通过模型试验 ,对位于西安市东郊因采沙使河道破坏严重的灞河河段进行了复现试验和研究 ,并以此为依据 ,通过优化比较为设计部门提供了合理的橡胶坝坝址和坝座高程。在此基础上 ,又对建坝后橡胶坝对上下游冲淤变化的影响进行了试验研究和分析 ,解决了工程设计中的一些关键技术问题     

Powder Deposition in Three Parallel-Oriented Dies of Different Shapes

Uniformity of bulk density distribution during the die filling process is required to minimize quality problems, such as distortion and cracking, for powder compacts. Understanding the die filling process is necessary in ensuring a uniform powder deposition. The second-generation pressure deposition tester (PDT-II) was used to investigate the deposition process and final pressure distribution of powder filling in toroidal, cylindrical, and E-shaped dies. All tests were conducted using a spray-dried free-flowing granular powder. The results indicated that for toroidal dies: (1) the area around 0° orientation (the leeward end) had the highest pressure values (1186.7 to 2498.0 Pa), with the average pressure values of the remaining area 353.7-648.0 Pa; (2) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; (3) the highest feed shoe speed (500 mm/s) led to the most nonuniform pressure distribution among the three speeds; (4) higher feed shoe speed did not always result in higher final pressure values; and (5) the right die tended to have higher final pressure values (215.0 to 2498.0 Pa) than the center die (95.4 to 2052.5 Pa). For E-shaped dies: (1) the final pressure values of the middle leg (308.9 to 760.7 Pa) were higher than those of the left and the right legs (148.9 to 530.3 Pa); (2) the area along the backside had the highest final pressure value (1054.6 to 1303.8 Pa); (3) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; and (4) neither the center die nor the right die always had higher pressure values than the other one at all locations. Comparison between cylindrical and toroidal dies indicated that: (1) neither of the two die shapes (cylinder and toroid) led to consistently higher or lower final pressure values at all locations and (2) for all three feed shoe speeds, the toroidal die had higher average final pressure values in the 0° orientation.     

The process window for diamond deposition from the vapor phase with sulfur in the C–H–O feed gas mixtures

Theoretical predictions using a modified radical species ternary diagram for C–H–O system indicate that addition of sulfur expands the C–H–O gas phase compositional window for diamond deposition. Sulfur addition to no-growth domain increases the carbon super-saturation by binding the oxygen and the addition of sulfur to the non-diamond domain reduces the heavy carbon super-saturation by decreasing C_nH_m species concentration in the gas phase. The overall effect of sulfur addition to gas phase mixtures is characterized as that of oxygen addition to the C–H system, i.e. expansion of the compositional window over which diamond can be deposited from the gas phase. In addition, the increasing sulfur concentration to diamond domain feed gases beyond 2000 ppm did not affect the steady state gas phase composition but the quality of diamond was reduced.     

黄河中游多沙粗沙区水沙控制途径的探讨

根据黄河中游多沙粗区暴雨洪水及产流产沙特点，提出了为控制水沙危害，黄河中游治理应分两步走的战略。第一步解决近期水沙控制和耕地问题，主要措施是建设淤地坝和骨干坝。研究表明，在现状坝地，梯田条件下，为满足粮食生产需要，每平方公里需新增坝地３．１８ｈａ，且能港口控制水沙的要求。第二步是进行坡面治理，改善生态环境，以达到根治水沙的目的。     

The growth and characterization of AlGaAs double heterostructures for the evaluation of reactor and source quality

AlGaAs double heterostructures are grown by low-pressure metalorganic chemical vapor deposition to evaluate the level of oxygen contamination in different trimethylaluminum sources. Effects of arsine purifiers, misoriented substrates, atmospheric exposure of the growth chamber, and possible phosphorus contamination are also studied. Extensive characterization is performed on these films by a variety of methods, including high-resolution x-ray diffraction, photoluminescence (PL), time-resolved photoluminescence, and secondary-ion mass spectrometry. The PL intensities for structures grown with the low-alkoxide grade are reproducibly much greater than those grown with the regular-grade TMA1. The use of AsH₃ purification improves the PL intensity.     

金刚石薄膜中晶粒尺寸的研究

扫描电子显微研究表明，化学汽相沉积的金刚石薄膜中晶粒大小比较均匀。但随着沉积时间和薄膜厚度的增加，晶粒逐渐变大，且每一层内，存在少量的大金刚石颗粒，讨论了晶粒尺寸变化和大晶粒形成的原因和机制。     

Hydride Vapor Phase Epitaxy of GaN Thick Films by the Consecutive Deposition Process Using GaCl3

GaN buffer and main layers were grown by the conventional hydride vapor phase epitaxy technique using GaCl₃ consecutively. The deposited buffer layers were investigated by atomic force microscopy and X-ray analysis. To examine the behavior of the buffer layers at main layer growth temperature, heat treatment was conducted at 900°C. Based on the results of the buffer layer study, GaN thick films were grown at 1050°C. Optimum deposition conditions of buffer layer from the buffer and main layer studies generally coincided. On the φ scanning pattern, the GaN films grown on (0001) Al₂O₃ were single-crystalline. Band-edge emission dominated photoluminescence was observed at room temperature.     

Silver Electrodeposition from Photographic Processing Solutions

This paper describes the parameters that are important in the industrial practice of silver removal from photographic fixers. The experiments were performed under potentiostatic control using synthetic solutions. The current efficiency was analysed as a function of the cathodic potential taking into account the deposit quality. A cathodic potential of ?0.5 V against a saturated calomel electrode is recommended. The conditions to prevent the darkening of the electrodeposit were investigated. The determination of silver concentration in the solution was made by direct potentiometry. The results obtained with synthetic fixers were corroborated by making the silver deposition from commercial fixers in an electrochemical reactor with rotating cylinder electrode intercalated in an electrolytic flow circuit in order to simulate practical conditions.     

石英晶体监控法镀制高精度光学薄膜

讨论了石英晶体监控法在光学薄膜镀制过程中的应用原理。通过与常规的光学监控法镀制的膜层相比较．证实了石英晶体监控法有助于提高光学薄膜的光学品质。试验表明所镀膜层的光学性能优异，在光通信和激光器等领域具有广阔的应用前景。     

超细氧化锌粉体的制备及尺寸控制

根据气相化学反应法 (CAD)制备超细粉的原理 ,从低品位氧化锌矿中采用火法冶金方法直接制备超细氧化锌粉 ,对所得氧化锌的粒度尺寸、微观结构和粒度分布进行测试 ;考察了冷却强度以及收集装置对超细氧化锌粒度及粒度分布的影响 ;讨论了氧化锌粉体团聚的原因及对策、试验条件对氧化锌尺寸的控制等