An infinite chain, {[Ni(tn)2]3[Fe(CN)4(μ-CN)2]2}n,a new catalyst for electrochemical-driven water splitting and photochemical-driven hydrogen evolution from water under blue light

A new catalyst for both water reduction and oxidation, based on an infinite chain, {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n, is formed by the reaction of NiCl₂, 1,3-propanediamine (tn) and K₃ [Fe(CN)₆]. {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n can electro-catalyze hydrogen evolution from a neutral aqueous buffer (pH 7.0) with a turnover frequency (TOF) of 1561 mol of hydrogen per mole of catalyst per hour (H₂/mol catalyst/h) at an overpotential (OP) of 837 mV {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n also can electro-catalyze O₂ production from water with a TOF of ～45 mol O₂ (mol cat)^?1s^?1 at an OP of 591 mV. Under blue light (λ = 469 nm), together with CdS nanorods (CdS NRs) as a photosensitizer, and ascorbic acid (H₂A) as a sacrificial electron donor, {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n can photo-catalyze hydrogen generation from an aqueous buffer (pH 4.0) with a turnover number (TON) of 11,450 mol H₂ per mole of catalyst (mol of H₂ (mol of cat)^?1) during 10 h irradiation. The average of apparent quantum yield (AQY) is as high as 40.96% during 10 h irradiation. Studies indicate that {[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n exists in two forms: a cyano-bridged chain ({[Ni(tn)₂]₃ [Fe(CN)₄ (μ-CN)₂]₂}_n) in solid, and a salt ([Ni(tn)₂]₃ [Fe(CN)₆]₂) in aqueous media; Catalytic reaction occurs on the nickel center of [Ni(tn)₂]²⁺, and the introduction of [Fe(CN)₆]^3- can improve the catalytic efficiency of [Ni(tn)₂]²⁺ for H₂ or O₂ generation. We hope these findings can afford a new method for the design of catalysts for both water reduction and oxidation.     

Influence of surfactants on rheological behaviors of polyacrylonitrile/dimethyl sulfoxide/silicon blending polymer solutions

KH550, KH560, CTAB, and F127 were adopted to modify silicon (Si) to improve the dispersity and stability of Si in the polyacrylonitrile/dimethyl sulfoxide (PAN/DMSO) polymer solutions. The influence of surfactants on rheological behaviors of PAN/DMSO/Si blending polymer solutions was investigated by an advanced solution and melt rotation rheometer. The homogeneity and stability were also studied. The results showed that the surfactants could change the viscosity dependence of blending polymer solutions on shear rate, temperature and storage time by increase the steric hindrance of Si. Among the four solutions, PAN/DMSO/Si blending polymer solution with F127 exhibited the lowest viscosity, activation energy and the smallest structural viscosity index and exhibited the trend close to the Newtonian fluids. Moreover, PAN/DMSO/Si blending polymer solution with F127 exhibited the best dispersity and stability, indicating its best physical properties and machinability.     

Ammonia production using iron nitride and water as hydrogen source under mild temperature and pressure

Ammonia generation was studied in the reaction between water and nitrogen-containing iron at 323 K and atmospheric pressure. Similar to metallic Fe, the interstitial compound Fe₃N reduced water through Fe oxidation to produce hydrogen gas, while the N combined with atomic hydrogen to produce ammonia as a byproduct. The addition of carbon dioxide to this system accelerated the reaction with concomitant consumption of carbon dioxide. The promoted ammonia production upon addition of carbon dioxide can be attributed to the generation of atomic hydrogen from the redox reaction of carbonic acid and Fe, as well as removal of used Fe from the reaction system through the formation of a soluble carbonato complex. When carbonate was added to the reaction system, the production rates of ammonia and hydrogen increased further. The results here confirmed that ammonia can be synthesized from iron nitride under mild conditions by utilizing carbon dioxide.     

