高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

Structure and electrical properties of Ca2+-doped (Na0.47Bi0.47Ba0.06)TiO3 lead-free piezoelectric ceramics

The lead-free piezoelectric ceramics (Na_.47Bi_.47Ba_.06)_1-xCa_xTiO₃ (x?=?0, 0.01, 0.02, 0.03, 0.05, and 0.08, abbreviated as BNBTC/0, BNBTC/1, BNBTC/2, BNBTC/3, BNBTC/5, and BNBTC/8, respectively) were obtained using the solid-state reaction method. The structure, electric conductivity, and dielectric, ferroelectric, and piezoelectric properties of the Ca²⁺-doped (Na_.47Bi_.47Ba_.06)TiO₃ ceramics were thoroughly investigated. The ceramics sintered at 1200?°C exhibit dense microstructures, having relative densities higher than 96%. The X-ray diffraction results demonstrate that all ceramics have a pure perovskite structure. The mean grain sizes of the ceramics are related to the Ca²⁺ quantity. A small quantity of Ca²⁺ ions (x?≤?0.03) improves the piezoelectric and ferroelectric properties of the samples. The dielectric behavior of the samples is sensitive to the Ca²⁺ content and electric poling. The results demonstrate that the electrical properties of the (Na_.47Bi_.47Ba_.06)TiO₃ lead-free ceramics can be well tuned by varying the Ca²⁺ quantity.     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

Thermal treatment of waste photovoltaic module for recovery and recycling: Experimental assessment of the presence of metals in the gas emissions and in the ashes

The rapid expansion of the photovoltaic (PV) module market in the last years will determine in the near future a remarkable growth of corresponding waste. Then, the hazardous materials contained in the modules, such as Cd, Pb and Cr, could be released in the environment if the waste panels will not be handled adequately. Recycling processes of silicon crystalline panels, finalized to separate PV cells from the glass, involve the removal of the EVA (Ethylene Vinyl Acetate) layer through different methods, as the thermal treatment. During this treatment, some hazardous components can be released due to thermal degradation process. In this paper the metals released in the gas emissions and in the ashes due to the thermal treatment of modules were evaluated. For this purpose, three samples of crystalline panels were heated in furnace up to 600 °C and the complete degradation of the EVA was obtained. A mass balance between the sample and its components, before and after treatment, was performed in order to assess the weight loss percentage. Finally, after thermal treatment a qualitative analysis on the separated PV cell surface was performed by SEM-EDS (Scanning Electron Microscope equipped with Energy Dispersive Spectrometer).     

A Distribution‐freeCUSUMChart for Monitoring Variability of AutocorrelatedProcesses

We present a distribution‐free tabular cumulative sum chart for monitoring the variability of an autocorrelated process. A quantity known as the asymptotic variance parameter is employed as a measure of the variability, and a distribution‐free tabular cumulative sum chart is applied to variance estimates calculated from batches of nonoverlapping samples. The proposed chart is applicable to a stationary process with a general marginal distribution and a general autocorrelation structure. It also determines control limits analytically without trial‐and‐error simulations. The performance of the proposed chart is tested on stationary processes with both normal and nonnormal marginals with various autocorrelation structures. Copyright © 2014 John Wiley & Sons, Ltd.     

Reducing numerical dissipation in smoke simulation

Numerical dissipation acts as artificial viscosity to make smoke viscous. Reducing numerical dissipation is able to recover visual details smeared out by the numerical dissipation. Great efforts have been devoted to suppress the numerical dissipation in smoke simulation in the past few years. In this paper we investigate methods of combating the numerical dissipation. We describe visual consequences of the numerical dissipation and explore sources that introduce the numerical dissipation into course of smoke simulation. Methods are investigated from various aspects including grid variation, high-order advection, sub-grid compensation, invariant conservation, and particle-based improvement, followed by discussion and comparison in terms of visual quality, computational overhead, ease of implementation, adaptivity, and scalability, which leads to their different applicability to various application scenarios.