热处理-机械粉碎法分离废弃混凝土中骨料与基质胶凝组分

利用热处理与机械粉碎相结合的方法进行了废弃混凝土中骨料与基质胶凝组分的分离试验研究。将废弃混凝土在150℃,250℃,350℃和500℃下进行热处理，然后分别在球磨机和振动磨中粉碎，考察了骨料与基质胶凝组分的分离效率，并分析了骨料与基质的分离机理。试验结果表明。随着热处理温度的提高，分离效率显著提高；热处理温度较低时，球磨粉碎的分离效率高于振动粉碎，但500℃热处理后，振动粉碎的分离效率高于球磨粉碎。     

钢渣细度对水泥混凝土物理力学性能影响

研究了钢渣细度对混凝土力学性能和安定性的影响 ,探讨了影响机理。实验表明 ,用钢渣等量替代部分水泥时 ,混凝土强度随钢渣细度增加而提高 ,特别在钢渣掺量小于 2 0 %时 ,强度增长更明显 ;实验所用各细度钢渣微粉的安定性能均满足要求。     

High-strength concrete with different fine aggregate

High-strength concrete (HSC) has undergone many developments based on the studies of influence of cement type, type and proportions of mineral admixtures, type of superplasticizer and the mineralogical composition of coarse aggregates. Most studies were carried out using natural sand with rounded and smooth grains. In practice, crushed sands from various sources are frequently used in concrete. In this paper, two aspects of the effect of crushed sands on HSCs are presented. First, the performance of crushed sands in relation to natural sand using a low water/cement (w/c) ratio and fixed coarse aggregate and cement content is analyzed. Results show that concrete with crushed sand requires an increase of superplasticizer to obtain the same slump. It also presents a higher strength than the corresponding natural sand concrete at all test ages, while its elastic modulus is lower at 28 days and is the same after that. Studies on the development of hydration and mortar phase of concrete show that the increase of strength can be attributed to the improvement of paste-fine aggregate transition zone. Second, the influence of the mineralogical source of the crushed sands was studied using three different types of crushed sands (granite, limestone and dolomite) with similar grading. Two mixtures containing 450 and 485 kg/m³ cement and low w/c ratio are analyzed. Results show the adverse effects of shape and texture on workability of concrete, but the compressive strength of concrete is improved. Granite crushed sand appears as the most advantageous sand for this purpose.     

基于APDL的ANSYS嵌入式配筋实现

以ANSYS为平台,应用APDL实现钢筋混凝土有限元模型中钢筋单元嵌入混凝土单元的功能.应用该方法可以在ANSYS中方便地建立复杂的钢筋混凝土分离式模型.利用Newton-Raphson方法求解等参数单元的坐标插值函数中被约束节点在自然坐标系下的坐标值,得到自然坐标系下节点对应形函数值,并将对应的形函数值作为约束方程中混凝土单元节点位移的分项因数,从而实现嵌入节点与被嵌入单元位移协调.计算结果与Marc的算例结果吻合良好,说明该方法合理.     

玻璃钢筋混凝土的有限元计算与试验

钢筋混凝土广泛应用于土木工程领域，但其结构耐久性因钢筋本身的锈蚀成为现今急待解决的问题。人们一直在寻找对钢筋混凝土进行改良的途径，用玻璃钢筋代替普通钢筋是解决这一问题的一个有效的方法，为此进行了试验和ANSYS有限元分析，结果证明此法具有可行性。     

Mechanical properties of high-strength concrete after fire

With compressive strength grade of C40, C60, and C70, respectively, normal-strength concrete (NSC) and high-strength concrete (HSC) were used to investigate compressive strength, splitting tensile strength, and bending strength after high temperature. The oil furnace is used in this study. Its temperature-time curve is close to standard curve, which conforms to Chinese standard GB/T 9978-1999. After being heated to temperatures of 200, 400, 600, 800, and 1000 °C, respectively, the mechanical properties of HSC were tested. The influence of temperature, water content, specimen size, strength grade, and temperature profiles on mechanical properties of HSC are discussed.     

再生混凝土力学性能提升技术与应用

针对大量混凝土废弃物造成生态环境日益恶化及天然骨料资源日益缺乏的问题,通过配制不同强度等级和不同再生骨料掺量的再生混凝土,并结合锡澄运河三级航道整治工程对再生混凝土力学性能及其提升技术进行试验研究。结果表明:再生骨料的掺量对C35及以下中低强度混凝土力学性能影响较小,而对C40及以上中高强度混凝土有较大影响,随再生骨料掺量的增加,再生混凝土力学性能降低;通过合理选用再生骨料级配、与天然骨料复掺、对再生骨料进行强化以及优化配合比参数等措施能提升混凝土力学性能;锡澄运河三级航道整治工程实际应用取得了很好的技术经济效益。     

水泥填料对心墙沥青混凝土长期水稳定性的影响

以优选的心墙沥青混凝土配合比为基础,分别采用质量分数为12%的石灰石粉、6%水泥+6%石灰石粉、12%水泥作为填料配制沥青混凝土试件,研究水泥填料对采用天然砾石骨料的心墙沥青混凝土长期水稳定性的影响。试验结果表明:采用12%石灰石粉为填料的沥青混凝土水稳定系数随浸水时间的延长而不断减小,且在浸水75 h后水稳定系数降至0.88,已不满足心墙沥青混凝土水稳定系数大于或等于0.90的要求;采用12%水泥、6%水泥+6%石灰石粉为填料的沥青混凝土水稳定系数随浸水时间的延长先增大后减小,且在浸水375 h后达到最大,分别为1.02和0.98,在浸水1 500 h后水稳定系数仍然能够满足规范要求;用水泥替代部分石灰石粉作填料也可有效改善心墙沥青混凝土的长期水稳定性。     

磷渣掺和料对混凝土力学性能影响的试验研究

针对当前资源能源匮乏、大量固体废弃物处理困难并严重污染环境的情况,以黄磷工业产生的废渣-磷渣为主要研究对象,通过一系列的试验,研究了磷渣作为掺和料在混凝土中的应用.重点研究了磷渣掺和料对混凝土力学性能影响的规律,以期达到合理利用废渣资源、减少环境污染、提高混凝土质量、降低生产成本的目的.     

严寒地区大型倒虹吸工程管道应力及水力安全控制

新疆北疆供水工程跨越吉拉沟大洼槽的三个泉倒虹吸,跨度11 km,内径2.8 m,工作水头160m,是国内外同类工程中综合难度较高的大型倒虹吸工程,在结构强度、材料工艺、安装敷设、工程质量方面都有极高的要求,特别是高水头管道运行、充水、放空、水锤防护等各种工况下的水力安全控制问题,高温差与严寒条件下管道的应力应变问题尤为突出。对该工程设计、科研、施工及运行管理方面的经验进行介绍,对其在新技术、新材料、新工艺等方面取得的理论研究和技术创新成果进行总结,研究认为:工程总体布置合理,工程运行后监测资料及工程安全评价表明各项性状指标良好,通过模型试验研究确定的闸门开度、关闭速率、充水排气、放空排水等水力安全控制关键技术科学合理,为严寒地区大型倒虹吸工程的技术发展提供借鉴。