淤泥软基爆炸固结试验研究

对爆炸效应在淤泥软基工程中的应用问题进行了探讨，并首次提出了爆炸在淤泥软基中的分界应力特征以及排水固结及破坏分区的基本模式。为采用动力加速对淤泥软基工程的处理，提供了试验依据，具有实用价值和指导意义。     

氧化铝陶瓷缺口件循环疲劳及断裂机理

用实验方法研究了Ａｌ＿２Ｏ＿３陶瓷缺口试件在循环载荷作用下的疲劳寿命。结果表明，缺口导致的应力集中效应显著降低了循环疲劳寿命；若用缺口根部最大应力为应力水平，则不同缺口半径陶瓷试件具有相同疲劳断裂规律，说明陶瓷材料的疲劳集中系数和理论应力集中系数相同。本文还分析讨论了陶瓷材料的循环疲劳寿命表达式和循环疲劳断裂机理。     

板式塔中无伸缩型受液槽的改进

对板式塔中的受液槽进行了改进，将无伸缩型改性伸缩型，避免了漏液，提高了常压塔的分离效果。     

湿硫化氢环境下的球罐腐蚀状况分析

在湿硫化氢环境下 ,尤其储存介质中的硫化氢含量超标时 ,很容易对储存容器壳体 (含焊缝和母材 )造成硫化氢应力腐蚀或氢鼓包。作者较仔细分析了 1 0 0 0m3 丙烯球罐产生硫化氢应力腐蚀开裂和40 0m3 LPG球罐产生氢鼓包的原因。提出了此类设备在设计选材、设备制造、施工安装和使用维护等环节应注意的问题。     

地壳应力场和密度场资料在油气检测中的应用

依据卫星轨道摄动测量结果反演的地壳区域构造应力场和密度场资料，可圈定油气区域构造圈闭和储集油气的低密度层。计算绘制了闽江口扇形洲区域构造应力场和密度卫星遥感图，图上显示出东海近海闽浙中拗陷含油气带与温东丽水油气构造带相接，敖江口官岭与闽江口川石储岛沥青苗等迹象都在此范围内，在闽江口扇形洲东部沿海沙泥沉积区，邻区东海宽长带深厚海沙软泥沉积区及本区北部罗源湾，用大地电磁CSAMT检测到1000－3000m深度范围内的低阻率地层，与本区卫星遥感图图低密度场相符。     

Texture Changes During the Ripening of Port Salut Argentino Cheese in 2 Sampling Zones

ABSTRACT: Texture changes during ripening of Port Salut Argentino cheese for different sampling zones were studied. Compression relaxation tests were performed and results were analyzed using both Maxwellian and Peleg's models. Elastic equilibrium modulus obtained from the Maxwellian model decreased from 1.22 to 0.11 10⁴Pa during ripening. The constants derived from Peleg's model, k₁ and k₂, diminished with ripening time from 1.18 to 0.71 min and from 1.27 to 1.12, respectively. Asymptotic equilibrium modulus from Peleg's model decreased from 0.95 to 0.07 10⁴Pa during ripening. Rate parameters derived from a 1st order kinetics applied to both equilibrium moduli showed that the decrease was faster in the external zone (0.0846 d⁻¹) than in the central zone (0.0368 d⁻¹). The correlation between equilibrium moduli, salt concentration, moisture content, and maturation indexes was obtained with a determination coefficient of 0.76.     

合成氨中置锅炉的修复

本文在分析中置锅炉失效原因的基础上，提出了详细的修复措施，为类似情况的设备修复提供了借鉴。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

Simulation of Strength Distribution in Ground Ceramics by Incorporating Residual Stress Effect

Strength of ground ceramics may be affected by residual stress as well as surface flaws induced by grinding. Strength prediction for ground ceramics is convenient for mechanical design of ceramic components. In this article, a numerical procedure based on fracture mechanics was proposed to estimate strength distribution of ground ceramics by considering grinding-induced residual stress. Bending strength and residual stress of ground ceramics were measured for three grinding-conditions. By comparison of simulated results with experimental ones, it was revealed that strength characteristics in experiments were well simulated by using the proposed procedure.     

Effects of hot-carrier stress on high performance polycrystalline silicon thin film transistor with a single perpendicular grain boundary

This paper is a report on the effect of a single perpendicular grain boundary on the hot-carrier and high current stability in high performance polycrystalline silicon (poly-Si) thin film transistors (TFTs). Under a hot carrier stress condition (Vg = Vth + 1 V, Vd = 12 V), the poly-Si TFT with a single grain boundary is superior to the poly-Si without any grain boundary because of the smaller free carriers available for electric conduction. The shift of transconductance in poly-Si TFT with a single grain boundary is less than 5% after hot carrier stress during a period of 1000 s. The shift of transconductance is about 25% in the case of the poly-Si TFTs without a grain boundary in the channel. On high current stress, the poly-Si TFT without the grain boundary is less degraded than the poly-Si TFT with the grain boundary because the concentrated electric field near the drain junction is lower.