Filler Wetting in Miscible ESBR/SSBR Blends and Its Effect on Mechanical Properties

The selective wetting behavior of silica in emulsion styrene butadiene rubber (ESBR)/solution styrene butadiene rubber (SSBR) blends is characterized by the wetting concept, which is further developed for filled blends based on miscible rubbers. It is found that not only the chemical rubber–filler affinity but also the topology of the filler surface significantly influences the selective filler wetting in rubber blends. The nanopore structure of the silica surface has been recognized as the main reason for the difference in the wetting behavior of the branched ESBR molecules and linear SSBR molecules. However, the effect of nanopore structure becomes more significant in the presence of silane. It is discussed that the adsorption of silane on silica surface constricts the nanopore to some extent that hinders effectively the space filling of the nanopores by the branched ESBR molecules but not by the linear SSBR molecules. As a result, in silanized ESBR/SSBR blends the dominant wetting of silica surface by the tightly bonded layer of SSBR molecules causes a low‐energy dissipation in the rubber–filler interphase. That imparts the low rolling resistance to the blends similar to that of a silica‐filled SSBR compound, while the ESBR‐rich matrix warrants the good tensile behavior, i.e., good abrasion and wear resistance of the blends.

     

锆元素对Zn-15Al钎料组织和性能的影响

通过扫描电镜、X射线衍射和纳米压痕等方法研究了微量Zr元素对铝合金/不锈钢异种金属钎焊用Zn-15Al钎料显微组织和性能的影响.结果表明,微量Zr元素的添加对钎料的熔点没有明显影响.Zr元素对Zn-15Al钎料基体中η-Zn相有明显细化作用,当Zr元素的质量分数为0.2%时,细化效果最佳;Zr元素的添加量过多时,钎料中形成块状的Al₂ZnZr化合物.当Zr元素的质量分数为0.2%时,Zn-15Al-0.2Zr钎料在不锈钢和铝合金母材上的铺展面积较Zn-15Al钎料分别提高了15.9%和10.2%,钎焊接头抗剪强度达到最大值143 MPa.Zn-15Al,Zn-15Al-0.2Zr,Zn-15Al-0.3Zr 3种钎料的蠕变应力指数分别为6.64,7.35,8.07.     

Sn改性Ti-Zr-Cu-Ni钎料的微观组织和力学性能

采用自制Ti-Zr-Cu-Ni-Sn钎料钎焊TA2钛合金,研究了不同Sn元素含量改性Ti-Zr-Cu-Ni钎料的熔化特性、微观组织及物相、润湿及熔蚀性、接头拉伸强度。研究表明,Sn含量增加,Ti-Zr-Cu-Ni-Sn钎料固、液相线温度基本升高,但温度差值基本变窄,可更好地抑制钎焊界面脆性化合物形成。Ti-Zr-Cu-Ni-5Sn钎料组织由Ti、Zr基体和晶体相构成,Sn倾向与Ti、Zr结合形成Ti₂Sn₃、Ti₆Sn₅、Zr₅Sn₃等低熔点共晶相。Sn≤1.5%时,随Sn含量增加,钎料对TA2钛合金的润湿性逐渐变差;继续增加Sn,钎料润湿性改善,添加5%Sn的钎料对基体润湿最佳。添加5%Sn并降低Cu、Ni总量的改性钎料对TA2钛合金熔蚀减弱。相同钎焊工艺下,添加5%Sn接头的强度和塑性均有提升。钎焊温度升高,Ti-Zr-Cu-Ni钎料产生更多强化物相,致接头强度大幅提升,而Ti-Zr-Cu-Ni-5Sn钎料产生的含Sn物相强化作用对接头强度提升有限;相...     

SiC纳米线对Ni-Cr-P钎料及Ni-Cr-P/Q235焊点组织与性能影响

采用具有优良高温强度、高热导率、高耐磨性能和耐腐蚀性能的SiC纳米线为Ni-Cr-P钎料的添加物,研究了钎料/焊点的组织与性能。结果表明,钎料的组织由Ni(Cr)固溶体、Ni₃P固溶体以及Ni(Cr)和Ni₃P共晶组织组成,微量的SiC纳米线可以显著细化基体组织,使焊点抗剪切强度提高29.6%。SiC纳米线的添加使钎料的熔化温度提高约4℃,显著促进钎料在Q235基板表面的润湿性,增幅达到12.5%。然而,过量添加SiC纳米线会显著粗化基体组织,降低钎料的润湿性和焊点的抗剪切强度。在不同SiC含量的Ni-Cr-P钎料中,Ni-Cr-P-0.1SiC钎料/焊点具有明显的优越性。     