Research and development of liquid hydrogen (LH2) temperature monitoring system for marine applications

Monitoring the temperature in liquid hydrogen (LH₂) storage tanks on ships is important for the safety of maritime navigation. In addition, accurate temperature measurement is also required for commercial transactions. Temperature and pressure define the density of liquid hydrogen, which is directly linked to trading interests. In this study, we developed and tested a liquid hydrogen temperature monitoring system that uses platinum resistance sensors with a nominal electrical resistance of approximately 1000 Ω at room temperature, PT-1000, for marine applications. The temperature measurements were carried out using a newly developed temperature monitoring system under different pressure conditions. The measured values are compared with a calibrated reference PT-1000 resistance thermometer. We confirm a measurement accuracy of ±50 mK in a pressure range of 0.1 MPa–0.5 MPa.     

Techno-economical evaluations of decarbonized hydrogen production based on direct biogas conversion using thermo-chemical looping cycles

Hydrogen production by biogas conversion represent a promising solution for reduction of fossil CO₂ emissions. In this work, a detailed techno-economic analysis was performed for decarbonized hydrogen production based on biogas conversion using calcium and chemical looping cycles. All evaluated concepts generate 100,000 Nm³/h high purity hydrogen. As reference cases, the biogas steam reforming design without decarbonization and with CO₂ capture by gas-liquid chemical absorption were also considered. The results show that iron-based chemical looping design has higher energy efficiency compared with the gas-liquid absorption case by 2.3 net percentage points as well as a superior carbon capture rate (99% vs. 65%). The calcium looping case shows a lower efficiency than chemical scrubbing, with about 2.5 net percentage points, but the carbon capture rate is higher (95% vs. 65%). The hydrogen production cost increases with decarbonization, the calcium looping shows the most favourable situation (37.14 €/MWh) compared to the non-capture steam reforming case (33 €/MWh) and MDEA and iron looping cases (about 42 €/MWh). The calcium looping case has the lowest CO₂ avoidance cost (10 €/t) followed by iron looping (20 €/t) and MDEA (31 €/t) cases.     

Nano-Al doped-MoO3 high-energy composite films with excellent hydrophobicity and thermal stability

Developing the thermal stability of metal-based ceramic composites or their films has always been challenging and bottlenecks for the utilization of energy. In this paper, the novel mesh-like functional Al doped-MoO₃ nanocomposite film with even distribution and high purity was firstly fabricated by the high-efficiency electrophoretic deposition and surface modification. The optimal suspension turned out to be the mixture of isopropanol and the additives of polyethyleneimine and benzoic acid. The microtopography, crystalline structure, environmental resistance and thermal stability were analyzed by field emission scanning electron microscope (FESEM), energy dispersive X-ray (EDX), X-ray diffractometer (XRD), exposure and droplet-impacting test, DSC analysis and ignition test, respectively. The water contact angle and sliding angle of product can reach ~170° and <1°, indicating the excellent anti-wetting property. In addition, the high heat-release (~3180 J/g) of product all kept almost unchangeable after six months exposure experiments, demonstrating the outstanding thermostability. The exquisite design idea here can perfectly match microelectromechanical system (MEMS), providing the valuable reference for fabricating other metal-based high-energy composites with long lifespan for real industrial applications.     

Green preparation of vanadium carbide through one-step molten salt electrolysis

Vanadium carbide (VC) as excellent ceramic and functional material is usually prepared by carbothermal reduction of V₂O₅ which must be extracted from a typical V slag by complex processes. Pollutants, such as ammonia-nitrogen wastewater, NH₃ and CO₂ are inevitably discharged. A novel and green method for VC preparation was proposed by one-step co-electrolysis of soluble NaVO₃ and CO₂ in molten salt. It was found that VC with high purity was easily obtained by reducing electrolysis temperature and CO₂ flow rate to 600 °C and 10 mL min⁻¹ at 3.0 V. Besides VC with particles and layered stacking structure in products, a small amount of carbon and oxygen elements existed. The atomic percentage contents of C, V, and O elements in VC were about 50.0%, 44.5% and 3.8%, respectively. During electrolysis, CO₃²⁻ and VO₃⁻ was reduced at about −0.55 V (vs. Ag/AgCl) and −1.38 V (vs. Ag/AgCl), respectively. CO₃²⁻ ions were more easily reduced than VO₃⁻, and was firstly reduced to CO₂²⁻ and then converted to C. Then, VC was prepared by two routes from CO₂ and NaVO₃. One route is that VO₃⁻ ions are firstly electroreduced to VO₂⁻ ions and then are further electroreduced to VC with C. Another route is that VO₃⁻ ions are electroreduced to V which in-situ reacted with C to VC. Both VO₃⁻ and CO₃²⁻ ions are electroreduced by two-step process. In final, VC is in-situ deposited on cathode. It provides a novel and green way to prepare VC and also achieves the high value-added utilization of vanadium slag and CO₂.     

