钯－银合金膜分离氢气的研究

采用厚为５０μｍ的Ｐｄ／Ａｇ（２３）合金膜进行了氢气渗透系数的测定和Ｈ＿２／Ｎ＿２混和气分离的研究，得出温度、压力、膜厚、进料气流量、膜的预处理和再活化及膜表面中毒等因素对氢气渗透的影响。分离Ｈ＿２／Ｎ＿２混和气可获得高纯氢气。     

CJ91胶粘剂在螺旋振动光整机中的应用

螺旋振动光整机槽内壁的橡皮保护层由于老化及磨损等原因出现裂口甚至脱落现象，严重影响设备的使用寿命和闸把壳体的外观质量。通过分析和试验筛选出螺旋振动光整机的理想胶粘荆——CJ91胶粘剂并介绍了粘接修补工艺。     

Cu-Zn-Al形状记忆合金直接淬火和分级淬火后马氏体稳定性的研究SCIEI

用透射电镜,X射线衍射仪和电阻法研究了Cu-14.84wt-％Zn-7.75wt-％Al形状记忆合金在直接淬火和分级淬火后马氏体的稳定性。试验结果表明,直接淬火和分级淬火(150℃,2min)后于室温时效约3h的马氏体均为M18R结构,但刚直接淬火后马氏体并不稳定,其某些衍射峰位置和电阻率均随室温时效而变化;而分级淬火(150℃,2min)后马氏体是稳定的,其所有衍射峰位置和电阻率几乎不随室温时效而变化。上述结果可用“马氏体再有序化机制”解释。     

Large magnetic-field-induced strains in rare earth polycrystalline Ni-Mn-Ga

The magnetic-field-induced strains (MFIS) of polycrystalline Ni50Mn29Ga21 alloys containing Tb were studied. A large MFIS of-1.10% was obtained under compressive prestress conditions. The addition of Tb can fine the crystal grains, enhance the bending strength obviously, and make MFIS increase further, indicating that a moderate amount of Tb does not hinder twin boundary motion and it conversely makes the material more practical.     

镁合金废料的回收

在镁合金零部件生产过程中，特别是在压力铸造生产中，产生出来的废料以及使用后报废的镁合金零件逐渐增多。出于成本和环境因素的考虑，必须对这与日俱增的镁合金废料进行有效回收。本文以生产占90％的镁合金零部件压力铸造为主线，介绍镁合金废料回收的经济分析，镁合金废料的来源和分类、现行回收技术的现状及发展趋势。并介绍香港生产力促进局和重庆硕龙科技公司最近研究开发的一种新型镁合金废料现场精炼回收系统。     

坯料外形对镁合金矩形盒拉深成形的影响

用商业有限元软件模拟了在同一套模具和成形条件下不同毛坯外形的镁合金矩形盒拉深成形过程．依据数值模拟结果，分析了不同坯料外形对镁合金矩形盒拉深成形的影响。结果表明：使用矩形圆角坯料比其他坯料的成形性能好。     

用双层辉光等离子法在钛表面制备的Ti-Pd合金层性能研究

采用双层辉光等离子冶金技术在纯钛表面制备了Ti—Pd合金层。其深度大约为90μm，Pd含量呈梯度变化，并出现了TiPd3，TiPd2，Ti2Pd3，Ti3Pd5，TiPd，Ti4Pd等6种化合物相和Pd相。合金层在100℃的NaCl饱和溶液＋HCl溶液以及40℃的8．6％H2SO4溶液中的耐缝隙腐蚀性能优于Ti0．2Pd合金；在室温80％H2SO4的溶液中，腐蚀速率仅为0．682mm／a，是Ti0．2Pd合金的18．2％：在室温30％HCl的溶液中，表面Ti—Pd的腐蚀速率仅为0．004mm／a，是Ti0．2Pd合金的12．5％。     

A novel electroless silver depositing method for magnesium alloys

Depositing silver on magnesium alloy by both electroless plating and organic coatings was studied. The organic coating was made by immersing samples in organosilicon heat-resisting varnish. In this method the organic coating acts as interlayer between the substrate and silver film. When the reaction starts, silver deposits directly on the interlayer. X-ray diffraction and SEM analysis were used to determine the composition and morphology of the interlayer and silver film. The potentiodynamic polarization curves for corrosion studies of coated magnesium alloys were performed in a corrosive environment of 3.5% NaCl（mass fraction） at neutral pH （6.9）. The results indicate that compared with the substrate, the corrosion resistance of coated magnesium alloys increases greatly. Moreover, the method proposed in this work is environmentally friendly, non-toxic chemicals were used. In addition, it provides a new concept for the corrosion inhibition of magnesium alloys.