Inorganic–organic hybrid materials are attracting a strong scientific interest mainly for their outstanding inherent mechanical and thermal properties, which can be traced back to the intimate coupling of both inorganic and organic components. By carefully choosing the experimental parameters used for their synthesis, chemically and thermally stable acrylate-based hybrid material embedding the zirconium oxocluster Zr4O4(OMc)12, where OMcCH2C(CH3)C(O)O, can be deposited as UV-cured films on aluminium alloys.
In particular, the molar ratios between the oxocluster and the monomer, the polymerisation time, the amount of photo-initiator and the deposition conditions, by using an home-made spray-coating equipment, were optimised in order to obtain the best performing layers in terms of transparency and hardness to coat aluminium alloy (AA1050, AA6060 and AA2024) sheets. Furthermore, it was also evaluated whether the hybrid coatings behave as barrier to corrosion.
Several coated samples were prepared and characterised. Environmental scanning electronic microscopy (ESEM) and scratch test were used to investigate the morphology of the films and to evaluate their scratch resistance, respectively. Electrochemical impedance spectroscopy (EIS) was performed in order to evaluate if the coatings actually protect the metallic substrate from corrosion.
In order to measure shear storage modulus (G′) and loss modulus (G″) of the materials used for coatings, bulk samples were also obtained by UV-curing of the precursors solution. Dynamical mechanical thermal analysis (DMTA) was performed in shear mode on cured disks of both the hybrid materials and pristine polymer for comparison. The values of Tg were read off as the temperatures of peak of loss modulus. The length and mass of all the samples were measured before and after the DMTA analysis, so that the shrinkage of the materials in that temperature range was exactly evaluated. 相似文献
We report on a single‐layer organic memory device made of poly(N‐vinylcarbazole) embedded between an Al electrode and ITO modified with Ag nanodots (Ag‐NDs). Devices exhibit high ON/OFF switching ratios of 104. This level of performance could be achieved by modifying the ITO electrodes with some Ag‐NDs that act as trapping sites, reducing the current in the OFF state. Temperature dependence of the electrical characteristics suggest that the current of the low‐resistance state can be attributed to Schottky charge tunnelling through low‐resistance pathways of Al particles in the polymer layer and that the high‐resistance state can be controlled by charge trapping by the Al particles and Ag‐NDs. 相似文献
The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex (NRL) was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln(OH)3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln (OH)3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what's more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy (OH)3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction. 相似文献