TiO2-SiO2复合薄膜光催化活性与亲水性关系的研究

采用溶胶凝胶法在载玻片表面制备了均匀透明的TiO2-SiO2超亲水性薄膜。利用XPS，XRD，lR等对光催化活性和亲水性关系进行了研究。结果表明：薄膜的亲水性与光催化活性协同作用是其保持自清洁的关键。添加SiO2后，复合氧化物中表面形成Lewis酸，薄膜表面吸附的羟基含量增多且稳定。在与有机物竞争吸附过程中，水优先吸附，可提高薄膜的超亲水性和光催化活性，有利于提高其自清洁性能。     

Hydrothermal synthesis of flaky crystallized La2Ti2O7 for producing hydrogen from photocatalytic water splitting

Flaky monoclinic La₂Ti₂O₇ was prepared via a hydrothermal method based on the reaction of Ti(SO₄)₂ and La(NO₃)₃. Relative to the solid-state reaction sample, the flaky La₂Ti₂O₇ showed higher surface areas, much smaller crystal size and more efficient light absorption. All these factors led to the higher photoactivity to produce H₂ from water splitting under UV irradiation.     

TiO2光催化膜的成膜技术

综述了TiO2光催化膜的各种成膜方法及其进展，其中包括在陶瓷玻璃等耐热基材上的TiO2烧结法、近年来发展很快的用于塑料等非耐热性材料的粘合剂成膜法，以及用于无纺布的抄造法和水泥的混练法等。     

阳光下TiO2/GAC光催化处理洗涤剂废水的研究

利用太阳光作光源，采用固定在颗粒活性炭中的TiO2(TiO2／GAC)作光催化剂，利用其将活性炭极好的吸附性与TiO2优良的光催化性能结合于一体的特性，设计了对以洗衣粉配置的洗涤剂模拟废水的两种处理方案：同时光照-吸附法和吸附饱和-光照水洗再生法，并在实验基础上对两种方案的一些性能进行了讨论。     

液相沉淀法制备纳米TiO2及其光催化性能的研究

提出了一种以TiSO₄为前驱体的制备锐钛矿型纳米TiO₂的液相沉淀法。通过控制适宜的制备条件，可将Ti^4+的初始浓度提高到15 mol·L^-1。以丙烯酰胺的光催化降解为模型反应，考察了所制备TiO₂的光催化活性。与萃取沉淀法制备的TiO₂和工业催化剂相比，该法制备的TiO₂不仅产率高，而且催化活性较好。     

Zr掺杂g-C3N4光催化降解有机污染物

以盐酸胍为前驱体，硝酸锆为锆源，通过热聚合法制备了Zr掺杂的Zr/g-C3N4光催化剂。运用XRD、SEM、UV-Vis DRS、PL、XPS、BET等手段对催化剂的结构、形貌、光学性能进行了表征分析。结果表明：Zr掺杂改性的Zr/g-C3N4光催化剂拓宽了可见光的吸收，增大了比表面积，且降低了光生电子-空穴的复合率，具有较好的光催化活性。可见光照射下，在60 min内，5Zr/g-C3N4对罗丹明B（RhB）的光催化降解率达99.29%，光催化降解过程符合一级动力学方程，其速率常数k= 0.08647 min-1，是纯g-C3N4的8.3倍。捕获剂实验发现降解RhB的主要活性物种为超氧自由基，并推测了可能的反应机理。     

Photocatalytic degradation rate of oxalic acid on the semiconductive layer of n-TiO2 particles in the batch mode plate reactor Part I: Mass transfer limits

Organic compounds dissolved in water can be decomposed on a layer of n-TiO2 particles irradiated by u.v. light, which generates holes and electrons in the TiO2 material. Dissolved oxygen was used as electron scavenger and holes reacted with water to give OH radicals. The rate of degradation of the dissolved organic compounds by OH radicals is limited by the transfer of either oxygen or of theorganic compounds to the surface of n-TiO2 particles. The consequence of these limits is that, in the batch mode reactor with recirculation of the liquid, the dependence of the concentration of an organic compound on time has either a linear or an exponential form. Experiments with decomposition of oxalic acid in aqueous solutions using a plate reactor (60 cm × 120 cm) confirmed the analysis. Equations for evaluation of the mass transfer coefficient of the dissolved species to the surface of the plate reactor with a moving liquid fil m were developed for the case of the thickness of the Nernst diffusion layer being thinner than the thickness of the liquid. The experimentally obtained decomposition rate of oxalic acid was about 60 to 80% of the theoretical decomposition rate limited by oxygen flux through the film of a moving liquid. The present theory neglects the diffusion of oxygen into the porous layer of n-TiO2.     

纳米二氧化钛的现状与发展

介绍了目前纳米（超细）二氧化钛的几种基本制造方法，指出了二氧化钛的光催化性质、条件及原理，并且介绍了纳米二氧化钛的应用途径，主要是作为紫外光吸收剂、特殊颜料和化学催化剂使用。预测了未来10a纳米二氧化钛的生产消费情况。指出，到目前为止所有纳米（超细）粉体材料中，二氧化钛具有较好的光催化性质。     

掺铜TiO^2光催化剂光催化氧化还原性能的研究

利用浸渍法制备了掺铜二氧化钛光催化剂，分别以乙酸降解和二氧化碳还原反应为探针，研究了催化剂的光催化氧化光催化还原性能．结果表明，铜掺杂能显著提高催化剂的光催化性能；结合光电子能谱、X光衍射分析等物理表征结果，对铜掺杂改性机制进行了讨论．     

坡缕石/Al掺杂CdS复合材料光催化降解罗丹明B

采用溶剂热法制备了坡缕石/Al掺杂CdS复合材料(PGS/CdS-Al),运用XRD、XPS、SEM、UV-Vis DRS及PL对材料的结构、形貌以及光学性能进行了表征.结果表明,Al元素成功掺杂到CdS中,CdS的晶体结构没有改变,但其禁带宽带变宽.可见光照射下,该复合材料对孔雀石绿、亚甲基蓝、甲基橙、结晶紫、罗丹明B有机染料均有光催化降解活性,且对罗丹明B的光催化降解效果最好.光照40 min,质量浓度为0.67 g/L 15％PGS/CdS-Al(15％为PGS的负载量,以生成的CdS质量计)对30 mL质量浓度为20 mg/L罗丹明B的降解率为98.7％,反应主要活性基团是h+.该降解反应符合一级动力学,反应速率常数为0.067 min–1.