Studies of temperature and time-dependent network formation in commercial epoxy resins using modified imidazole curing agents

Two commercial epoxy resins, MY750 and MY720, were cured over a range of cure temperatures with a series of novel curing agents based on modified imidazoles. A combination of techniques, including dynamic viscometry, proton nuclear magnetic resonance spectroscopy, differential scanning calorimetry, high performance and gel permeation chromatography, were used to analyse the reaction mixture. It appears that for a given formulation and given resin, the viscosity behaviour near gelation is different for different cure temperatures and the mechanism appears to be dependent not only on the nature of the imidazole curing agent, but also on the cure temperature. Higher temperature cure appears to lead to the formation of a less ‘homogeneous’ reaction mixture at the gel point, containing oligomeric chain lengths of higher polydispersity, whereas in the lower temperature cure, oligomers of a smaller range of chain lengths are present.     

EVOH基梳型聚合物的合成和表征

以乙烯-乙烯醇共聚物(EVOH)为原料,在乙醇钠的催化作用下,通过与环氧乙烷(EO)的反应,合成出侧链为醚链结构且端基为羟基的梳型聚合物.采用红外光谱(IR)、核磁共振波谱(NMR)、凝胶渗透色谱(GPC)法对梳型聚合物的结构及其分子量进行了表征.讨论了EVOH与EO摩尔配比(r)和催化剂对接枝反应速度、接枝度、接枝长度、粗产率、分子量及其分子量分布的影响.结果表明:增加催化剂的用量有利于环氧乙烷的转化率提高,接枝反应速度明显增加;随着r的减少,EVOH的接枝度增加,侧链上接枝EO的数目逐渐变大,而产物的粗产率变化不大,均为35%左右.     

紫铜表层Fe-Al共渗工艺研究

利用固体法Fe-Al共渗工艺,对紫铜表层进行强化处理。用JSM-6380LA型扫描电镜J、ED-2300能谱仪和HMV显微硬度计分析渗层的组织形态、成分和显微硬度,用MLD-10型动载磨料磨损试验机对三种试样进行耐磨性试验,结果表明:在塑性好的α1或α1+(α2+γ2)亚共析组织基体上,均匀分布有Fe、Al共渗的(α2+γ2)共析相,其耐磨性好于单渗Al和未渗的试样。随着加热温度的升高、保温时间的增长,渗层越深。     

纳米蒙脱土填充紫外光固化涂层的介质传输行为

采用静态浸泡法绘制了漆膜增重-时间曲线,研究了纳米蒙脱土(nanoMMT)填充紫外光固化涂层的吸水性及纳米蒙脱土用量、环氧丙烯酸酯(EA)与合成活性稀释剂(RD)比例、光固化涂层的固化程度与介质传输行为的关系.结果表明,WEA∶WRD越大、涂层的固化程度越高,涂层的抗介质渗透性能越好.添加纳米蒙脱土能促进涂层中酯键的水解,对涂层的耐介质传输性能不利.     

乙烯-乙烯醇共聚物(EVOH)的辐射效应研究

用凝胶抽提、凝胶渗透色谱以及傅立叶变换红外光谱等方法研究了两种乙烯-乙烯醇共聚物（Ethylene-vinyl alcohol copolymers,EVOH）本体和E151／甘油体系的室温辐射效应。在氮气保护下,试样在^60Co源中的吸收剂量最高达到1800kGy。结果显示,EVOH在室温下是一种十分难交联的聚合物。E151本体（乙烯醇摩尔分数56％）在吸收剂量达到800kGy时出现痕量凝胶,当吸收剂量增至1200kGy时,体系凝胶含量也只有5．9％。而F101本体（乙烯醇摩尔分数68％）在1800kGy才出现痕量凝胶。造成这两种EVOH的凝胶化剂量不同的原因是乙烯醇基含量不同。EVOH在辐照过程会产生共轭双键,其含量在辐照初期随吸收剂量的增加而增大,达到最大值后随吸收剂量的增加而减少。双键的存在促使EVOH产生了交联。加入增塑剂甘油后,体系在800kGy以前与本体一样无凝胶,而在800kGy之后凝胶含量随着吸收剂量的增大而增大,且比本体E151的凝胶含量值大。     

Fe-Al/Al2O3阻氚涂层热处理条件对HR-2不锈钢力学性能影响

采用室温力学拉伸试验、显微硬度测试、X射线衍射及组织观察等方法研究了"室温熔盐电镀铝+热处理+选择性氧化"工艺路线制备Fe-Al/Al2 O3阻氚涂层热处理过程对HR-2奥氏体不锈钢力学性能及显微组织的影响.结果表明:经热处理后的HR-2不锈钢仍然保持奥氏体组织;980℃热处理180 min时抗拉强度为580.48 M...     

土工织物垂直渗透系数测试技术研究

收集了国内外有关土工织物渗透性能的测试标准,并进行了比较。分析了土工织物的微观结构以及渗透原理,通过系列的试验数据探讨了土工织物渗透性能的规律,即水头差与流速的关系,比较三种拟合方式的拟合程度,提出最合适的拟合关系作为水头差和流速的理论关系式。分析比较几种检测标准取值的依据,提出检测结果取值的方案,为国家测试标准GB/T 15789-1995《土工布透水性测定方法》的修订提供依据。     

制浆过程木材浸渍研究进展

从多个角度对木材浸渍研究进展进行了分析论述,全面阐述了基于渗透理论及扩散理论的木材浸渍理论模型,介绍了木材浸渍研究的3种常用连续测量方法,详细论述了木材浸渍的影响因素及改善措施。     

食用油中邻苯二甲酸酯的GC-MS测定方法研究

为了检测食用油中邻苯二甲酸酯污染程度,建立了气相色谱-质谱法检测食用油中邻苯二甲酸酯含量的方法.样品经环己烷-乙酸乙酯溶解,凝胶渗透色谱分离系统净化,减压浓缩至于,正己烷定容,气相色谱-质谱联用仪测定,外标法定量.在50μg/L～5000μg/L范围内具有良好的线性关系(R2＞0.997),方法检测限小于40μg/kg;在100μg/kg～5000μg/kg的添加水平下,邻苯二甲酸酯的加标回收率在77.52%～103.10%之间,相对标准偏差在0.29%～4.68%之间;方法精密度实验的相对标准偏差在5%之内;基质加标校正曲线的定量优于标准品校正曲线.结果表明,该方法适用于食用油中邻苯二甲酸酯定性和定量测定.     

纸张毛细管半径测量的新方法

利用印刷过程中油墨渗透深度随印刷压力和印刷速度的变化关系,建立了纸张毛细管半径方程,用实验方法测量了印刷过程中油墨在纸张中的渗透深度,由印刷压力、印刷速度、渗透深度测量值实现了纸张毛细管半径的定量测量。