Austenitizing treatment influence on the electrochemical corrosion behavior of 0.3C-14Cr-3Mo martensitic stainless steel

Effects of austenitizing treatment temperatures on aqueous corrosion properties of martensitic stainless steels were investigated by electrochemical tests (potentiodynamic test, potentiostatic test and electrochemical impedance spectroscopy), and surface analyses (optical microscopy and XRD). The results of potentiodynamic test revealed that the breakdown potential increased with the increased austenitizing temperature, indicating increased relative resistance to initiation of localized corrosion. EIS measurements showed that MSS3 (1030 °C) exhibits larger polarization resistance value than MSS1 (970 °C) and MSS2 (1000 °C) at passive and breakdown states. This was caused by decreasing the amount of Cr-rich M₂₃C₆ carbide which acts as preferential sites for pitting corrosion.     

Microstructural Investigation on Failure of Internal Drive Shaft

17-4 PH stainless steel is used as internal drive shaft material in liquid engine pumps. One of the drive shafts failed during operation. The shaft pieces were in contact for short duration after failure, which has resulted in abrasion of fractured surfaces. Samples from the location of failure were taken, and investigation of the failure was carried out using optical and scanning electron microscopy. The microstructural analysis of the material and fractographic analysis of the fractured surface show that the failure was caused by excessive torsion.     

海洋平台双相不锈钢管线的焊接

就双相不锈钢的特异性能．介绍双相不锈钢管线的焊接特点与技术。     

钢带试样位向及拉伸性能的探讨

从碳素结构钢热轧钢带各向异性的事实出发 ,阐述不同试样位向导致同一钢带不同的拉伸性能 ,因而影响钢带合格与否的判定。在全面考虑钢带和焊管标准的基础上 ,提出解决钢带判定的两种方法。同时 ,还对标准中存在的缺点作了说明 ,提出改进意见 ,供标准修订时参考。     

重轨钢非铝脱氧工艺研究

介绍了攀钢重轨钢非铝脱氧工艺，在满足钢中脆性夹杂物控制的前提下，采取“预脱氧＋终脱氧”的工艺，达到钢液脱氧良好，钢轨内部质量大幅提高，钢轨T[O],[Al]及氧化物夹杂评级完全满足200km/h高速铁路钢轨标准的要求。     

65 Mn热轧带钢表面裂纹分析

分析了热轧带钢表面裂纹产生的原因，介绍了采取的工艺措施及其效果。     

模拟焊后热处理对锅炉用钢板SA-299力学性能的影响

对新日铁供货的SA-299钢板取样进行了供货状态及610～650℃/8h炉冷的模拟焊后热处理,以进行力学性能对比试验。试验结果表明,经过630℃/8h炉冷的模拟焊后热处理后σs降低25～40MPa、σb降低55～65MPa,但力学性能符合ASMESA-299标准和采购规程C1F19-98的要求。     

Effect of RE－Al－N on Structures and Properties of M2 Cast High Speed Steel

M 2highspeedsteel (M 2steel)isamaterialwidelyusedintoolsanddies[1,2 ] .M 2steelischarac terizedbyalongsolidificationrangeandcomplexeu tecticreactions ,whichresultsinsegregationofalloy ingelementsandformationofseveraldifferenttypesofcarbidesduringsolidification[3,4 ] .Forconventionallyprocessedhigh speedsteels ,itisinevitablethatacoarsecarbidenetworkwillbeformedduringsolidifi cation .Coarseprimarycarbidestendtoresultinun evencarbidebandsdistributionafterasubstantialamountofhotprocessing[5] .Ma…     

转炉出钢口套整体袖砖工艺技术开发

介绍了天津天铁冶金集团有限公司炼钢厂转炉出钢口袖砖工艺的开发过程，主要工艺参数的制定，实践证明，该工艺的应用取得了良好的使用效果。     

Improvement in Stress Corrosion Crack Growth Resistance of an Austempered Cast Steel by a Novel Two-Step Austempering Process

An investigation was carried out to examine the influence of microstructure on the stress corrosion cracking (SCC) growth behavior of an austempered high-carbon (1.00%), high-silicon (3.00%), and high-manganese (2.00%) cast steel. Compact tension specimens were prepared from this cast steel as per American Society for Testing Materials standard E-399 and were given four different heat treatments to produce different microstructures. The SCC behavior of these specimens was studied in 3.5% NaCl solution. The test results indicate the K_ISCCvalue of the material increases as the austenite content increases. Significant improvement in SCC resistance was achieved by using a novel two-step austempering process. Intergranular crack growth was observed in all these specimens.