氮化硅/石墨激光合金化涂层的组织结构与性能研究

为获得金属表面特别是高副接触金属表面含自润滑特性且具有高硬度耐磨特性的功能材料 ,研究了 45 # 钢表面激光合金化氮化硅 /石墨复合涂层的工艺方法、组织特征、界面形态及其形成机制 ,利用光学显微镜、扫描电镜和X射线能谱对所形成合金化层的元素分布和含量进行了分析 ,并对试样硬度进行了测定。结果表明 ,合金化层中元素Fe ,Co ,Si,C分布均匀 ;C含量达到了 15 6 9%,大部分以石墨的形式存在 ,具有一定的自润滑性能 ;但在形成合金化层的温度条件下 ,氮化硅分解严重 ;合金化层硬度提高的主要原因是Si Fe ,Co Fe固溶体的强化作用及高碳马氏体的生成和高硬度碳化物的存在。     

Magnetic Properties of Fe-Doped Rutile

Ball-milling method was applied to dissolve Fe into titanium dioxide (TiO₂). X-ray diffraction indicated the starting anatase changed to a rutile-type structure with oxygen deficiency after ball milling. Transmission electron microscopy and X-ray absorption experiments were conducted to examine the possible existence of magnetic impurities in the ball-milled powders after they were leached in HCl solutions. Temperature dependence of the resistivity shows semiconducting behavior and the magnetic hysteresis loops at 5 and 300 K exhibit ferromagnetic characteristics. Fe-doped TiO₂ films were also prepared by pulsed laser deposition. The magnetic properties of the films are discussed.     

激光剥离GaN/Al2O3材料温度分布的解析分析

分析了脉冲激光作用下GaN的衬底剥离过程。利用简化的一维模型，给出一种比较直观的脉冲激光辐照下GaN／Al2O3材料温度分布的解析形式，得到了分界面温度和脉冲宽度的关系。表明，单脉冲作用下分界面的温度与加热时间的平方根成正比，并得出脉冲过后随着深度变化温度梯度的分布。在连续脉冲作用时，分界面的温度呈锯齿状不断升高。     

基于MODBUS协议的激光雕刻切割系统HMI人机交互设备

近年来,国内激光雕刻切割控制器技术发展迅速,基于PC的传统控制器已相当成熟.为了显著提高工业生产效率,适应工业生产规模扩张的需要以及工业对系统稳定性要求的提高,目前国内几家专业运动控制器厂家已经实现了激光雕刻切割控制器的完全脱机运行.本文针对脱机控制器的需要设计一款人机交互设备,该设备采用AT89C55WD单片机为主控制器,采用标准的MODBUS协议实现HMI与脱机控制器的可靠通讯.     

面向应用的无线传感器网络

结合具体的应用环境分析了无线传感器网络发展到第二阶段需要考虑的重点问题；探讨了基于上述应用需求的无线传感器网络的协议栈结构和今后的研究方向。     

火炮身管内表面激光硬化处理的实验研究

提高身管寿命是火炮行业亟待解决的关键技术问题，激光表面改性技术是解决这一问题的有效方法之一。本文在分析激光表面相变硬化性能的基础上，对身管内表面进行了激光硬化处理实验研究，检测了其内表面阳线和阴线的硬化层硬度和深度，对比分析了离焦量和焦深对其内表面硬化层硬度的影响，并对激光相变硬化层金相组织进行了分析。经激光硬化处理后，身管的内表面硬度有明显提高，硬化层较深，且为很细的条状马氏体组织。     

Mechanical properties of polyethylene mixtures crystallized under high pressure

The mechanical properties of a medium molecular weight polyethylene (MMW‐PE) and an ultrahigh molecular weight PE (UHMW‐PE) binary mixture with different weight fractions crystallized from the melt at 0.1 and 450 MPa were studied. The tensile modulus, yield stress, and strain were obtained as a function of the weight fractions in the PE mixtures at 25 and 85°C. The tensile modulus in the sample crystallized at 0.1 MPa decreased from 1.5 GPa of pure MMW‐PE to about 0.4 GPa of pure UHMW‐PE with the UHMW‐PE content but it did not decrease with the UHMW‐PE in the sample crystallized at 450 MPa in testing at 25°C. A decreasing rate of the storage modulus E′ of UHMW‐PE in a dynamic measurement for the sample crystallized at 0.1 MPa with the temperature is larger than that of the sample crystallized at 450 MPa. These experimental facts are interpreted in relation to the molecular motion and crystallinity of the sample. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1962–1968, 2003     

随机激光器的最新进展

综述了近年来随机激光器的最新研究结果，包括随机激光产生的机制，随机增益介质的制备方法，随机激光器的激励与发光特性和随机激光理论。最后，介绍了随机激光器的应用前景。     

化学复合镀层激光处理研究

研究了激光处理对Ni-P -SiC化学复合镀层的影响。借助于扫描电镜、能谱仪、X射线衍射、显微硬度计等设备对激光处理后复合镀层的表面形貌、组织结构及性能进行了综合分析。结果表明 ,对复合镀层进行激光处理可以获得与炉内加热同样的镀层硬度 ,且当激光功率 4 0 0W ,扫描速度 1.5m /min时 ,镀层硬度高于炉内加热的硬度     

应用激光活化饵料藻种的研究

应用Nd:YAG激光(波长1.06μm,功率5w,照射时间0.5-3 min)和Ar+激光(波长488nm,功率70mw,照射时间5-15min)对长期保存的不同保存形式的塔胞藻(Pyramidomonassp.)进行辐照处理。研究了不同剂量激光辐照对藻体生长和叶绿素含量的影响。实验结果表明:照射剂量为60s的Nd:YAG激光及剂量为15min的Ar+激光对液体保存形式的藻种有较明显的促长效果,接种后这两种激光处理组的比生长速率分别较对照提高达53.33%和28.89%,叶绿素含量分别增加73.33%和65.69%。两种激光对液体保存藻种的活化效果均好于固体保存种。