硫酸盐侵蚀水泥改良路基段上拱研究

首先对某高速铁路无砟轨道路基上拱问题进行了资料调研,通过现场变形监测、填料取样试验、矿物成分分析等手段,明确了硫酸盐侵蚀水泥改良填料膨胀是引起路基上拱主要原因,然后结合化学反应机理和室内模拟试验,对发生此类膨胀变形的反应条件、膨胀变形特征进行了分析。研究结果表明,膨胀变形主要发生在路基水泥改良填料层位,该土层具有大量硫酸盐侵蚀水泥产物钙矾石和硅灰石膏发育的特征,路基上拱与硫酸盐侵蚀水泥改良土形成钙矾石和硅灰石膏晶体相关;水泥改良填料中相对潮湿的高PH值碱性环境和石膏等硫酸盐矿物的存在是发生此类膨胀变形的必要条件;硫酸盐侵蚀水泥改良填料将发生持续性膨胀变形,上拱持续时间可达数年,破坏性强。本文研究成果可供类似环境下路基工程的建设及相关研究借鉴。     

三种不同导电填料对聚氨酯导电涂层应用性能的影响

目的 筛选出对聚氨酯涂层导电性能改善最佳的导电填料和助剂。方法 使用三种不同的无机导电填料—微米级ITO、微米级导电云母和导电钛白粉,用不同的分散剂DISPERBYK-P104S、DISPERBYK- 163、DISPERBYK-2001对三种无机填料分别进行分散处理改性,选出对改性填料分散性最好的助剂,然后研究用该助剂改性的填料对聚氨酯树脂涂层导电性、力学性能、耐热性能等应用性能的影响,最终选出最好的导电填料。结果 利用沉降试验,筛选出了提高填料分散性能最好的助剂为DISPERBYK-P104S。通过测试涂层的导电性能、耐腐蚀、力学性能和耐热性能发现,用助剂DISPERBYK-P104S改性过的导电钛白粉掺入聚氨酯树脂涂层后,所有性能均优于其余填料掺入的涂层。涂层的电阻在室温下最小,为10.84 MΩ,而且在100 ℃加热2 h后,电阻仍然只有24.53 MΩ。水接触角（WCA）方面,该涂层初始时接触角为107°,在3.5% NaCl溶液中浸泡400 h后,水接触角仍能达到90°以上。涂层在3.5% NaCl溶液中浸泡800 h后,附着力仍然在2.1 MPa以上。该涂层拉伸强度为16.53 MPa,拉断伸长率为650%,具有较好的弹性和力学强度。同时,在300 ℃下烧蚀三次后（每次15 min）,该涂层的表面仍然保持平整。结论 当导电填料为用DISPERBYK-P104S改性过的导电钛白粉时,聚氨酯树脂涂层的表面电阻在100 ℃以下均介于0.5~25 MΩ之间,而且该导电涂料的其他应用性能为最佳。     

TiZrNiCu/Ti60润湿性及与TiBw-TC4钎焊研究

本文采用座滴法在真空下系统研究了硼含量对TiZrNiCu/Ti60润湿性的影响,且在940°C保温10分钟条件下实现了与的钎焊。通过SEM、XRD以及剪切实验研究了界面显微组织及剪切力学性能。添加B元素可以与Ti原位合成TiBw,从而细化界面的显微组织。当B含量为0.3 wt %时,TiBw-TC4 /TiZrNiCu-B/Ti60接头的最大剪切强度为177 MPa,比无B含量的接头强度高65%。然而,过量的B含量使TiZrNiCu-B在Ti60合金基体上产生大量的TiBw,导致润湿性恶化,在钎焊接头形成微孔和未焊合区域,从而使剪切强度下降。     

A brief review of brazing diamond in cutting tools

Diamond has high hardness and good wear resistance. It is widely used in cutting tools and workpieces. Brazing is an effective method to realize high quality cemented carbide joints in various materials connection technologies. This paper analyzes the research status of diamond brazing in detail. The materials used as brazing filler in diamond brazing are reviewed. Copper base filler and nickel base filler are the most commonly used brazing filler in diamond brazing. The advantages and disadvantages of diamond grinding tools under different production methods are analyzed. In addition, a series of new brazing alloys such as amorphous Ni based brazing filler metals are analyzed. Finally, the development trend of diamond brazing is pointed out.     

石墨烯纳米片对AgCuTi钎料熔点与润湿性的影响

采用球磨法在AgCuTi钎料中添加不同质量分数的石墨烯纳米片(GNSs)制备出复合钎料,利用差示扫描量热仪(DSC),SEM以及XRD等方法研究了微量的石墨烯纳米片对AgCuTi钎料微观形貌、熔点以及在蓝宝石表面润湿性的影响. 结果表明,球磨法对GNSs-AgCuTi复合钎料的物相没有影响,石墨烯均匀地分散在AgCuTi颗粒周围;复合钎料熔点随着石墨烯含量的增加而降低,当石墨烯含量为0.5%,熔点降低了3.2 ℃;微量的石墨烯,改善钎料在蓝宝石表面的润湿性,0.3%GNSs-AgCuTi复合钎料的润湿角减小了4.4°,铺展面积增加了10 mm2,而过多的石墨烯也使得复合钎料的润湿性变差;石墨烯与元素Ti反应生成TiC,复合钎料与蓝宝石界面反应产物为Ti₃Cu₃O相.     