20％磷威乳油（沅化938）的配制

２０％磷威乳油（沅化９３８）是一种以有机磷、氨基甲酸酯类农药为有效成分的新的混配制剂，在防治棉蚜、棉铃虫、棉叶螨等方面的增效作用十分显著。它有击倒快、触杀作用强、广谱等特点。该乳油配方先进，独特，系国内首创。生产工艺简单，易于操作，产品性能稳定。     

Synthesis and characterization of thermosensitive composite microsphere latex

Monodisperse aqueous latex dispersions, prepared from mixtures of styrene, N‐isopropylacrylamide, and N,N′‐methylenebisacrylamide, were characterized. Thermosensitive composite microspheres with diameters greater than 1.0 μm, consisting of a polystyrene core and a poly(N‐isopropylacrylamide) shell, were prepared. The morphology of the composite microspheres was observed with transmission electron microscopy, and the particle size of the composite microspheres was estimated with dynamic light scattering. The thermosensitive properties of the composite microspheres were evaluated via the hydrodynamic size of the composite microspheres. The particle size of the composite microspheres decreased with increasing temperature. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 824–828, 2005     

共聚型聚醋酸乙烯酯乳液胶粘剂的研制

利用醋酸乙烯酯与两种烯类单体共聚,研制出防冻性、耐水性较好的环保型聚醋酸乙烯乳液胶粘剂,并通过研究发现聚醋酸乙烯乳液组成(聚乙烯醇、共聚单体以及乳化剂等)均对乳液性能产生影响。     

扩链剂对阳离子聚氨酯乳液性能的影响

本文讨论了用三乙醇胺制备阳离子聚氨酯乳液，三乙醇胺用量，扩链剂，如乙二醇、丁二醇、二甘醇、三甘醇对乳液性能的影响。还讨论了扩链剂对其粘结强度的影响。     

Barocalorimetric technique for monitoring pressurized copolymer reactors

The problem of on‐line estimation of the conversion and composition evolutions in a pressurized batch copolymer reactor with temperature and pressure measurements was addressed. The estimation model consisted of mass and energy balances with a pressure equation built from phase‐equilibrium considerations. The application of a nonlinear geometric estimation approach yielded the underlying solvability condition with physical meaning, a straightforward estimator construction, and a conventional‐like tuning procedure. The resulting barocalorimetric estimator was an on‐line dynamic measurement processor with a model‐based predictor and a measurement‐driven corrector, and whose implementation did not require the polymerization rates and heat‐transfer coefficient function dependencies. The technique was tested with a representative laboratory styrene–butadiene system. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 96: 475–482, 2005     

原位乳液聚合制备聚苯乙烯丁二烯橡胶/凹凸棒石纳米复合材料

采用原位乳液聚合制备了聚苯乙烯丁二烯橡胶(SBR)/凹凸棒石(AT)纳米复合材料。凹凸棒石的存在一定程度上降低了乳液聚合速率,但对最终聚合产物的分子质量及分子质量分布影响不大。凹凸棒石以长0.5～5μm、直径为20～50nm的棒状纤维均匀的分散在SBR基体中。在硫化过程中,凹凸棒石纤维与橡胶形成互穿网络结构,增加了橡胶的交联密度。随着凹凸棒石的填充量增加,纳米复合材料的300%定伸应力和拉伸强度与纯SBR相比均提高了20%～100%,其补强效果明显高于等量的炭黑N330,还表现出良好的耐磨性能。     

有机硅乳液稳定性的研究

以阳离子型乳液聚合为例，详细讨论了聚合反应因素及环境因素对环氧改性有机硅乳液稳定性的影响。结果表明：在聚合反应温度为65℃、催化剂的用量为总加料量的0．3％～0．5％、硅烷偶联剂的用量为D4质量的3％～5％、乳化剂用量为总加料量的10％、阳／非离子型乳化剂的质量比为1．5～1．8、D4与水的质量比为0．3～0．4条件下，制得的环氧改性有机硅乳液稳定性良好；采取急冷的方式中止聚合反应，并以醋酸中和至pH值为6～7，有利于环氧改性有机硅乳液稳定性的提高。     

影响氟改性硅丙乳液聚合及其聚合物膜表面特性的因素

采用种子乳液聚合方法制备了阴、阳离子型氟改性硅丙乳液,用红外光谱对聚合物进行了表征,考察了聚合温度、氟改性单体和种子乳液的用量、乳化剂用量和pH值等因素对转化率和聚合物膜与水之间接触角的影响。结果表明,该聚合物中含有聚硅氧烷链段和CF2基团;聚合温度对转化率的影响较显著;在阳离子乳化体系中,当聚硅氧烷种子乳液、含氟丙烯酸酯单体和乳化剂的用量分别为10%、10%和1.1%时,转化率可以达到90%左右,接触角达到104°以上;随着体系pH值的逐渐增大,阳离子型氟改性硅丙乳液的Zeta电位明显降低,但阴离子型乳液的Zeta电位变化较小。     

氯乙烯-丙烯腈共聚物乳液合成技术及其表征

介绍了氯乙烯-丙烯腈共聚物的乳液聚合方法,研究了合成过程中乳化剂、引发剂的加入方式及工艺条件对共聚物性能的影响,并对共聚物进行了表征。结果表明:乳化剂的最佳投加方式为(以乳化剂/VCM表示):先投加0.02,反应开始后流加0.02;引发剂的最佳投加方式为(以引发剂/VCM表示):先投加0.012,反应开始后流加0.012。该共聚物具有优良的阻燃性能。     

核壳结构聚合物乳液乳胶粒粒径及重量分布测试

对核壳结构聚合物乳液乳胶粒的粒径及其分布进行了测试,并与同一聚合物体系的其它乳液加以比较、分析,得出其粒径最小、分布最均匀的重要结论.