Q345B钢氧化铁皮的高温粘附性研究

热轧板带加热过程中高温氧化将直接影响氧化铁皮的结构、元素分布以及粘附性,进而间接影响后续除鳞效果以及粗轧和精轧后得到的成品钢板表面质量。本文利用Gleeble热模拟试验机模拟Q345B连铸坯粗轧前在1 150和1 250℃加热阶段的氧化情况,并结合拉伸试验研究了两个温度下氧化铁皮的表面形貌、次生氧化铁皮的裂纹以及氧化铁皮与基体界面处截面形貌和各合金的元素分布。研究表明：高温短时氧化生成的一次氧化铁皮粘附性小,仅微小变形即可完全剥离脱落;次生氧化铁皮粘附性大,但强度低,塑性差,易产生裂纹。此外,次生氧化铁皮与基体界面处反应生成的Fe₂SiO₄会改变氧化铁皮FeO内层的相间分布,对氧化皮起到钉扎作用,导致氧化皮的粘附性强,这增大了后续除鳞的难度。为改善钢板的表面质量,生产实践中建议在粗轧除鳞前控制钢板氧化铁皮界面温度高于Fe₂SiO₄凝固温度,以降低氧化铁皮与钢板基体附着力。     

Effects of Fe/Ni Ratio on Microstructure and Properties of FeNiCrAlNb High-Entropy Alloys

Herein, the effects of Fe/Ni ratio on the microstructure, mechanical properties, and corrosion resistance in a 3.5 wt% NaCl solution of Fe_xNi_65−xCr₂₀Al₁₀Nb₅ are investigated systematically. It is found that the phases shifted from the FCC-dominated to the BCC-dominated with the molar ratio of the Fe/Ni increased. The strength of Fe_xNi_65−xCr₂₀Al₁₀Nb₅ increases with the molar ratio of Fe/Ni further increased, while the plasticity decreases. The yield strength reaches 1,653 MPa at x = 45. The alloy exhibits the best corrosion resistance when x = 35 which is attributed to the dominant FCC phases in the dendritic region.     

Preparation of Porous Silver Nanowires-Melamine Formaldehyde Hybrid Composite Materials and Their Electromagnetic Shielding and Flame-Retardant Properties

Along with the booming development of communication technology and electronic equipment, higher requirements of flame-retardant and EMI shielding performances for electromagnetic interference (EMI) shielding materials are put forward. Herein, the ultralight and porous silver nanowires (AgNWs)-melamine formaldehyde (MF) hybrid composite with unique micro-/nanostructure is developed by a facile dip-coating method, which uses the AgNWs as 1D conductive coating and MF foam (MF foam) as 3D skeleton template. Benefiting from the unique porous micro-/nanostructure, the resultant hybrid composite displays low density, excellent EMI shielding performances, and superior flame-retardant property. The EMI shielding effectiveness (SE) and specific EMI SE (SSEt) of the hybrid composite in X-band (8.2–12.4 GHz) can be up to 77 dB and 26971.4 dB cm⁻² g⁻¹, respectively. At the same time, the hybrid composite also passes the vertical burning test and shows an increased LOI value of 40.6%. The combination of flame-retardant and EMI shielding performances for EMI shielding materials makes the AgNWs-MF hybrid composite great application potential in civil and military fields. This work provides a new guide for the design of multifunctional high-performance EMI shielding materials.     

马钢2500m~3高炉炉渣的冶金性能

在目前的原燃料条件下,为保证马钢2500m3高炉炉渣具有良好的流动性和较高的脱硫能力,炉渣的CaO／SiO2应控制在1．05至1．15之间,炉渣温度不低于1450℃．     

公有住房使用权收益价格评估

公有住房使用权价格评估是公房使用权有偿转让的基础性工作,但因我国的公房使用权有别于一般租赁产权,故房地产估价的常观收益法在此并不全然适用。文章在分析我国公房使用权特殊性的基础上,变通了既有的收益法估价公式,提出了确定相关技术参数的思路。作为讨论结果的具体应用,文章最后给出了一宗评估案例。     

锥阀特性研究

本文主要是结合实际生产, 在理论上分析了锥阀的一些特性, 提出了在设计锥阀时所注意的一些要素     

影响涂料印花增稠剂增稠及抗渗化性能的因素

讨论了反乳液聚合法合成涂料印花增稠剂时,影响聚合产物的抗渗化性能及增稠效果的主要因素。研究发现,提高聚合温度可以提高聚合产物的抗渗化性,但配制高粘度印花浆时对增稠效果不利,而在配制低粘度印花浆时则反之。降低交联单体用量有利于提高聚合产物的抗渗化性,并可提高聚合产物在配制较低粘度印花浆时的增稠效果。     

板栗壳棕色素的提取及理化性质研究

研究了板栗壳棕色素的提取及其理化性质。实验结果表明,该色素对光,热稳定性很好,具有一定的应用开发价值。     

十二烷基葡糖苷的合成与性能研究

在催化剂存在下,采用双醇交换法合成了新型淀粉基表面活性剂十二烷基葡糖苷,确定了合成反应条件,产物收率≥９３％。性能测试结果表明,十二烷基葡糖苷具有表面张力低、性能温和、起泡和润湿性优良等特点,是一种新型的非离子表面活性剂。     