65Mn钢的组织超细化与超塑性

利用盐浴加热循环淬火对６５Ｍｎ钢进行奥氏体晶粒的超细化，并对晶粒细化后的６５Ｍｎ钢进行超塑拉伸试验。结果表明，热轧或正火态的６５Ｍｎ钢经８１０℃循环淬火３次，奥氏体晶粒即可细化至１３级，在温度６６０～７２０℃、变形速率０．５～３．７×１０（－２）ｍｉｎ（－１）范围内呈现超塑性，δ≥２００％，最高达２９４％，σ最低仅３８ＭＰａ，ｍ值为０．３８左右。     

Effects of molten aluminum on H13 dies and coatings

The effects of molten aluminum casting alloy A390 on a commercially heat treated H13 die steel and two wear-resistant coatings, Cr₂₃C₆ and TiN, were investigated by an accelerated corrosion test. The H13 steel suffered severe corrosion due to the rapid formation of intermetallic compounds. The formation of multilayer intermetallic compounds and the simultaneous dissociation of the intermetallic compound τ6 (Al₄FeSi) were attributed to the fast dissolution of H13 steels into the melt. This dissolution of the H13 steel was accelerated dramatically by turbulence and an increase in melt temperature. Significant improvement in corrosion resistance was achieved for the H13 steel coated by Cr₂₃C₆ via a pack cementation process.     

缓蚀剂对316L不锈钢在酸性氯离子溶液中应力腐蚀开裂的作用

研究表明316L不锈钢在55℃的1mol/L HCl+1mol/L NaCl溶液中对SCC比较敏感。316L不锈钢在所研究的体系中处于活化溶解状态。对添加缓蚀剂的体系的电化学参数的测试和分析表明,缓蚀剂抑制SCC的能力与缓蚀剂抑制阳极反应有关。     

纳秒激光微刻蚀取向硅钢的形貌特征及磁性能

为有效降低取向硅钢铁损、改善其磁性能，采用红外纳秒激光对取向硅钢进行微刻蚀试验。利用3D共聚焦显微镜、扫描电镜与能谱仪研究典型工艺参数下的硅钢表面烧蚀形貌特征及表面质量，利用铁损仪测试不同刻蚀参数下取向硅钢的铁损、相对磁导率等磁性能参数及动态磁滞回线，对比分析刻痕前后磁性能的变化行为、规律及磁滞特性。结果表明：激光刻痕后，硅钢的铁损、相对磁导率、矫顽力及剩磁等性能得到明显改善，铁损的改善表现在高磁感强度下、相对磁导率的改善表现在低磁场强度下，回线特性得到优化。扫描速度为800 mm/s、脉冲能量为0.25 mJ时，刻痕边界呈近似规则的“波浪线”，且刻痕表面质量较高，铁损降低高达11.6%、剩磁降低12.8%等；刻痕后相对相对磁导率明显提高，提高约为5.7%~15.16%，最大可达2.598×10⁴。激光频率与扫描速度的耦合关系是影响刻痕边界形状与磁畴细化效果的重要因素。     

焊接工艺对2205双相不锈钢焊接接头综合性能的影响

采用等离子弧焊打底 TIG焊盖面及等离子弧焊打底 MIG焊盖面焊接工艺焊接了2205双相不锈钢,研究了2205双相不锈钢的焊接性,并对焊后固溶处理与未进行固溶处理的焊件组织特征、力学性能及抗腐蚀性进行了比较,研究了不同焊接热输入和固溶处理工艺对焊接接头综合性能的影响.     

低碳Si-Mn系TRIP钢的热处理工艺对组织的影响

低碳Si-Mn系TRIP钢有着复杂的显微组织，主要由多边形铁素体（F）＋无碳贝氏体（B）＋残留奥氏体（AR）组成。本试验采用了彩色金相法，并结合X－ray衍射、SEM和TEM等手段研究了低碳Si-Mn系TRIP钢显微组织与工艺的关系，发现随着两相区退火温度的升高，最终显微组织中铁素体基体体积分数变小，并且贝氏体量增多，残留奥氏体的稳定性呈起伏式变化；在贝氏体转变区的等温温度过高或过低，均使最终显微组织中残留奥氏体体积分数减少；在贝氏体转变区等温时，所形成贝氏体表现出粒状的特征。     

不同冷轧状态的ELC-BH钢板连续退火再结晶规律

对不同压力率的ELC-BH钢板进行了连续退火试验。研究结果发现，随着冷轧压下率增加和冷轧板厚度减薄，ELC-BH钢板的连续退火再结晶过程提前并缩短，晶粒长达过程相对延长，这对于不同厚度产品的生产工艺调整十分重要。     

45钢的离子氮碳共渗-离子渗氧复合处理

研究了45钢离子氮碳共渗-离子渗氧复合处理工艺。试验表明，45钢经离子氮碳共渗-离子渗氧复合处理后，表层可获得化合物和氧化物的复合层，该复合处理可以明显提高45钢的耐磨性。     

The effect of neutral red on the corrosion inhibition of cold rolled steel in 1.0 M hydrochloric acid

The corrosion inhibition of neutral red on the corrosion of cold rolled steel in 1.0 M hydrochloric acid (HCl) was studied using weight loss method and potentiodynamic polarization method. Results obtained revealed that neutral red is an effective inhibitor. It was found that the adsorption of neutral red could prevent steel from weight loss and the adsorption accorded with the Langmuir adsorption isotherm. Potentiodynamic polarization studies showed that neutral red mainly acted as a mixed-type inhibitor for steel in 1.0 M hydrochloric acid. Thermodynamic parameters such as adsorption heat, adsorption entropy and adsorption free energy were obtained from experimental data of the temperature studies of the inhibition process at four temperatures ranging from 30 to 45 °C. The most suitable range of inhibitor concentration was discussed. The kinetic data such as apparent activation energies and pre-exponential factors at different concentrations of the inhibitor were calculated, the effect of the apparent activation energies and pre-exponential factors on the corrosion rates of cold rolled steel was discussed. The inhibitive action was satisfactorily explained by using both thermodynamic and kinetic models. Synergism between chloride ion and neutral red was proposed. The results obtained from weight loss and potentiodynamic polarization were in good agreement.     

不锈钢基体上化学镀铜工艺研究

不锈钢基体上化学镀铜易造成镀层鼓泡,这不仅影响了镀层与基体的结合力,而且直接影响到外观质量.为此,将镀前酸处理过的不锈钢片放在烘箱中加热,以除去酸洗时渗入到基体的氢.确定了热处理温度和时间,采用此方法解决了镀层起泡问题,得到所需要的镀层.