Mechanical Activation of Tetracalcium Phosphate

It was found that prolonged high-energy ball-milling of Hilgenstokite (tetracalcium phosphate, TTCP) resulted in a decrease in both particle and crystallite size, leading to a mechanical activation of the compound. This mechanically activated material demonstrated a high reactivity such that, in contrast to highly crystalline TTCP, a setting reaction with water to nanocrystalline hydroxyapatite (HA) and Ca(OH)₂ could be achieved at 37°C. However, crystalline TTCP is practically unreactive at physiologic temperatures because of the formation of a thin HA layer on the particle surface preventing further reaction.     

纳米碳酸钙的表面活化改性研究

本文主要介绍通过加入特定的表面改性剂,制得了表面改性的活性碳酸钙.并对活化过程中的一系列影响因素,如活化温度、活化时间、碳酸钙悬浊液浓度、表面改性剂用量进行了研究.     

纳米碳酸钙的制备及表征

研究了以氧化钙和二氧化碳为原料,化学法制备纳米碳酸钙的工艺条件、添加剂的影响及形态。结果表明:中间体氢氧化钙的初始浓度、二氧化碳的流量、反应温度、搅拌速度及添加剂等在控制制备纳米碳酸钙颗粒的形状和尺寸中均十分重要。透射电镜观察结果表明:通过控制反应及添加剂,可以得到尺寸规整的链锁形、纺锤形和球形纳米碳酸钙。表面能谱证实产品为高纯的碳酸钙。X射线衍射和电子衍射的结果进一步表明:所制纳米碳酸钙均属方解石型六方晶系,a0=0.498 9 nm,c0=1.706 2 nm;为多晶结构。     

中空纤维超滤膜去除乳酸钙中蛋白质的研究

发酵法联合生产乳酸-乳酸钙工艺中,分离出的乳酸钙产品含有蛋白质、还原糖、重金属等杂质,影响产品的品质。本实验研究了中空纤维膜对乳酸钙中蛋白质的去除,并分析了压差、温度、浓度及pH值等因素的影响。得到了较好的工艺操作条件为Δp=0.05MPa,Δ=30g/L,30°C,pH=4。进一步提出用多步超滤能提高蛋白质的去除率15%～27%。     

浅析超细碳酸钙的几项主要指标

根据对超细碳酸钙制备研究和应用推广试验的体会和经验，阐述了对超细碳酸钙粒径、晶形、比表面积、吸油值、主含量等几项指标的认识，指出超细碳酸钙的重点发展方向是专用化、系列化、多品种化、功能化。应根据用途的不同，对粒径大小、晶体形状、比表面积、吸油值、主含量等提出具有针对性、各具特色的要求。     

饲料级磷酸氢钙中钙含量偏高的原因

通过不同温度下的烘干、灼烧实验 ,分析饲料级磷酸氢钙中钙含量偏高的主要原因是产品结晶水含量少 ,仅 0 .3个结晶水。取消中和槽蒸汽加热 ,保持常温反应 ;改闪蒸干燥为气流干燥 ;用氢氧化钙作中和剂 ;使饲钙产品中钙含量由平均约 2 8%降至 2 2 %。     

采用改进的温梯法生长氟化钙晶体

对现有的晶体生长温梯法进行改进,将炉内温场分为坩埚底部温度高于坩埚顶部温度的化料区和坩埚底部温度低于坩埚顶部温度的温梯生长区两部分.通过对坩埚相对于温场位置的控制,获得适宜进行熔体均一化和晶体生长条件.生长了尺寸为φ135 mm×150 mm氟化钙(CaF2)晶体,生长的CaF2晶体质量较好,位错密度＜330/mm2,从190 nm到9000 nm透过良好,紫外200 nm处和红外9 μm处透过率可达80%以上.     

普钙产品转化率的数值计算方法

对影响普钙产品转化率的各种因素进行了分析,利用MATLAB 软件包得到了转化率的计算公式,提出了确定未分解磷矿的比例和由倍半氧化物引起的有效磷退化幅度的方法,为生产系统的预测和调整提供了一种途径。     

Structural Modulations in Monoclinic Tricalcium Silicate Solid Solutions Doped with Zinc Oxide, M(I), M(II), and M(III)

Structural modulations in solid solutions of C₃S doped with various amounts of ZnO were investigated via the selected-area electron diffraction method. Three monoclinic modifications (M(I), M(II), and M(III)) were identified in the solid solutions. The modifications had pseudohexagonal subcells that were modulated to form supercells. Coordinates of the reflections attributable to the supercells could be expressed by the following linear combinations of vectors of the reciprocal lattices: m₁(−2 a */5.4 + 2 b */5.4 − 7 c */5.4) for M(I), m₂(− a */5 + b */5 − c *) for M(II), and m₃(− a */6 + b */6 + 7 c */6) for M(III), m₁ and m₂=±1 and ±2, and m₃=±1, ±2, and ± 3. All the monoclinic modifications possessed structural modulations of a one-dimensional type. The modulation waves could be detected as wavy contrasts by high-resolution transmission electron microscopy.     

渤海莱州湾地下卤水纳滤过程的结垢趋势研究

针对莱州湾地下卤水纳滤过程中纳滤膜表面无机物结垢的问题,利用饱和度法系统研究了碳酸钙、硫酸钙在卤水体系和纳滤过程中的结垢趋势和影响因素。结果表明,在常温下原料卤水中的碳酸钙处于饱和状态,而其中的硫酸钙处于不饱和状态,因此在外部因素诱导下,碳酸钙更容易发生沉淀;降低卤水的pH可以有效抑制碳酸钙结垢;当逐步提高卤水的产水回收率时,纳滤浓水侧卤水中硫酸钙结垢的风险增大,在纳滤精制卤水过程中选择合适的产水回收率可以降低硫酸钙结垢的风险。