首钢外购焦炭质量恶化后的高炉生产实践

针对焦炭质量劣化的状况，高炉操作以活跃炉缸为主，从上下部调剂入手，采取疏导煤气、控制合理的实际风速和鼓风动能、缓解焦炭在高温区的粉化等措施，有效地改善了高炉的顺行状况，并逐步恢复高炉指标。     

Dynamic modes of Ti combustion in a coflow of N<Subscript>2</Subscript>-Ar mixture

Combustion of bulk density Ti powder (containing 20 wt % TiN as a diluent) in a coflow of N₂-Ar mixture was investigated upon variation in the nitrogen content of the gaseous mixture. The obtained data are believed to open up new horizons for fabrication of layered and composite ceramics by infiltration-mediated combustion.      

Characteristics of Milk Powders Produced by Spray Freeze Drying

Skim and whole milk powders were manufactured at lab scale by spray freeze drying (SFD), using liquid nitrogen as the cryogen. The polydispersity of droplet/particle sizes was limited using an encapsulator nozzle to atomize the feed. Particle morphology was examined using a scanning electron microscope. Samples were compared with equivalent spray-dried powders in tests of wettability and dissolution in water. The spray freeze-dried powders were found to be highly porous, with a uniform structure of pores throughout the entire particles. When tested in water, SFD skim milk powders wetted roughly three times as fast as industrially spray-dried agglomerated skim milk powders and were observed to dissolve rapidly by breaking down into smaller particles.     

Final Drying of Whole Milk Powder in Vibrated-Fluidized Beds

Vibro-fluidized beds are widely used in drying sticky powders and agglomerated materials as milk powder. Using a vibro-fluidized laboratory scale dryer, this work is aiming at analyzing preliminarily the effect of its operational variables on the drying kinetics and characteristics of whole milk powder. The full-factorial design technique with three replications at the central point has been employed to generate data and correlations to quantify the effect of inlet air temperature, air flow rate, and vibration bed amplitude on the drying curves and the milk powder properties related to its faster reconstitution in water (as tapped density, Hausner cohesion ratio, agglomerate size distribution, and internal pore concentration). Results obtained are analyzed and discussed to identify the adequate operation condition for final drying whole milk powder in vibro-fluidized beds, assuring a high product quality.     

Powder Deposition in Three Parallel-Oriented Dies of Different Shapes

Uniformity of bulk density distribution during the die filling process is required to minimize quality problems, such as distortion and cracking, for powder compacts. Understanding the die filling process is necessary in ensuring a uniform powder deposition. The second-generation pressure deposition tester (PDT-II) was used to investigate the deposition process and final pressure distribution of powder filling in toroidal, cylindrical, and E-shaped dies. All tests were conducted using a spray-dried free-flowing granular powder. The results indicated that for toroidal dies: (1) the area around 0° orientation (the leeward end) had the highest pressure values (1186.7 to 2498.0 Pa), with the average pressure values of the remaining area 353.7-648.0 Pa; (2) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; (3) the highest feed shoe speed (500 mm/s) led to the most nonuniform pressure distribution among the three speeds; (4) higher feed shoe speed did not always result in higher final pressure values; and (5) the right die tended to have higher final pressure values (215.0 to 2498.0 Pa) than the center die (95.4 to 2052.5 Pa). For E-shaped dies: (1) the final pressure values of the middle leg (308.9 to 760.7 Pa) were higher than those of the left and the right legs (148.9 to 530.3 Pa); (2) the area along the backside had the highest final pressure value (1054.6 to 1303.8 Pa); (3) the pressure distribution was symmetrical about the centerline parallel to the feed shoe movement direction; and (4) neither the center die nor the right die always had higher pressure values than the other one at all locations. Comparison between cylindrical and toroidal dies indicated that: (1) neither of the two die shapes (cylinder and toroid) led to consistently higher or lower final pressure values at all locations and (2) for all three feed shoe speeds, the toroidal die had higher average final pressure values in the 0° orientation.     

激光法合成SiC超细粉末物理化学过程的研究——Ⅰ.实验规律及粉末特性

用50W连续波CO_2激光器为热源,诱发SiH_4和C_2H_4反应,合成SiC超细粉末。实验确定了反应腔体内压力p、气源中的C/Si原子比、喷嘴内径2r以及激光功率密度与粉末特性之间的关系,并对合成的产物进行物理、化学表征。     

Development of sealing compositions with nanostructure iron-based fillers

The possibility of utilizing nanopowders of iron and Fe-Co-Ni produced bu a thermochemical method in the fabrication of sealing composition materials is investigated. It is established that such hermetic sealing composition materials function reliably under extremal conditions and guarantee elevated strength of adhesion to the surface of the metal and high corrosion and temperature stability. __________ Translated from Poroshkaya Metallurgiya, Nos. 3–4(448), pp. 112–117, March–April, 2006.     

Synthesis and characterisation of a submicrometre silicon carbide powder

A beta-silicon carbide powder with a surface area of 30m²g^?l and a mean particle size of < 1μm was produced from the thermal conversion of silicon resin in an atmosphere of hydrogen. The amount of product increased with increasing iron content (0–2.1 wt%) and firing temperature (1200–1500°C). Chemical analysis, X-ray diffraction and i.r. absorption spectrometry were used to follow the conversion reaction.     

石油系油浆与煤系闪蒸油的焦化性能——I．热解条件的影响

通过偏光显微镜观察了石油系油浆（LH）与煤系闪蒸油（SN）焦化后所得焦块的光学结构。结果表明，在较宽条件下两种原料单独焦化均得不到取向度高的流线型结构。将两种原料以一定比例混合后先热解丙焦化所得焦块的光学结构明显好于二者混合后直接焦化所得焦块的光学结构，其中LH和SN以3：2的重量比混合后在440℃、1MPa下热解3．5h然后再在530℃、1MPa下焦化8h所得焦块为具有较高取向度的流线型结构，适合于作为针状焦的起始原料。     

THE STICKY ISSUES OF DRYING

Unconrolled agglomeration of particles and adhesion of the particulate mass to wall surfaces are common severe problems in many drying operations. This paper reviews the mechanisms of interparticle and particle-surface attraction as well as the theory and the existing tests for characterising powders in terms of internal strength, wall friction and adhesion. The usefulness of the information obtained from these tests in dryer design and operation is critically reviewed. The importance of powder stickiness in various types of dryers is discussed and established methods of combating the problem are presented Recommendations an made for further research in the area of powder cohesion and adhesion.