药物相互作用研究在新药研发和审评决策中的应用

药物相互作用改变了剂量效应关系，可能会降低疗效或增加毒性，是临床应用中合并用药治疗时重要的考虑因素。预测具有临床意义的药物相互作用是药物研发过程中获益风险评估的重要环节。本文概述了药物研发过程中药物相互作用研究的目的和意义，体内和体外研究的主要内容；梳理分析了2020年国家药品监督管理局（National Medical Products Administration, NMPA）和美国食品药品监督管理局（Food and Drug Administration, FDA）批准上市的新药药物相互作用研究情况，旨在为我国药物研发过程中药物相互作用研究及其监管审评提供参考。     

Nanolayer CrAlN/TiSiN coating designed for tribological applications

With the goal to produce a hard and tough coating intended for tribological applications, CrAlN/TiSiN nanolayer coating was prepared by alternative deposition of CrAlN and TiSiN layers. In the first part of the article, a detailed study of phase composition, microstructure, and layer structure of CrAlN/TiSiN coating is presented. In the second part, its mechanical properties, fracture and tribological behavior are compared to the nanocomposite TiSiN coating. An industrial magnetron sputtering unit was used for coating deposition. X-ray photoelectron spectroscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, scanning electron microscopy, and transmission electron microscopy were used for compositional and microstructural analysis. Mechanical properties and fracture behavior were studied by instrumented indentation and focused ion beam techniques. Tribological properties were evaluated by ball-on-disk test in a linear reciprocal mode. A complex layer structure was found in the nanolayer coating. The TiSiN layers were epitaxially stabilized inside the coating which led to formation of dislocations at interfaces, to introduction of disturbances in the coating growth, and as a result, to development of fine-grained columnar microstructure. Indentation load required for the onset of fracture was twice lower for the nanolayer CrAlN/TiSiN, compared to the nanocomposite TiSiN coating. This agrees very well with their mechanical properties, with H³/E² being twice higher for the TiSiN coating. However, the nanolayer coating experienced less severe damage, which had a strong impact on tribological behavior. A magnitude of order lower wear rate and four times lower steady state friction coefficient were found for the nanolayer coating.     

Effects of upholstery materials on the burning behavior of real‐scale residential upholstered furniture mock‐ups

Fire spread and growth on real‐scale four cushion mock‐ups of residential upholstered furniture (RUF) were investigated with the goal of identifying whether changes in five classes of materials (barrier, flexible polyurethane foam, polyester fiber wrap, upholstery fabric, and sewing thread), referred to as factors, resulted in statistically significant changes in burning behavior. A fractional factorial experimental design plus practical considerations yielded a test matrix with 20 material combinations. Experiments were repeated a minimum of two times. Measurements included fire spread rates derived from video recordings and heat release rates (HRRs). A total of 13 experimental parameters (3 based on the videos and 10 on the HRR results), referred to as responses, characterized the measurements. Statistical analyses based on Main Effects Plots (main effects) and Block Plots (main effects and factor interactions) were used. The results showed that three of the factors resulted in statistically significant effects on varying numbers of the 13 responses. The Barrier and Fabric factors had the strongest main effects with roughly comparable magnitudes. Foam was statistically significant for fewer of the responses and its overall strength was weaker than for Barrier and Fabric. No statistically significant main effects were identified for Wrap or Thread. Multiple two‐term interactions between factors were identified as being statistically significant. The Barrier*Fabric interaction resulted in the highest number of and strongest statistically significant effects. The existence of two‐term interactions means that it will be necessary to consider their effects in approaches designed to predict the burning behavior of RUF.