压铸模具钢4Cr5MoSiV1的热处理工艺及组织

介绍了压铸模具钢4Cr5MOSiV1的材质和热处理工艺及组织，分析了组织缺陷，得出了常见缺陷的解决办法。此外，还对4Cr5MOSiV1铜的未来发展趋势进行了展望。     

用深冷处理改善高铬铸铁的性能

将深冷处理工艺引入高铬铸铁的性能研究，初步探讨了深冷处理对材料宏观力学性能及耐磨性的影响。试验结果表明，适当的深冷处理能够提高高铬铸铁硬度、冲击疲劳抗力及滑动磨损与滚筒磨损性能，但作用效果有限。     

Effect of heat treatment on thermal stability of Ti40 alloy

Five new heat treatment processes were designed, which were divided into three groups by their characteristics. The microstructures and mechanical properties of the alloy after the five heat treatments and thermal exposure at 500, 550℃ for 100 h were tested. The results indicate that a little differences exist in the performance of mechanical properties at room-temperature after the five heat treatments, and the thermal stability is the key factor for determining heat treatment process. Among the three groups of heat treatment processes, the best thermal stability is achieved after the first group of heat treatment. After annealing treatment at intermediate temperature, some defects and uneven grain boundaries are remained, which leads to the reduction fractions of precipitations on unit grain boundary and the harmful effect of precipitations on grain boundary is weakened. The process of annealing at 650 ℃for 4 h is recommended the best heat treatment process for Ti40 alloy.     

挤压铸件的热处理起泡缺陷研究

热处理起泡是挤压铸件常见的缺陷之一,它与挤压方式、工艺、模具等有关。对直接挤压铸件,只要不用油剂涂料,解决好排气,均能顺利进行固溶热处理,对于间接挤压铸件,还要设计好其内浇道系统,并严格控制好液态金属充型速度,防止夹杂等,也是可以进行固溶热处理的。     

多孔体制备工艺对C/C-SiC复合材料弯曲性能的影响

以针刺整体炭毡为坯体,采用CVD和树脂浸渍／炭化混合法增密制备了4种C／C多孔体,然后熔硅浸渗C／C多孔体制备了C／C-SiC复合材料;研究了不同炭涂层、高温热处理对C／C-SiC复合材料弯曲强度和断裂方式的影响。结果表明：热解炭涂层可减少制备过程中炭纤维的损伤,具有适中的界面结合强度,使复合材料的弯曲强度达到161．5MPa,表现出良好的“假塑性”;适当选择高温热处理工艺可制备弯曲性能较高,具有一定“假塑性”的C／C-SiC复合材料。     

热轧态Cu-Fe-P合金的相变动力学研究

通过对热轧态Cu—2．5％Fe—0．03％P—0．1％Zn合金导电率与析出的第二相体积分数之间的变化关系的测定与分析，研究了该合金的相变动力学。由合金在不同温度时效时的导电率实验数据确定了该合金的相变动力学方程的系数，从而描绘出不同温度时效时的相变动力学“S”曲线以及等温转变TTT曲线。     

Solar furnace surface treatment of plasma-sprayed thermal barrier coatings

An original process of superficial thermal treatment is described. This process has been successfully applied to partially stabilized yttria-zirconia coatings (ZrO₂-Y₂O₃) to increase the lifetime of the thermal barriers. A thin superficial layer was melted, and morphological transformations were observed. A microstructural comparison between as-sprayed layers and thermally treated layers is presented.     

W-Cu合金深冷处理及其组织性能研究

对粉末冶金熔渗技术制备的不同成分W—Cu合金在-196℃，保温48h进行深冷处理。采用X射线衍射仪和透射电子显微镜分析长时间深冷处理的现象与机理。结果表明：深冷处理后铜颗粒以短棒状形态在钨基体上弥散析出。析出的细小弥散的铜颗粒阻碍晶粒粗化和位错移动，铜颗粒部分填充到材料微孔内，同时深冷处理过程中的体积收缩也使材料内的部分缺陷如空位和微孔得到弥合，从而使不同成分的W—Cu合金的硬度提高，密度增大，电导率降低。     

外场处理对低合金钢焊接接头组织和性能的影响

研究了电磁搅拌、氩弧表层处理、超声喷丸处理对低合金钢焊接接头组织和性能的影响。结果表明 :电磁搅拌促进奥氏体晶粒内针状铁素体生成和细化 ,使针状铁素体的含量由 85%提高到 92 % ,从而提高了焊缝金属的韧度。氩弧加热处理使焊缝表层发生熔化和重结晶 ,可消除焊缝表层的柱状晶 ,处理后的组织主要由针状和细晶铁素体组成。对接头焊趾部位进行氩弧快速重熔处理可消除焊趾部位的几何截面突变 ,使焊缝与母材圆滑过渡 ,有利于消除焊趾部位的应力集中 ,对抗应力腐蚀性能十分有益 ;焊趾部位热影响区中粗大的晶粒细化。表面高能喷丸处理使焊接接头表面层形成尺寸均匀的等轴状纳米晶 ,不仅提高了表层的硬度 ,而且可使焊接接头的疲劳强度提高 50 %。     

热处理对铸铁基多孔陶瓷复合材料组织与性能的影响

研究了热处理对铸铁基多孔陶瓷复合材料组织与性能的影响，结果表明，热处理正火，淬火均可不同程度地提高该复合材料的整体强度与耐磨性，而不影响铸铁－陶瓷的界面结构及材料的透气性。