丙烯酸接枝线形低密度聚乙烯的热学行为及结晶形态

利用差示扫描量热仪研究了丙烯酸接枝线形低密度聚乙烯（PE-LLD-g-AA）的热学行为，结果表明，与纯线形低密度聚乙烯（PE—LLD）相比，PE-LLD-g-AA的熔融温度（Tm）略有增加，结晶温度（Tc）增加大约4℃，熔融焓（AHm）随AA含量的增加而降低。还利用差示扫描量热仪研究了PE—LLD和PE—LLD-g—AA的等温结晶动力学，用扫描电子显微镜观察了PE—LLD-g—AA等温结晶形态。结果表明，PE-LLD-g-AA的结晶速率大于纯PE—LLD的，随着接枝率的增加，PE-LLD的球晶半径减小，接枝到PE—LLD分子链上的AA分子起到了成核剂的作用。     

Bubble temperature data for phenol-alcohol systems: Phenol-I-Amyl alcohol and phenol-n-Amyl alcohol systems

In order to supplement the literature data on VLE, isobaric bubble temperature data were collected for the binary systems phenol-i-amyl alcohol and phenol-n-amyl alcohol over the entire composition range by indirect method using a standard Swietoslawski type ebulliometer. The measurements were made at three sub-atmospheric pressures. The experimental t-x data were correlated with both equation of state method and gamma-phi methods. In the former approach, the Soave equation of state is used, whereas in the latter case Wilson, NRTL and UNIQUAC equations are used.     

Influences of zinc oxide and an organic additive on the electrochemical behavior of pure aluminum in an alkaline solution

The corrosion behavior of pure aluminum in inhibited and uninhibited 4 MKOH was investigated by means of hydrogen collection, polarization curve measurement and electrochemical impedance spectroscopy (EIS). The results showed that the corrosion of pure aluminum was greatly inhibited by the addition of ZnO and dimethyl amine epoxy propane (designated as DE). EIS and EDAX analyses revealed that ZnO produces its effect by depositing on the aluminum surface, which increases the overpotential of hydrogen evolution. It was also found that the addition of DE could greatly improve the deposition of zinc layers.     

酸性镀锡液的新进展

从近几年美国发明专利的角度扼要综述酸性镀锡液的新进展。说明酸性镀锡液由氟硼酸盐型发展为烷基磺酸盐型的改进过程。列出参考文献９篇。     

电子陶瓷和器件的低温共烧技术

较系统地介绍了电子器件用低温共烧陶瓷(low temperature cofired ceramics,LTCCs)材料,探讨了其工艺中的若干问题。电子器件用低温共烧陶瓷材料包括:玻璃/陶瓷复合材料、结晶化玻璃、晶化玻璃/陶瓷复合材料以及液相烧结陶瓷,其中典型的和最为常用的LTCCs为玻璃/陶瓷(特别是氧化铝)复合材料。正在研究的一些陶瓷介质材料中,Bi基介质材料引起了人们的关注。玻璃/陶瓷复合材料的制备工艺中,应当着重关注和加深了解玻璃的流动性和结晶性、玻璃的起泡、玻璃和陶瓷颗粒间的反应、共烧材料的匹配等问题,从优选材料配方和优化工艺着手,从而获得优质可靠的材质和器件。     

The adhesion of amorphous polystyrene surfaces below Tg

The bonding of polystyrene (PS) surfaces below T_g was investigated by two different fracture tests: the lap-shear joint method and the cantilever beam method. Adhesion energy values obtained by the two methods are in agreement and develop with (time)^1/2, at temperatures as low as T_g−16 °C. Even if the double cantilever method is the most common test found in the literature for adhesions above T_g, for low adhesion values, below T_g, the lap-shear joint geometry is more appropriate. Moreover, when the glass transition temperature is used as a reference temperature, polydisperse and monodisperse PS adhesion energy curves are superposable, suggesting that the auto-adhesion is not significantly favored by the presence of numerous chain ends at the surface (due to the low molecular weight chains provided by the polydisperse PS).     

试验温度和停放时间对胶料加工性能的影响

研究试验温度和停放时间对胶料加工性能的影响。结果表明，试验温度对胶料的门尼粘度、门尼焦烧时间和硫化特性均有一定影响。门尼粘度测定的试验温度选择100℃；门尼焦烧时间测定的试验温度一般选120℃，SBR胶料可提高至130℃左右，以缩短试验时间；硫化特性测定的试验温度一般选185℃。试验前模腔达到规定温度后再保持15min，以使转子与模腔温度一致。胶料停放时间应控制在2h左右。     

Comments on the characterisation of oxidation catalysts using TPR/TPO

Temperature programmed reduction (TPR) and oxidation (TPO) are used extensively in catalyst characterisation. In this paper, we examine the use of TPR/TPO cycles for the characterisation of a range of molybdates and single oxides. In particular we observe that the first cycle differs from that of subsequent analyses, even when the maximum temperature is limited to that used in the catalytic reaction. The effect is independent of heating rates and cooling atmospheres and has been demonstrated using different bed configurations. This observation has significance when these oxides are used in periodic flow reactors that involve many cyclical reduction/oxidation.     

High temperature swelling of coal/tetralin mixtures in a high pressure microdilatometer

High pressure microdilatometer experiments were performed on a subbituminous (Wyodak) and a bituminous (Illinois no. 6) coal in helium and hydrogen atmospheres with and without added tetralin. Wyodak coal samples showed no swelling but contractions ranging between 24 and 40 vol% upon heating at 20 and 100 °C min^{− 1} under helium or hydrogen pressures between 150 and 1000 psig (˜1.0–6.9 MPa). Under the same conditions, Illinois no. 6 coals displayed contractions (25–60 vol%) prior to swelling up to 117 vol%. Upon tetralin addition (at 35–190 wt% of the coal), Wyodak coal samples did not swell but showed an increasing contraction with increasing helium or hydrogen pressure due to a slight softening and fusion of the coal particles. In contrast, addition of tetralin at much lower concentrations (5–35 wt%) had a marked effect on the contraction and swelling behaviour of Illinois no. 6. A maximum swelling of 200 vol% was obtained at a tetralin addition of 30 wt%. The increased swelling results from more extensive softening and fusion of coal particles in the presence of tetralin. Both coals showed a decreasing char yield with increasing tetralin concentration. The substantially lower extent of interaction observed between Wyodak coal samples and tetralin compared to Illinois no. 6 coal can be attributed to the differences in pore structure and/or chemical constitution of the two coal samples. Examination of the resultant solids by optical microscopy revealed the microstructural changes produced by thermal treatment in dilatometer experiments.