and less shear strength than that of Layer 9. Also, the critical state parameters and maximum dilatancy rate of different layers were discussed.     

DP980+Z烘烤硬化值与退火温度的关系

摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

Liquid phase sintering and characterization of SiC ceramics

The present study focuses on the sintering of silicon carbide-based ceramics (SiC) by liquid phase sintering (LPS) followed by characterization of the produced ceramics. AlN/Re₂O₃ mixtures were used as additives in the LPS process. In the first step, the LPS-SiC materials were produced in a graphite resistance furnace in the form of discs at different temperatures. The conditions with the best results regarding real density and relative density were taken as reference for sintering in the form of prismatic bars. In the second step, these samples were evaluated regarding fracture toughness (K_IC), by the Single Edge V Notch Beam – SEVNB – method, and flexural strength. K_IC behavior was evaluated according to the depth and curvature radius of the notches. Reliable K_IC values were presented when the ceramic displayed a small curvature radius at the notch tip. When the radius was large, it did not maintain the square root singularity of the notch tip. Tests were carried out to determine K_IC values in atmospheric air and water. K_IC results were lower in water than air, with a decrease ranging between 2.56% and 11.26%. The observations indicated a direct grain size correlation between K_IC values and fracture strength of the SiC ceramics.     

Deformation-Strength Relationships in Short-Term Tension of Heat-Resistant Materials

The analysis of 124 curves obtained in short-term tensile tests demonstrate that they can be described by varying strain hardening and softening characteristics. Different stress–strain curves can be produced at invariable yield strength and ultimate strength and interrelated proportional variations of the above characteristics. To determine some specific stress–strain curve, it is necessary to take account of yield strength and ultimate strength as well as strain corresponding to the latter. The relations between yield strength, ultimate strength and hardening and their practically complete absence between these parameters and softening were statistically established.     

天然气井作业屏蔽暂堵技术的研究与应用

在天然气井进行井下作业前，将暂堵剂挤入生产层位附近，以暂时封堵生产层，使地层压力不被释放，井筒内的压井液不污染地层，待施工作业结束后，及时进行解堵，确保天然气井不受伤害或少伤害，从而恢复天然气井的生产能力。针对天然气井大修作业时，经常补充压井液，由于作业时间长，大量压井液进入地层，造成严重污染，导致天然气井恢复生产困难的问题，研制出一种新型气井作业的屏蔽暂堵剂，具有污染小，易解堵等特点，有效解决了大修污染问题，现场应用取得良好效果。     

水力射孔对套管强度的影响研究

水力射孔技术是一种新型的完井方式，深穿透水力射孔技术辅助定向水力压裂可以实现油气层改造和油气井增产。但是，水力射孔套管会在孔眼处造成应力集中，使得局部应力过大而削弱了套管和水泥环的强度，可能会影响套管的使用寿命。因此，文章利用有限元软件建立了射孔套管的三维有限元模型，分析了水力射孔后套管管体的应力分布，重点研究了水力射孔参数-孔密、孔径、孔深、射孔方位角等对套管强度的影响规律。分析结果表明，沿着最大水平地应力方向深穿透水力射孔，选择合适的孔密、孔径可将射孔对套管的损害降至最小。研究结果为提高水力射孔完井设计水平提供了一定的参数依据。     

高性能大尺寸永磁体粘合强度的测定

介绍了一种用三点弯曲试验法测定高性能大尺寸粘接永磁体粘合强度的方法，及利用布氏硬度计的加载系统，实现100％检验粘接质量的方法。