13SiMnNiCrMoV钢切口疲劳裂纹萌生门槛值

本文研究在13SiMnNiCrMoV 结构钢中用尖裂纹的应力强度因子来反映三点弯曲缺口试样的疲劳裂纹萌生规律。当 R=0.1,f=100Hz,试样尺寸 B×W×L=12.5×25×117mm 时,缺口名义应力幅的门槛值为Δσ_(th)=3315ρ~(0.352) MPa,0.5mm≤ρ≤5mmΔK_(th)=250ρ~(0.352) MPam~(1/2)门槛值与ρ有关。同时得到缺口裂纹萌生的循环次数 N_i 与名义应力幅Δσ、缺口曲率半径ρ的定量关系是N_i=3.98×10~(22)ρ~(1.62)/Δσ~(4.85),N_i≤10~(5.5)并讨论了(ΔK_1/ρ~(1/2))_(th)与ρ无关的结论。     

Reticulated Porous Multiphase Ceramics with Improved Compressive Strength and Fracture Toughness

A multiphase reticulated porous ceramic (RPC) as Si₃N₄–Al₂O₃–SiO₂ was fabricated by replication techniques. Proper volumes of additives and twice sinter- twice immerse process endow the RPC an excellent crack healing and submerging property. The compressive strength and fracture toughness improved owing to the crack bridging behavior. The existence of pores in struts in RPC blunt the crack tip and increased the external force needed to propagate the crack. The mechanisms play a beneficial role in enhancing the compressive strength and fracture strength. Si₃N₄ RPC with additives of 5%Al and 5% Al₂O₃ yielded the compressive strength of 9.8 MPa and fracture toughness of 0.3 MPa m^1/2.     

疲劳裂纹的灰色残差预测

借助灰色理论，建立了预测疲劳裂纹扩展的灰色残差预测模型，并应用此模型预测了某不锈钢构件腐蚀疲劳裂纹的扩展，得到了较高精度的预测结果，为疲劳裂纹预测提供了一种简易而可靠的新途径。     

大体积砼产生裂缝的原因及防治措施

大体积砼裂缝问题是建筑业普通关心的问题.对砼裂缝进行控制,就必须研究砼结构中裂缝产生的原因以及在实际的设计和施工过程中采取合理的、经济的措施来控制裂缝.本文通过对大体积砼裂缝成因的理论研究,提出了合理的裂缝控制的设计和施工措施.     

有梭织机光电探纬系统的改进

依据红外反射式光电探纬的组成和工作原理，对有梭织机光电探纬系统进行了改进。将反光装置（膜）固定在梭芯上，减少了反光装置的数量，无需改动梭子和纬管，系统探纬准确，减少了换梭时纡脚回丝。     

Determination of Discrete-Structure Parameters of Coatings with Allowance for Residual Stresses

The authors suggest that the dimensions of a discrete section of a coating should be chosen on the basis of calculation of the critical crack spacing in cohesion cracking. This approach allows for residual stresses in the coating. The reliability of the calculation method has been verified experimentally by direct measurement of the crack spacing.     

海洋平台损伤检测的发展现状与展望

针对海洋平台损伤检测技术进行了分析，总结了国内外海洋平台损伤检测技术的最新进展。对各种检测方法进行了分类与比较，分析了不同检测方法的基本原理及其适用范围，提出了海洋工程结构损伤检测的二步法，可以综合利用不同的损伤检测方法，更准确、有效地对平台进行损伤检测。     

锌基合金模具的应用及探讨

本文分析了锌基合金模具制造及使用过程中容易出现热裂、翘曲、收缩的问题，并提出了解决这些问题的措施。     

65 Mn热轧带钢表面裂纹分析

分析了热轧带钢表面裂纹产生的原因，介绍了采取的工艺措施及其效果。     

基于高抗热震性能的陶瓷刀具材料的微观结构设计

本文以现有的抗热震断裂和抗热震损伤的评价理论为基础，通过对材料中微裂纹的长度进行预测，从而实现了对陶瓷刀具材料的抗热震性能的微观结构设计。根据此理论对现有材料的抗热震性能的进行预测，预测结果与实际的测量结果相符，验证了该理论的正确性。