Catalytic reduction of N2O with CH4 and C3H6 over Ag–Rh/Al2O3 bimetallic catalyst in the presence of oxygen

A study of nitrous oxide (N₂O) reduction with methane (CH₄) and propene (C₃H₆) in the presence of oxygen (5%) over Ag/Al₂O₃, Rh/Al₂O₃ and Ag–Rh/Al₂O₃ catalysts, with Ag and Rh loadings of 5 wt% and 0.05 wt% respectively, has been performed. From the results, it was observed that the Ag–Rh bimetallic catalyst was the most active for both nitrous oxide removal (more than 95%) and hydrocarbon oxidation. This high activity seems to be connected with a synergistic effect between Ag and Rh. The findings from X‐ray diffraction and X‐ray photoelectron spectroscopy studies showed also, that there were no strong interactions (eg alloying) between Ag and Rh. Copyright © 2005 Society of Chemical Industry     

爆炸焊接——热轧双相不锈钢复合钢板研制

本文主要阐述了通过爆炸焊接和热轧的方法,研制成功可焊性良好的且具有较好强度、韧性与综合性能的双相耐应力腐蚀的不锈复合钢板。还将热轧与热处理的两种试验作了较全面的常规、特殊检验试验,结果完全达到使用要求。     

Exchange and oxidation of CO on O-predosed Rh---Al2O3 and Rh---CeO2 catalysts

Exchange and oxidation of C¹⁶O were investigated at 450°C on ¹⁸O-predosed Rh and Pt catalysts supported on A1₂O₃, CeO₂ and CeO₂-Al₂O₃. In all cases, a rapid exchange of C¹⁶O with the surface can be observed. CO oxidation leads to C¹⁶O₂, C¹⁶O¹⁸O and C¹⁸O₂. Significant formation of C¹⁶O₂ is due to the relatively high ¹⁶O coverage in reaction resulting from the C¹⁶O exchange and from an exchange between O surface species and ¹⁶O internal atoms. Hydrogen is also formed via a water-gas shift reaction (CO + surface OH) in higher proportion on CeO₂-containing catalysts than on A1₂O₃. Chlorine inhibits all the reactions (exchange, oxidation and WGS) and particularly the internal exchange.     

Experimental and numerical investigation of fracture in double-edge notched steel plates

Double-edge notched (DENT) steel plates were pulled until complete fracture and several experimental observations were made (using profilometry and scanning electron microscopy). The essential work of fracture (EWF) model was found to be well verified. Numerical simulations—up to the maximum load only—of some experiments were performed using the finite element method (FEM), and incorporating geometric and material non-linearities (large deformation elasto-plasticity). Some experimental measurements were compared with the corresponding numerical computations and excellent agreement was found.     

WC对Cu/WC_P复合材料性能及组织的影响

通过ＷＣ含量对ＷＣ／Ｃｕ复合材料性能的影响，确定了冷压－烧结法制备Ｃｕ／ＷＣ材料的适宜ＷＣ含量为１０ｖｏｌ％左右。并就ＷＣ对该材料组织和再结晶行为的影响进行了有益的探讨。     

氧化铝/锌合金复合材料界面的SEM观察

利用挤压铸造制备氧化铝／锌合金复合材料，在扫描电镜（ＳＥＭ）上观察复合材料的界面。结果表明，在复合材料中纤维与基体间存在致密界面层，合金元素通过适当的化学反应可改善纤维与基体间的结合；在凝固过程中，纤维／基体界面上的硅在共晶体的共生生长过程中起了领先相作用，导致复合材料的共晶转变是由铝硅共晶转变和锌铝共晶转变两者组成。     

简易炉外处理在电炉钢生产中的应用

阐述了小电炉采用投资少，见较快，简单易行的炉外处理措施，提高了钢质量和生产率，生产实践和应用结果表明，本措施可为同类型企业的炼钢工艺完善和技术进步提供参考。     

THE FRACTURE MECHANISM OF 475°C EMBRITTLEMENT IN A DUPLEX STAINLESS STEEL

The mechanism of “475°C embrittlement” of a duplex stainless steel was investigated using finite element modelling of the stress distribution at brittle fracture initiation. Brittle fracture initiated at a critical shear stress, which increased with ferrite hardness. The fracture stress was affected by the duplex microstructure. Fracture was nucleated by deformation twins, which were identified using electron back-scatter diffraction. The ductile-to-brittle fracture transition was sensitive to age-hardening and could be described simply by the effect of age-hardening and test temperature on the yield stress.     

单轴-平面W型复合锶铁氧体的制备及其吸波特性研究

用草酸盐共沉淀和微量掺杂法研制六角晶系W型Ni,Zn,Co,Al多元复合锶铁氧体，通过调节Ni2W同Co2W的摩尔比例，可使该种铁氧体易磁化方向从C单轴型向垂于C轴的平面型转化，控制置换锶铁氧体中部分Fe3 的微量掺杂Al3 ，可以调整4πMs值，提高磁晶各向异性场，测试分析了5种不同含Co量的W型复合锶铁氧体粉料涂层的吸波特性，发现其自然共振吸收峰随Co含量增加向低频方向偏移，最高吸收峰可达32．8dB，是适用于电子隐形技术的高品位的微波吸收剂。     

Failure analysis of a wire rope

Wire ropes, pulleys, counterweights, and connecting systems are used for auto tensioning of contact wires of electric railways. A wire rope in one such auto tensioning system suffered premature failure. Failure investigation revealed fatigue cracks initiating at nonmetallic inclusions near the surface of individual wire strands in the rope. The inclusions were identified as Al-Ca-Ti silicates in a large number of stringers, and some oxide and nitride inclusions were also found. The wire used in the rope did not conform to the composition specified for AISI 316 grade steel, nor did it satisfy the minimum tensile strength requirements. Failure of the wire rope was found to be due to fatigue; however, the ultimate fracture of the rope was the result of overload that occurred after fatigue failure had reduced the number of wire strands supporting the load.