含钼废渣冶炼钼铁的优化试验

利用含钼废料钼酸钙为原料,采用碳还原法冶炼钼铁,通过单因素分析试验及正交试验优化得出最佳的试验条件,钼酸钙加入量应低于10%,熔炼温度为1 525 ℃,保温时间为25 min,碱度为1.3。通过XRD、SEM、EDS分析得出用此方法生产得到的钼铁合金中,钼以Mo₂C、Fe₃Mo以及Fe₃Mo₃C的形式存在,渣系为二元玻璃渣系,具有与普通玻璃相似的成分系统。经测定合金中钼的回收率大于99%,钼资源回收效益可观。     

电弧炉短流程冶炼石油套管钢中夹杂物的演变规律

为研究石油套管钢(34Mn6)中夹杂物的演变规律,对钙处理效果进行精准化控制,进行全流程取样分析,通过采用SEM-EDS分析夹杂物形貌和成分,同时结合Aspex夹杂物自动分析仪统计夹杂物的数量、成分和尺寸分布。研究结果表明,LF精炼具有较好的脱硫与脱氧能力;钙处理前,由于渣钢反应的进行,夹杂物数量明显减少,夹杂物成分中SiO₂含量增加;经过钙处理后,夹杂物成分发生显著变化,由MgO-Al₂O₃系转变为MgO-Al₂O₃-CaO系和SiO₂-Al₂O₃-CaO系,夹杂物形貌由尖角夹杂向球状夹杂过渡。在铸坯中,夹杂物数量减少,其成分已偏离液相区,向富CaO区域移动。对钙处理进行优化,通过利用热力学软件FactSage进行计算,得出钢液中钙的质量分数稳定在0.001 3%时对夹杂物的改性效果最佳,钢液中的夹杂物控制较好。     

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Mg-Li ALLOY WITH Ca ADDITION

Mg-9wt%Li-2wt%Zn alloy was prepared and studied in this article. The addition of Ca to the alloy from 0.1wt% to 1wt% can refine the α-Mg and the best effect of refinement occurs when Ca content is 0.4wt%-0.5wt%. The billets can be rolled to thin sheets at room temperature, from which it is obvious that the addition of Ca improves alloys ormalin. while it decreases with the excess addition of Ca. The results also show that the ultimate tensile strength （UTS） and yield strength （YS） of the alloy with lwt% Ca may rise by 28% and 25%, respectively, however, the elongation decreases. It is clarified that the adsorption of proper Ca on the grain boundaries refines α-Mg and improves the tensile properties, but the presence of excess Ca and stable Ca2Mg6Zn3phase worsens the elongation.     

环氧脂肪酸钙/锌的直接合成法及其热稳定作用

以一种简便的方法制备了环氧基保留完好的高纯度环氧脂肪酸钙/锌，并对其热稳定性进行了研究。研究表明，环氧脂肪酸钙/锌对聚氯乙烯（PVC）的热稳定作用类似于硬脂酸钙/锌，但其热稳定效能明显优于后者，环氧脂肪酸钙比硬脂酸钙具有较好的初期着色性，环氧脂肪酸锌较硬脂酸锌具有较长的“锌烧”时间。     

Initial stages of tin electrodeposition from sulfate baths in the presence of gluconate

Tin electrodeposition in its initial stages in acid sulfate/gluconate baths was studied with varying tin and gluconate concentrations using potential-controlled electrochemical techniques. The deposit morphology was observed by scanning electron microscopy (SEM). A comparison with tin electrodeposition from acid sulfate baths in the absence of gluconate was also carried out. Use of a highly acidic bath leads to nonuniform deposits, even in the presence of gluconate; at pH 4 deposits are uniform, brilliant and suitable for finishing applications. Tin crystallites have a well defined morphology which depends on bath agitation conditions. In the absence of agitation, the crystallites have the same tetragonal shape as in a sulfate bath without gluconate.     

