MICROSTRUCTURAL EVOLUTION OF HIGHLY UNDERCOOLED EUTECTIC Ni78.6Si21.4 ALLOY

A large undercooling level up to 550K （0.386Te） was achieved in eutectic Ni78.6Si21.4melt by the combination of molten-glass and cyclic superheating. A microcrystaUine structure is obtained at large undercooling. Surprisingly, the morphology of ct（Ni） phase transits from the non-faceted phaseto faceted phase at large undercooling of 390K. Based on the classical nucleation theory and transient nucleation theory, the process of microstructure evolution and competitive nucleation was analyzed, and the refinement of crystal structure is determined by the high nucleation rate under large undercooling.     

非晶态Fe－B－Si合金的退火脆化

非晶态Ｆｅ－Ｂ－Ｓｉ合金的退火脆化具有明显的成分依赖性，并且对制备条件和退火方式比较敏感；近共晶成分的合金（如Ｆｅ８０Ｂ１１．５Ｓｉ８．５和Ｆｅ７９Ｂ１１．５Ｓｉ９．５等）和适当液淬工艺条件下制备的非晶合金薄带具有相对较小的脆化倾向。与常规退火工艺相比，脉冲电流加热快速退火，可在保持延性基本不变的情况下，明显改善合金的磁性；是获得非晶态Ｆｅ－Ｂ－Ｓｉ合金磁性优化与良好延性配合的有效途径之一     

Tb在快速凝固Ag合金中固溶度扩展

采用电弧熔化快速锤砧急冷技术制备含Tb直到10at.-%的Ag-Tb合金箔,厚度0.05—0.08mm,其冷却速度为10~6K/s数量级,采用晶格参数法确定Tb在快速凝固Ag-Tb合金中亚稳扩展固溶度可达到5at-%,确定亚稳共晶中的第二相为Ag_3Tb,观察了快凝Ag-Tb合金的显微结构与缺陷。     

激光快速修复Ti-6Al-4V合金的显微组织与力学性能

针对Ti-6Al-4V合金在加工和服役过程中的损伤特点,对Ti-6Al-4V合金锻件的3种典型误加工缺陷——槽缺陷、面缺陷和体缺陷进行了激光快速修复研究。激光修复区与锻件基体形成致密冶金结合,Al、V合金元素由锻件基体到激光修复区均匀分布,无宏观偏析。激光修复区组织为粗大原始β晶粒内分布细长的α针及编织细密的α+β板条组织,呈现典型的魏氏结构,热影响区组织从锻件的等轴α+转变β组织逐步过渡到魏氏(α+β)组织。对预制有3种类型缺陷的激光修复试样进行室温静载拉伸试验和硬度测试,结果表明修复试样的拉伸性能达到锻件标准(HB5224-1982)。激光修复试样的硬度和强度高于锻件基体,而塑性则低于锻件基体。因此,激光修复区和锻件基体可看作是一种“强+弱”的组合,这与二者的显微组织是相对应的。     

Rapidly solidified hypereutectic Al-Si alloys prepared by powder hot extrusion

Rapidly solidified hypereutectic Al-Si alloys were prepared by powder hot extrusion.By eliminating vacuum degassing procedure.the fabrication routine was simplified.The tensile fracture mechanisms at room temperature and elevated temperature were investigated by SEM fractography.Compared with KS282 casting material,the tensile strength of rapidly solidified Al-Si alloy is greatly improved due to silicon particles refining while its density and coefficient of thermal expansion are lower.than those of KS282.The wear resistance of RS AlSi is better than that of KS282.     

热压快速凝固Fe0.92Mn0.08Six半导体的热电性能

采用快速凝固和热压的方法制备了p型热电材料Fe0.92Mn0.08Six(x=1.9, 2.0, 2.1, 2.3, 2.5).X射线衍射分析表明,热压试样退火24 h后,完全转变为β半导体相.所有试样的致密度均高于90%.测量试样的电学性能发现,原料配比为Fe0.92Mn0.08Si2.1的试样在整个测量温度范围内的功率因子最大,550℃时达到了400 μW·m-1·K-1以上.     

基于焊接机器人的三维快速成形的方法研究

将RP技术与熔焊技术结合．依据焊接工艺的特点对切片和多径规划算法进行了研究，得出了根据不同类型零件使用不同路径规划算法的结论。据此。使用Visual C^ 基于UniGraphics二次开发的方式实现了切片、路径规划算法，完成了面向焊接机器人性速成形软件的编写，实现UG实体模型的切片、路径规划以及机器人数控代码的生成。利用MotoMan机器人远程控制接口软件包MotoCom32编写了用于机器人快速成形的远程成形控制软件。采用CO2气体保护焊成功实现了基于焊接机器人的典型零件的快速成形。     

快速凝固MlNi4．0 Al 0．3 Si 0．1 Fe0．6无Co贮氢电极合金的微结构和电化学性能

研究了单辊快淬快速凝固处理对无Co贮氢电极合金MlNi4．0Al0．3Si0．1Fe0．6的微结构和电化学性能的影响。XRD分析表明，快凝合金仍为单相CaCu5型结构，但合金相的成分和结构均匀性得到明显改善。金相观察和能谱分析显示，铸态合金为比较粗大的树枝晶结构并存在明显的成分偏析，而快凝合金呈细小的胞状晶结构，合金中元素的分布趋于均匀化。电化学测试表明，快速凝固处理后合金的活化性能不变，循环稳定性得到显著改善，但其放电容量和高倍率放电性能有所降低。研究发现，快凝合金电极的交换电流密度Io以及氢在合金中的扩散系数D较铸态合金有所减小是导致其高倍率放电性能降低的主要原因。快速凝固处理导致无Co合金电化学性能的变化与合金的微结构的改变有关。     

快速原型制造中的前期数据准备

介绍了快速原型技术的原理和实现过程,对快速原型制造中的前期数据准备工作,快速原型机的输入数据来源、三位模型数据的近似处理、三维模型数据切片处理作了详细讨论.     

纳米晶Al88Ce2Ni10铝合金的形成

通过晶化法，可以将快凝Ａｌ８８Ｃｅ２Ｎｉ１０非晶铝合金制备成纳米晶合金。纳米晶合金的组织为αＡｌ固溶体和金属间化合物Ａｌ３Ｎｉ及Ａｌ１１Ｃｅ３组成的多相纳米晶结构。在６０３～７７３Ｋ较宽退火温区内，用Ｓｃｈｅｒｅｒ公式计算各晶化相，得到αＡｌ、Ａｌ３Ｎｉ及Ａｌ１１Ｃｅ３的晶粒尺寸分别为３１～３１６、２２～２０７及１９～１６５ｎｍ。结果表明，通过控制热处理条件，可以获得不同晶粒尺寸的纳米晶合金。其中获得晶粒细小、结构均匀超细纳米晶合金的最佳退火温度为第二ＤＳＣ峰值温度附近