湿式储气罐防腐失效原因分析及改进措施

分析了济钢10万m3低压湿式储气罐防腐失效的原因,从防腐涂料的选择、施工过程等环节提出了改进的措施,实施后效果良好。     

Stresses in bent copper tubing: Application to fatigue and stress-corrosion cracking failure mechanisms

The residual and applied stresses in u-bent copper tubing are addressed in the context of both cyclic fatigue and stress-corrosion cracking. Failures as a result of fatigue and stress corrosion cracking in u-bent copper tubing have been observed to initiate at nonintuitive locations when only the applied stresses on the component are considered. This paper presents both qualitative classical and quantitative finite-element stress analysis results for the forming of u-bends. The resulting residual stress distributions are compared to fracture patterns generated by both fatigue and stress-corrosion cracking mechanisms.     

切口翻边中的防错移

在研究切口翻过程中材料变形及受力情况基础上，提出切口翻边模具设计中的防错移措施。     

复杂电力系统灾变防治的综合集成方法论

电网的大规模互联成为世界范围内电力系统发展的必然趋势。现代电力系统的强非线性和高维等复杂特性,使得传统的理论分析方法已不能较好地分析复杂电网的动态行为及由电网连锁反应故障造成的大面积停电事故的成因。作为科学的方法论,综合集成方法论综合了计算机网络技术、数据融合技术、知识与信息及专家群体智能的各方面优势,其应用在研究方式和工作方式上都突破了传统还原论思想的束缚。从复杂性科学的角度,介绍了复杂电力系统的特征,并着重论述了应用研究复杂系统的方法论——从定性到定量综合集成方法进行电力系统灾变防治研究的方法。     

环境氡气辐射规律及防治研究

氡对人体的辐射伤害占人体所受到的全部环境辐射的55%以上。氡气会导致肺癌、白血病、皮肤癌及其它呼吸道病变的产生。本文在国内外相近课题研究基础上,采用仪器测量及理论分析相结合的方法,对全国各地多种地质构造取样的数据进行分析处理,总结了地壳中放射性元素的分布规律及大气中氡的来源。文章着重从岩石、土壤、地下(热)水、矿山及室内几个方面讨论了氡浓度的影响因素及分布规律。最后提出了室内氡气防治方法及降氡措施,以便更好地进行放射性环境评价以避免氡对人体的危害。     

砖混结构墙体裂缝的分析与防治

通过对墙体裂缝的观察、分析,归纳产生原因,提出了在设计、施工中相应采取的防治方法和措施.     

Stress-corrosion cracking of a monel 400 tube

A bent Ni-Cu Monel 400 alloy tube, which operated as part of a pipeline in a petrochemical distillery installation, failed by through-thickness cracking. The pipeline was used to carry a stream of gaseous hydrocarbons containing hydrochloric acid (HCl) into a reaction tower. The tower provided a caustic solution (NaOH) to remove HCl from the stream, before the latter was directed to a burner. Metallographic examination showed that the cracks were intergranular and were frequently branched. Although nominal chemical composition of the component was found within the specified range, electron dispersive analysis by X-ray (EDXA) indicated significant segregation of sulfur and chlorine on grain boundaries. Failure was attributed to hypochlorous-acid (HClO)-induced stress-corrosion cracking (SCC). The HClO was formed by the reaction of HCl with atmospheric O₂, and the oxygen entered the tube during shutdowns/startups of the installation. Residual stresses, originating from the in situ bend forming of the tube during assembly of the line, provided a driving force for crack growth, and the segregation of sulfur on grain boundaries enhanced the susceptibility of the material to cracking.     

与时俱进与马克思主义中国化

论述了马克思主义中国化从实事求是到解放思想、实事求是，再到解放思想、实事求是、与时俱进的发展轨迹，并进一步阐释与时俱进在新时期的科学内涵；论述了以人为本，全面、协调、可持续的科学发展观是马克思主义中国化的新境界。     

Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment

In order to investigate stress corrosion cracking (SCC) of X70 pipeline steel and its weld joint area in acidic soil environ-ment in China, two simulating methods were used: one was to obtain bad microstructures in heat affected zone by annealing at 1300°C for 10 min and then, quenching in water; the other was to get different simulating solutions of acidic soil in Yingtan in south-east China. The SCC susceptibilities of X70 pipeline steel before and after quenching in the simulating solutions were analyzed...