硫酸钾生产出现问题的机理分析及改进建议

曼海姆法硫酸钾生产装置出现 3个问题 :原料 KCl中有机碳的分析结果非常高 ;测定副产盐酸总酸度 ,加 1～ 2滴甲基橙不显红色 ;分析副产盐酸中 SO4 2含量超标 (≥ 0 .1% )。分析产生以上问题的原因并提出解决措施     

关于生产精制元明粉的探讨

介绍了以山西运城南风自产芒硝为原料生产精制元明粉的几种工艺,以及国内外精制元明粉的市场及生产状况.精制工艺包括化学除杂法、原料优选法、重结晶法.结果表明,精制元明粉的生产过程实质是一个除杂、提纯过程：对于钙离子含量高的原料,可采用化学除杂法;对于氯离子含量高的原料,可采用氯离子富集法、冷冻法或洗涤法;镁离子较难去除,可采用水硝洗涤、冷冻法.     

The effect of increasing application rate of granular calcium ammonium nitrate on net nitrification in a laboratory study of grassland soils

Soil incubation studies were undertaken in controlled environment cabinets at 15°C to investigate the effect of increasing application rates of calcium ammonium nitrate (CAN) on net nitrification in two grassland soils. Granular CAN was applied to the surface of freshly collected, moist soil, at a rate equivalent to 0, 100, 200, 400, 800 and 1600µg NH ₄ ⁺ -N and NO ₃ ^- -N per gram of oven dry soil. In half the treatments finely ground CaCO₃ was incorporated into the moist soil to raise the starting pH. Changes in soil mineral N and pH were measured at weekly intervals up to six-weeks. The most probable number (MPN) technique was used to enumerate the NH ₄ ⁺ -N and NO ₂ ^- -N oxidizers at the beginning and end of the incubation.At low rates of CAN application there was considerable NH ₄ ⁺ -N oxidation to NO ₃ ^- -N during the incubation of both soils. Lime stimulated this N transformation. At high application rates (i.e. 800 and 1600 ppm) there was little change in NH ₄ ⁺ -N or NO ₃ ^- -N on either soil during the 6 week incubation, in the presence or absence of lime. The rate of NO ₃ ^- -N produced peaked at 5.6 and 3.8 mg NO ₃ ^- -N kg^–1 d^–1 on soil 1 and 2 respectively, in the presence of lime. Above a level of 400 ppm CAN (equivalent to 38 kg N ha^–1) the rate of NO ₃ ^- -N produced decreased. The higher rate of net nitrification in soil 1 compared with soil 2 was probably due to a higher number of nitrifying bacteria. Although high rates of CAN decreased the nitrifying activity of both soils there was little difference between treatments in the actual numbers of NH ₄ ⁺ -N and NO ₂ ^- -N oxidizers determined by the MPN technique.The results showed that the rate of granular CAN applied to the soil surface can influence the local activity of nitrifying bacteria and subsequent N transformations. At application rates of CAN generally used agriculturally for grass production, it is likely that net nitrification of the NH ₄ ⁺ -N in the fertilizer granule will be inhibited.     

纳米碳酸钙原位聚合聚氯乙烯树脂的性能及应用

介绍了纳米碳酸钙原位聚合聚氯乙烯的结构和性能,同时对该树脂进行了有关的应用试验,并对其发展前景作了科学展望。     

火焰原子吸收光谱法测定高纯石英粉中痕量钙

系统地研究了用空气——乙炔火焰原子吸收光谱分析法测定高纯石英粉中钙的最佳条件，建立了14％的乙醇作为增感剂，在2％盐酸介质中，0．4％ LaCl3溶液作为释放剂，用塞曼火焰原子吸收法测定的可行性方案，探讨了共存元素对钙的干扰及其消除。方法操作简便快速，干扰少，方法相对标准偏差小于3％，适用于日常分析石英粉中的杂质。