薄板坯连铸连轧工艺对铌微合金化高强度钢组织和性能的影响

首先建立薄板坯连铸连轧工艺的试验室模拟技术，并运用该模拟技术，研究薄板坯连铸连轧工艺(CSP)和传统板坯再加热工艺(TRP)两种工艺对铌微合金化高强度钢的显微组织和力学性能的影响。研究结果表明：CSP钢的晶粒细化效果不如TRP钢，两者的平均铁素体晶粒尺寸分别为8．17μm和6．30μm。在CSP试验钢板中铌的析出量较大，特别是在铁素体中细小颗粒的铌的析出物较多，沉淀强化效果较强。CSP试验钢的σ0.5和σb分别较TRP工艺低约40MPa和约25MPa，同时其低温冲击韧性较好，FATT温度较低。     

尖晶石型纳米钴蓝陶瓷颜料的制备

采用化学共沉淀法作为钴蓝颜料的制备方法,探讨了主要工艺因素对制备钴蓝颜料性能的影响,对制备的样品进行了测试与表征。结果表明:Co2+和Al3+物质的量比为1∶2.5时,制备的钴蓝样品颜色饱和度与明度最高,沉淀剂为尿素时制得的样品的粒度最小,粒度分布比较均匀。前驱体的洗涤过程采取水洗加醇洗的方法可有效减少样品的硬团聚现象,且前驱体的最佳煅烧温度为950℃左右。     

Effect of pH on the Crystallization of Homogeneously Precipitated Nanosized PZT Powder

Nanosized lead zirconate titanate (PZT) powder with Zr:Ti ratio in the morphotropic phase boundary region was synthesized by homogeneous precipitation of metal ions. The powder precipitated at 90°C and at pH 6.7 resulted single-phase perovskite lead zirconate titanate powder when calcined at 550°C and above for 4 hours in air. The solution pH and the precipitation temperature strongly affect the composition of the calcined powder. The results obtained by structural characterization of homogeneously precipitated powder were compared with that obtained from the conventional precipitation method using ammonia in terms of crystallization, homogeneity, and microstructure. The homogeneously precipitated powder showed smaller particle size, minimum agglomeration and uniform shape on calcination and annealing. Powdered samples that precipitated by homogeneous precipitation crystallized directly to perovskite PZT, without any intermediate pyrochlore phase formation. In contrast, the NH₃ precipitated powder converted to perovskite PZT via metastable pyrochlore and it showed phase segregation upon annealing at higher temperatures. The reaction kinetics has been studied by X-ray diffraction, differential thermal analysis, and differential scanning calorimetry.     

System for Sewing Machine Industry Standard Innovation——Constructive Research for a Technical Standards System for Sewing Machines

Constructive research of a market-oriented industry's system of technical standardization by redefining those technical standards is the basis of innovation. Through considering and implementing innovation of the industry's standards,rapid development and standardization of the industry can be achieved.     

钢带试样位向及拉伸性能的探讨

从碳素结构钢热轧钢带各向异性的事实出发 ,阐述不同试样位向导致同一钢带不同的拉伸性能 ,因而影响钢带合格与否的判定。在全面考虑钢带和焊管标准的基础上 ,提出解决钢带判定的两种方法。同时 ,还对标准中存在的缺点作了说明 ,提出改进意见 ,供标准修订时参考。     

How Meta-Analysis Increases Statistical Power.

One of the most frequently cited reasons for conducting a meta-analysis is the increase in statistical power that it affords a reviewer. This article demonstrates that fixed-effects meta-analysis increases statistical power by reducing the standard error of the weighted average effect size (T?.) and, in so doing, shrinks the confidence interval around T?.. Small confidence intervals make it more likely for reviewers to detect nonzero population effects, thereby increasing statistical power. Smaller confidence intervals also represent increased precision of the estimated population effect size. Computational examples are provided for 3 effect-size indices: d (standardized mean difference), Pearson's r, and odds ratios. Random-effects meta-analyses also may show increased statistical power and a smaller standard error of the weighted average effect size. However, the authors demonstrate that increasing the number of studies in a random-effects meta-analysis does not always increase statistical power. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

《钢结构工程施工质量验收规范》修订简介

简要介绍《钢结构工程施工质量验收规范》(GB 5 0 2 0 5 - 2 0 0 1)的修订原则、方法以及对原规范进行修订中新增加的内容及要求 ,并进行了详细解释 ,以便于对新规范的理解     

NaAlO_2-Al_2(SO_4)_3法制备拟薄水铝石成胶机理的研究

研究了拟薄水铝石和三水氧化铝的生成机理。考察了成胶pH、成胶温度对生成物类型的影响,在此基础上确定了NaAlO2溶液和Al2(SO4)3溶液成胶过程中完全中和时的临界体积比Ψ/Ψ0,在成胶过程中,当Ψ/Ψ0≤1时,NaAlO2溶液与Al2(SO4)3溶液发生中和反应生成拟薄水铝石和/或碱式硫酸铝;当Ψ/Ψ0>1时,过量的NaAlO2溶液发生自发水解反应,生成三水氧化铝。     

高纯超细氧化铝的制备

介绍一种利用氧化铝生产过程的中间物料———铝酸钠溶液 ,生产高纯超细氧化铝的方法 ,即利用钡盐净化铝酸钠溶液 ,得到A/S >10 0 0 0的精制溶液 ,再进行种分分解 ,得到超细Al(OH) 3 ,经过酸洗 ,最终得到纯度达 99 99% ,粒度 90 %小于 2 μm高纯超细氧化铝。