快速评定砂浆配方对钢筋腐蚀的影响

用电化学方法测定砂浆试件中钢筋的极化电阻，并测定了砂浆的孔隙率，结果发现:砂浆的孔隙率、孔径分布与钢筋极化电阻大小有良好的对应关系。电化学方法能可靠、快速测定砂浆配合比、添加剂对钢筋腐蚀速度的影响。     

水泥膨胀珍珠岩砂浆的保温试验研究与应用

荆江分洪北闸加固工程２号护坦（斜面）混凝土的保温层采用了水泥膨胀珍珠岩砂浆，并对这种材料的保温效果进行了试验研究。试验表明：水泥膨胀珍珠岩砂浆降低最高温差，减小内表温差，缩小表温变幅和防止混凝土表面裂缝效果显著。在北闸２号护坦混凝土表面铺设１万平方米保温层，获得良好效果。     

Pullout tests of epoxy-coated reinforcement in concrete

The bond strength and slip of epoxy-coated reinforcing bars in concrete have been evaluated by carrying out single pullout and double pullout tests. In extended single pullout tests, slip measurements were made while tensile force was applied to reinforcing bars embedded in concrete. In double pullout tests, 20 cycles of load were applied at levels of steel stress between zero and 0·5 times characteristic steel strength. Strains were measured by electrical resistance strain gauges glued inside the bars. Both epoxy-coated and uncoated bars were used in the investigation, to obtain comparative results. The strain gradient along the bar was found to be less for the coated reinforcement. In general, the epoxy coating was found to increase slip in bond and thereby reduce the bond performance of coated bars.     

几种高强度钢腐蚀疲劳裂纹扩展行为的研究

本文研究了ＧＣ－４，３０ＣｒＭｎＳｉＮｉ２Ａ和３００Ｍ超高强钢的腐蚀疲劳裂纹扩展行为。考虑了环境，热处理制度，应力比和频率对裂纹扩展的影响。研究结果表明：腐蚀环境和热处理制度对疲劳裂纹扩展有显著影响。在侵蚀性环境中随频率降低，裂纹扩展大幅度上升，随应力比提高，环境影响加剧。利用扫描电镜对试样断口形貌进行了分析，并讨论了高强钢的腐蚀疲劳机理。     

结构陶瓷的高温疲劳强度衰减理论

提出了陶瓷材料疲劳强度衰减理论并由此导出了各种疲劳关系式。建立了疲劳基本方程ｄσ＿ｒ／ｄ＿ｉ＝一Ａσ（ｔ）￣ｎｔ￣（－ｍ），得出了疲劳寿命公式Ｔ＝Ｍ（σ＿０－σ）／Ａσ￣ｎ（静疲劳时Ｍ＝１，连续增载疲劳时Ｍ＝ｎ＋１，循环疲劳时Ｍ＝（ｎ＋１）／（１＋Ｒ＋Ｒ￣２＋……＋Ｒ￣ｎ），逐级加载时，并导出不同疲劳方式下疲劳寿命间的关系。同时，用多种Ｓｉ＿３Ｎ＿４材料在高温中作了论证试验，结果与理论一致。     

反向凝固法生产H90-钢-H90复合带

研究H90-钢-H90反向凝固复合过程中复合层厚度的变化规律以及复合带的组织和性能，探讨界面结合机理。结果表明：随着浸渍时间的增加，复合层的厚度变化经历了凝固生长、平衡相持和回熔3个阶段，钢带的预热温度越低，获得的最大复合层厚度越厚；H90复合层的组织为等轴晶粒，复合界面处Cu和Fe发生了扩散，而Zn未发生明显扩散，扩散层较薄，约为4μm；复合带的界面结合牢固；不同复合层厚度的复合带，其力学性能略有差异，但均达到GB5213——85所规定的F级深冲钢板的力学性能要求。     

不锈钢精密薄壁件外表面磁力研磨工艺研究

磁性研磨是一种利用磁场中的磁性磨料,对具有相对运动的工件表面进行光整加工的新技术。选择铝、镍、钴磁粉作为磁性磨料时,对奥氏体不锈钢精密薄壁件外表面具有良好的研磨作用。     

Reticulated Porous Multiphase Ceramics with Improved Compressive Strength and Fracture Toughness

A multiphase reticulated porous ceramic (RPC) as Si₃N₄–Al₂O₃–SiO₂ was fabricated by replication techniques. Proper volumes of additives and twice sinter- twice immerse process endow the RPC an excellent crack healing and submerging property. The compressive strength and fracture toughness improved owing to the crack bridging behavior. The existence of pores in struts in RPC blunt the crack tip and increased the external force needed to propagate the crack. The mechanisms play a beneficial role in enhancing the compressive strength and fracture strength. Si₃N₄ RPC with additives of 5%Al and 5% Al₂O₃ yielded the compressive strength of 9.8 MPa and fracture toughness of 0.3 MPa m^1/2.     

混凝土浇筑质量对钢管混凝土性能的影响

着重阐述钢管与其核心砼粘结强度对钢管砼承载影响问题 ,并介绍三种常用浇筑方式和检测方法。     

W-Cu材料室温强度和组织均匀性的影响因素

用浸透法对孔隙度为12%～17%的烧结钨进行了渗铜试验 ,研究了影响低铜含量的W -Cu材料室温бb及渗铜组织均匀性的因素 ,研究结果表明 ,铜对钨骨架的强化和韧化机制对提高W -Cu材料的室温бb 有重要作用 ;钨骨架具有合适的孔隙度是W -Cu材料获取均匀一致的渗铜组织的重要条件。